Surface enhancement treatment method for heavy hammer sheet
A surface enhancement and treatment method technology, applied in the direction of pretreatment surface, device for coating liquid on the surface, coating, etc., can solve the problems of low bonding strength of the substrate, affecting the stability of use, and the decline of mechanical strength, etc., to achieve the benefit of Cross-linking and fixing, improving the use effect and life, and enhancing the effect of mechanical quality
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0031] Example 1
[0032] A method for enhancing the surface of a heavy hammer plate includes the following steps:
[0033] (1) Surface cleaning treatment:
[0034] Put the heavy hammer into acetone for 8min, then take it out and rinse it with deionized water and dry it for later use;
[0035] (2) Shot peening:
[0036] Put the weight plate processed in step (1) into the shot blasting machine for surface shot peening, take it out after completion and blow off the particles and impurities remaining on the surface with compressed air for use;
[0037] (3) Surface plasma treatment:
[0038] Put the heavy hammer plate processed in step (2) into a low-energy plasma processor for plasma treatment, and take it out for use after 15 minutes;
[0039] (4) Coating spray treatment:
[0040] a. First, titanium nitride and zirconium dioxide are mixed according to a weight ratio of 1.5:1, and then put into the roller mixer for mixing for 3 hours, and mixed powder A is taken out for use;
[0041] b. Put the...
Example Embodiment
[0055] Example 2
[0056] A method for enhancing the surface of a heavy hammer plate includes the following steps:
[0057] (1) Surface cleaning treatment:
[0058] Put the heavy hammer into acetone and soak for 9 minutes, then take it out and rinse it with deionized water and dry it for later use;
[0059] (2) Shot peening:
[0060] Put the weight plate processed in step (1) into the shot blasting machine for surface shot peening, take it out after completion and blow off the particles and impurities remaining on the surface with compressed air for use;
[0061] (3) Surface plasma treatment:
[0062] Put the weight plate processed in step (2) into a low-energy plasma processor for plasma treatment, and take it out after 18 minutes for use;
[0063] (4) Coating spray treatment:
[0064] a. First, titanium nitride and zirconium dioxide are mixed according to a weight ratio of 1.8:1, and then put into the roller mixer for mixing treatment for 4 hours, and mixed powder A is taken out for use; ...
Example Embodiment
[0079] Example 3
[0080] A method for enhancing the surface of a heavy hammer plate includes the following steps:
[0081] (1) Surface cleaning treatment:
[0082] Put the heavy hammer into acetone for 10 minutes, then take it out and rinse it with deionized water and dry it for later use;
[0083] (2) Shot peening:
[0084] Put the weight plate processed in step (1) into the shot blasting machine for surface shot peening, take it out after completion and blow off the particles and impurities remaining on the surface with compressed air for use;
[0085] (3) Surface plasma treatment:
[0086] Put the weight plate processed in step (2) into a low-energy plasma processor for plasma treatment, and take it out after 20 minutes for use;
[0087] (4) Coating spray treatment:
[0088] a. First, titanium nitride and zirconium dioxide are mixed according to a weight ratio of 2:1, and then put into a roller mixer for mixing for 5 hours, and mixed powder A is taken out for use;
[0089] b. Put the mic...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap