Long afterglow pe masterbatch, its preparation method, pe plastic parts and its preparation method

A long afterglow and masterbatch technology, applied in PE plastic parts and its preparation, long afterglow PE masterbatch, its preparation field, can solve the problems of uneven dispersion of luminous powder, black color of masterbatch, low content of luminous powder, etc. , to achieve the effect of improving compatibility, reducing the darkening of masterbatch color and high brightness

Active Publication Date: 2021-12-17
INST OF RESOURCES UTILIZATION & RARE EARTH DEV GUANGDONG ACAD OF SCI
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, when processing and preparing luminous PE resin, the luminous powder is generally mixed directly with the PE resin used and then blow molded or injection molded. The mass fraction of luminous powder in the obtained product is 5%-15%, but there are PE luminous masterbatches on the market Problems such as uneven dispersion of luminous powder, low content of luminous powder, black color of masterbatch, low luminous brightness, short luminous time, and reduced mechanical properties of molded parts after adding this kind of masterbatch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Long afterglow pe masterbatch, its preparation method, pe plastic parts and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] The preparation of the graft polymer is a routine experiment for those skilled in the art, and will not be described in detail in the present invention.

[0048] Further, the above-mentioned dispersant is a hyperbranched polymer. For example, at least one of C100, C181, HyPerC10, HyPerC20, HyPerC30 and HyPerC40 produced by Guangdong Fujiang Chemical Reagent Co., Ltd. can be used. The use of the above-mentioned dispersant can further promote the uniform mixing of the luminous powder and the PE resin, prevent the aggregation of the luminous powder, and reduce the aging of the PE resin, thereby ensuring the luminous effect of the long-lasting PE masterbatch.

[0049] Further, the heat stabilizer is a stearic acid compound, preferably a stearate, more preferably zinc stearate or calcium stearate, the use of the above heat stabilizer can further reduce the aging of the PE resin during the preparation process, ensuring Long afterglow PE masterbatch has bright luminous color,...

Embodiment 1

[0064] This embodiment provides a long afterglow PE masterbatch, the composition of raw materials is as follows, 68.5g of PE-MAH (maleic anhydride modified polyethylene, grafting rate of 0.5%), 0.5g of C100 dispersant, 1g of Zinc Stearate, 30g of BL-2A Luminous Powder.

[0065] This embodiment also provides a preparation method of long afterglow PE masterbatch:

[0066] Add each component to the mixer and mix for 3 minutes in a mixer with a rotation speed of 100r / min. After mixing evenly, add it to a twin-screw extruder with a rotation speed of 200r / min, and melt at 140°C After blending and extruding, it is granulated, then dried, and packaged to obtain long-lasting PE masterbatch.

Embodiment 2

[0068] This embodiment provides a long afterglow PE masterbatch, the composition of raw materials is as follows, 64gPE-MAH (grafting rate 0.5%), 1gC181 hyperdispersant, 5g calcium stearate, 30g of GL-8C luminous powder.

[0069] This embodiment also provides a preparation method of long afterglow PE masterbatch:

[0070] Add each component to the mixer and mix for 10 minutes in a mixer with a rotation speed of 200r / min. After mixing evenly, add it to a twin-screw extruder with a rotation speed of 500r / min and melt it at a temperature of 150°C. After blending and extruding, it is granulated, then dried, and packaged to obtain long-lasting PE masterbatch.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of composite materials, in particular to a long afterglow PE masterbatch, a preparation method thereof, a PE plastic part and a preparation method thereof. Long afterglow PE masterbatch, in parts by weight, its raw materials include 28-68.5 parts of PE resin, 0.3-1 part of dispersant, 0.5-5 parts of heat stabilizer and 30-70 parts of luminous powder, and The luminous powder in the long afterglow PE masterbatch forms a bond with the PE resin. The content of luminous powder in the long afterglow PE masterbatch of the present invention can reach 30-70%, and the luminous powder is evenly dispersed, and the long afterglow PE masterbatch has bright color, long luminescence time and high brightness.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a long afterglow PE masterbatch, a preparation method thereof, a PE plastic part and a preparation method thereof. Background technique [0002] Glow in the dark powder is aluminate activated by a variety of rare earth ions, which can continue to glow in the dark for a long time after being irradiated by light and heated. Polyethylene (PE for short) is a kind of thermoplastic PE resin obtained by polymerization of ethylene. Good resistance to most acid and alkali corrosion, insoluble in common solvents at room temperature, low water absorption, excellent electrical insulation. The luminous material made by adding luminous powder to PE resin plastic can be widely used in toys, decoration, clothing, outdoor signs and other fields. At present, when processing and preparing luminous PE resin, the luminous powder is generally mixed directly with the PE resin used and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L51/06C08K5/098C08J3/22
CPCC08J3/226C08L23/06C08J2323/06C08J2451/06C08L2207/062C08L51/06C08K5/098
Inventor 杨锐孔振兴戴子林倪海勇丁建红傅汉清区菊花李桂英
Owner INST OF RESOURCES UTILIZATION & RARE EARTH DEV GUANGDONG ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com