cmc/fa-chitosan hydrochloride composite nanoparticles, its preparation method and application

A chitosan hydrochloride, composite nanoparticle technology, applied in the application, nanotechnology, food ingredients and other directions, to avoid Ostrich ripening, excellent antioxidant properties, easy to industrialize the effect of production

Active Publication Date: 2021-10-26
HEFEI UNIV OF TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no document / patent report on making carboxymethyl cellulose and ferulic acid into a compound, and then compounding it with chitosan hydrochloride to prepare nanoparticles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • cmc/fa-chitosan hydrochloride composite nanoparticles, its preparation method and application
  • cmc/fa-chitosan hydrochloride composite nanoparticles, its preparation method and application
  • cmc/fa-chitosan hydrochloride composite nanoparticles, its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] 1. Preparation of carboxymethyl cellulose / ferulic acid complex

[0050] The carboxymethyl cellulose was dissolved in distilled water to obtain a 0.1 wt% carboxymethyl cellulose solution. The solution was continuously stirred at 250 rpm for 1 hour, and the pH was adjusted to 4. EDC and ferulic acid are dissolved in ethanol, its mixed solution is added dropwise in the carboxymethyl cellulose solution 250rpm continuous stirring 1 hour, the mol ratio of ferulic acid and carboxymethyl cellulose is 1:3 (the concrete dosage is respectively For: 10mg, 30mg), and the pH of the solution was adjusted to 4 using 0.1M hydrochloric acid.

[0051] 2. Preparation of carboxymethyl cellulose / ferulic acid-chitosan hydrochloride composite nanoparticles

[0052] Chitosan hydrochloride is placed on the stirrer and stirred and dissolved and the pH is adjusted to be 4 to obtain 0.2wt% chitosan hydrochloride solution; Ferulic acid complex solution was added dropwise to chitosan hydrochloride ...

Embodiment 2

[0057] 1. Preparation of carboxymethyl cellulose / ferulic acid complex

[0058] Carboxymethyl cellulose was dissolved in distilled water to obtain a 0.1 wt% carboxymethyl cellulose solution, stirred continuously at 250 rpm for 1 hour, and the pH was adjusted to 4. ED and ferulic acid are dissolved in ethanol, its mixed solution is added dropwise in the carboxymethyl cellulose solution 250rpm continuous stirring 1 hour, the mol ratio of ferulic acid and carboxymethyl cellulose is 1:2 (the specific dosage is respectively For: 10mg, 20mg), and use 0.1M hydrochloric acid to adjust the pH of the solution to 4.

[0059] 2. Preparation of carboxymethyl cellulose / ferulic acid-chitosan hydrochloride composite nanoparticles

[0060] Chitosan hydrochloride is placed on the stirrer and stirred and dissolved and the pH is adjusted to be 4 to obtain 0.2wt% chitosan hydrochloride solution; Ferulic acid complex solution was added dropwise to chitosan hydrochloride solution to obtain carboxym...

Embodiment 3

[0065] 1. Preparation of carboxymethyl cellulose / ferulic acid complex

[0066] Carboxymethyl cellulose was dissolved in distilled water to obtain a 0.1 wt% carboxymethyl cellulose solution, stirred continuously at 250 rpm for 1 hour, and the pH was adjusted to 4. ED and ferulic acid are dissolved in ethanol, its mixed solution is added dropwise in the carboxymethyl cellulose solution 250rpm continuous stirring 1 hour, the mol ratio of ferulic acid and carboxymethyl cellulose is 2:1 (the concrete consumption is respectively For: 20mg, 10mg), and the pH of the solution was adjusted to 4 using 0.1M hydrochloric acid.

[0067] 2. Preparation of carboxymethyl cellulose / ferulic acid-chitosan hydrochloride composite nanoparticles

[0068] Chitosan hydrochloride is placed on the stirrer and stirred and dissolved and the pH is adjusted to be 4 to obtain 0.2wt% chitosan hydrochloride solution; Ferulic acid complex solution was added dropwise to chitosan hydrochloride solution to obtai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of CMC / FA-chitosan hydrochloride composite nanoparticles, which comprises: passing carboxymethyl cellulose and ferulic acid through 1-ethyl-(3 ‑Dimethylaminopropyl) carbodiimide (EDC)-mediated esterification to form carboxymethylcellulose / ferulic acid complex; preparation of chitosan hydrochloride solution, preparation of carboxymethyl fiber element / ferulic acid complex solution; under stirring, described carboxymethyl cellulose / ferulic acid complex solution and chitosan hydrochloride solution mixed reaction, make carboxymethyl cellulose / ferulic acid- Chitosan hydrochloride composite nanoparticles. The invention also discloses a method for preparing Pickering emulsion by using the composite nanoparticle. The composite nanoparticle provided by the invention has good dispersibility and emulsifying performance, and the Pickering emulsion prepared by using it as an emulsifier has good physical stability and antioxidant activity, and can be widely used in food, medicine and cosmetics and other fields.

Description

technical field [0001] The present invention relates to a preparation method of oil-water emulsion, in particular to a CMC / FA-chitosan hydrochloride composite nanoparticle, its preparation method and application, such as the use in the preparation of Pickering emulsion, which belongs to emulsifier technology field. Background technique [0002] Pickering emulsion is a type of emulsion stabilized by solid particles instead of surfactants. The stabilization mechanism is that nanoparticles, as stabilizers, are irreversibly adsorbed at the oil-water interface to provide a physical barrier, forming a film or coagulation of particle aggregates around the oil droplets. The colloidal structure improves the stability of Pickering emulsions to coalescence and Ostwald ripening. This mechanism endows Pickering emulsions with greater stability compared to small molecule surfactants and traditional emulsions stabilized with natural macromolecules. However, common problems such as biocom...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L5/08C08L1/28C08J3/12B82Y40/00A23P10/30A23L29/30
CPCA23V2002/00A23L29/30A23P10/30B82Y40/00C08J3/12C08J2305/08C08J2401/28A23V2250/51082A23V2250/511
Inventor 章宝孟然潘怡李小敏刘文杰李小龙
Owner HEFEI UNIV OF TECH