An optical-grade aluminum dihydrogen phosphate technology, applied in the chemical industry, can solve the problem that the purity of aluminum dihydrogen phosphate cannot meet the needs of use, and achieve the effect of uniform particles

Pending Publication Date: 2020-01-07
上海麟光新材料科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide an optical-grade aluminum dihydrogen phosphate, which can solve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1:

[0021] 1) Take 250 kilograms of distilled water and 200 kilograms of aluminum hydroxide into the No. 1 reactor, turn on the mixer to stir and dissolve, then add 600 kilograms of 31% industrial hydrochloric acid and 350 kilograms of 85% industrial phosphoric acid while stirring, and continue the stirring reaction 30 minutes, at this time the temperature of the solution is between 80-85°C, stop stirring and cool for about 2 hours, the solution is separated into layers, the lower layer is released, and the upper layer solution is transferred to the No. 2 reactor;

[0022] 2) Add 12 kilograms of extracting associating agent to the No. 2 reactor to purify and remove impurities, where the mass ratio of tributyl phosphate and kerosene in the extracting bottom associating agent is 8:10, then stir for 30 minutes, and stand for stratification;

[0023] 3) Remove the lower layer solution for analysis. If the iron content in the lower layer solution is less than 2PPM, copper ...

Example Embodiment

[0026] Example 2

[0027] 1) Take 300 kilograms of distilled water and 240 kilograms of aluminum hydroxide into the No. 1 reactor, turn on the mixer to stir and dissolve, then add 800 kilograms of 31% industrial hydrochloric acid and 420 kilograms of 85% industrial phosphoric acid while stirring, and continue the stirring reaction 30 minutes, at this time the temperature of the solution is between 80-85°C, stop stirring and cool for about 2 hours, the solution is separated into layers, the lower layer is released, and the upper layer solution is transferred to the No. 2 reactor;

[0028] 2) Add 15 kilograms of extracting associating agent to the No. 2 reactor to purify and remove impurities, in which the mass ratio of tributyl phosphate and kerosene in the extracting bottom associating agent is 8:10, then stir for 30 minutes and stand for stratification;

[0029] 3) Remove the lower layer solution for analysis. If the iron content in the lower layer solution is less than 2PPM, copper...

Example Embodiment

[0032] Example 3

[0033] 1) Take 380 kg of distilled water and 300 kg of aluminum hydroxide into the No. 1 reactor, turn on the mixer to stir and dissolve, then add 1000 kg of 31% industrial hydrochloric acid and 520 kg of 85% industrial phosphoric acid while stirring, and continue the stirring reaction 30 minutes, at this time the temperature of the solution is between 80-85°C, stop stirring and cool for about 2 hours, the solution is separated into layers, the lower layer is released, and the upper layer solution is transferred to the No. 2 reactor;

[0034] 2) Add 18 kilograms of extracting associating agent to the No. 2 reactor to purify and remove impurities, in which the mass ratio of tributyl phosphate and kerosene in the extracting bottom associating agent is 8:10, then stir for 30 minutes, and stand for stratification;

[0035] 3) Remove the lower layer solution for analysis. If the iron content in the lower layer solution is less than 2PPM, copper is less than 1PPM, cobalt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses optical grade aluminum dihydrogen phosphate. The optical grade aluminum dihydrogen phosphate comprises the following raw material components in parts by mass: 200-300 parts ofaluminum hydroxide, 660-1000 parts of 31% industrial hydrochloric acid, 350-520 parts of 85% industrial phosphoric acid, 520-790 parts of electronic-grade phosphoric acid, 250-380 parts of distilled water and 12-18 parts of an extraction association agent. The optical grade aluminum dihydrogen phosphate has high purity, the content of impurity iron is smaller than 2 ppm, and the content of impurities such as copper, cobalt and nickel is smaller than 0.1 ppm.

Description

technical field [0001] The invention relates to the technical field of chemical industry, in particular to an optical-grade aluminum dihydrogen phosphate. Background technique [0002] According to national major project construction and international market demand, and with the continuous progress and maturity of strong laser device technology, laser energy, as a green energy, is expected to replace existing energy in 2030, and its market value potential is huge. [0003] Laser neodymium glass is the core device of high-power laser devices, which plays the role of laser energy amplification. The core raw material for preparing laser neodymium glass directly determines the quality of laser neodymium glass, and its quality directly determines the amplification characteristics and energy output level of the laser energy gain of the strong laser device. The main composition of laser neodymium glass is R 2 O-RO-(R 2 o 3 )-P 2 o 5 , where the core raw material R 2 o 3 The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B25/36C03C1/00
CPCC01B25/36C03C1/00C01P2006/80Y02E60/10
Inventor 沈洪娟
Owner 上海麟光新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap