A kind of rice paper porcelain and its preparation method and application

A technology of rice paper porcelain and rice paper, which is applied in the field of ceramics, can solve the problems of the toughness of porcelain plate painting cotton and the incomparability of infinite tension rice paper, and achieve the effect of excellent artistic appreciation, bright colors and clear ink rhyme

Active Publication Date: 2022-03-01
黑龙江省辽金源陶瓷有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the toughness and infinite tension of porcelain paintings are incomparable with rice paper.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of rice paper porcelain and its preparation method and application
  • A kind of rice paper porcelain and its preparation method and application
  • A kind of rice paper porcelain and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～5

[0047] A kind of rice paper porcelain, in terms of mass percentage, the components are as shown in Table 1;

[0048] Table 1

[0049]

[0050]

[0051] Wherein, in embodiment 1~5, kaolin is made up of the material of mass percentage shown in table 2;

[0052] Table 2

[0053] project quartz Feldspar Kaolinite illite Example 1 17.5 15 62.5 5 Example 2 63 24 12 1 Example 3 17 15 63 5 Example 4 17.5 15 62.5 5 Example 5 17.5 15 62.5 5

[0054] The particle diameter of kaolin and quartz sand in embodiment 1~5 is as shown in table 3;

[0055] table 3

[0056] project Particle size of kaolin / mm Particle size of quartz sand / mm Particle size of five-color soil / mm Example 1 0.18 0.18 0.18 Example 2 0.05 0.18 0.05 Example 3 0.18 0.05 0.18 Example 4 0.18 0.18 0.05 Example 5 0.18 0.05 0.05

Embodiment 1

[0058] SiO of quartz sand in embodiment 1 2 The content is 65%, SiO in five-color soil 2 The content is 61~65%, Al 2 o 3 The content is 19-21%;

Embodiment 2

[0059] SiO of quartz sand in embodiment 2 2 The content is 65%, SiO in five-color soil 2 The content is 64.6%, Al 2 o 3 The content is 20.43%;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a rice paper porcelain and its preparation method and application. The rice paper porcelain comprises the following components in terms of mass percentage: 30-40% of kaolin; 10-20% of quartz sand; 5-15% of five-color soil; amount; among them, kaolin is kaolin with specific components, and SiO in quartz sand 2 The content is 60-65%, SiO in five-color soil 2 The content is 61~65%, Al 2 o 3 The content is 19-21%. The rice paper porcelain uses unique kaolin, quartz sand, and five-color soil as the main raw materials. Through the synergistic effect of specific components, the water absorption rate of the prepared rice paper porcelain is 2.7-3.1%, and the acid resistance and alkali resistance are both high. More than 99%, the bending strength is as high as 110MPa, and the compressive strength is as high as 710.9MPa. Through specific variable temperature firing, the prepared rice paper porcelain has no fading phenomenon when placed indoors and outdoors, and has excellent moisture resistance and color retention.

Description

technical field [0001] The invention relates to the field of ceramics, in particular to a rice paper porcelain and its preparation method and application. Background technique [0002] my country's porcelain plate painting has a long history. By the middle of Qing Dynasty, the development of porcelain plate painting was prosperous. Porcelain painting artists at that time devoted themselves to transplanting Chinese paintings on rice paper to porcelain. Therefore, porcelain plate paintings were favored by people and became important commodity porcelain. Porcelain-inlaid screens, whether it is a screen, a screen or a hanging screen, are often seen with porcelain paintings inlaid with strong decorative meanings. Existing porcelain plate paintings are often made by firing ink or glaze on the surface of ceramics. However, due to the small amount of ink, the color of the sprayed ink will become lighter during the sintering process after the ink is sprayed. Phenomena, resulting in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/04C04B33/32C04B33/13B44D2/00
CPCC04B33/04C04B33/32C04B33/13B44D2/00C04B2235/3418C04B2235/3463C04B2235/3445
Inventor 旷理勇
Owner 黑龙江省辽金源陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com