A steel slag modifier with structure grinding aid and surface wrapping effect and preparation method thereof

A modifier and steel slag technology, applied in chemical instruments and methods, other chemical processes, grain processing, etc., can solve the problems of poor grindability and poor dispersibility of steel slag, and achieve reduced grinding energy consumption, low cost, and obvious economy Effects of benefits and social benefits

Active Publication Date: 2020-12-08
MAANSHAN IRON & STEEL CO LTD
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a steel slag modifier with structure grinding aid and surface wrapping effect, which solves the problems of poor grinding property and poor dispersibility of steel slag, and has simple composition and low cost, which is suitable for the promotion and large-scale application of steel slag micropowder technology Provide technical support

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A steel slag modifier with structure grinding aid and surface wrapping effect and preparation method thereof
  • A steel slag modifier with structure grinding aid and surface wrapping effect and preparation method thereof
  • A steel slag modifier with structure grinding aid and surface wrapping effect and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A steel slag modifier with structural grinding aid and surface wrapping effect, made of raw materials of the following quality:

[0025]

[0026] A preparation method of a steel slag modifier having the functions of structural grinding aid and surface wrapping, comprising the following steps:

[0027] 1) After mixing the above-mentioned ethylene glycol, triisopropanolamine and triethanolamine, use a constant temperature magnetic stirrer to stir at a temperature of 35°C at a speed of 900r / min for 80min to obtain ethylene glycol-triisopropanolamine - Triethanolamine mixture.

[0028] 2) After mixing the above-mentioned liquid paraffin and kerosene, stir with a constant temperature magnetic stirrer at a temperature of 40° C. at a speed of 600 r / min for 110 min to obtain a liquid paraffin-kerosene mixture.

[0029] 3) After mixing the ethylene glycol-triisopropanolamine-triethanolamine mixed solution obtained above with the liquid paraffin-kerosene mixed solution, use a...

Embodiment 2

[0031] A steel slag modifier with structural grinding aid and surface wrapping effect, made of raw materials of the following quality:

[0032]

[0033] A preparation method of a steel slag modifier having the functions of structural grinding aid and surface wrapping, comprising the following steps:

[0034] 1) After mixing the above-mentioned ethylene glycol, triisopropanolamine and triethanolamine, use a constant temperature magnetic stirrer to stir at a temperature of 40°C at a speed of 700r / min for 120min to obtain ethylene glycol-triisopropanolamine - Triethanolamine mixture.

[0035] 2) After mixing the above-mentioned liquid paraffin and kerosene, stir with a constant temperature magnetic stirrer at a temperature of 30° C. at a speed of 900 r / min for 90 min to obtain a liquid paraffin-kerosene mixture.

[0036] 3) Finally, after mixing the ethylene glycol-triisopropanolamine-triethanolamine mixed solution obtained above with the liquid paraffin-kerosene mixed soluti...

Embodiment 3

[0038] A steel slag modifier with structural grinding aid and surface wrapping effect, made of raw materials of the following quality:

[0039]

[0040] A preparation method of a steel slag modifier having the functions of structural grinding aid and surface wrapping, comprising the following steps:

[0041] 1) After mixing the above-mentioned ethylene glycol, triisopropanolamine and triethanolamine, use a constant temperature magnetic stirrer to stir at a temperature of 30°C at a speed of 500r / min for 100min to obtain ethylene glycol-triisopropanolamine - Triethanolamine mixture.

[0042] 2) After mixing the above-mentioned liquid paraffin and kerosene, stir with a constant temperature magnetic stirrer at a temperature of 35° C. at a speed of 1000 r / min for 70 min to obtain a liquid paraffin-kerosene mixture.

[0043] 3) After mixing the ethylene glycol-triisopropanolamine-triethanolamine mixed solution obtained above with the liquid paraffin-kerosene mixed solution, use ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a steel slag modifier with structural grinding aid and surface coating functions and a preparation method thereof. The steel slag modifier with the structural grinding aid and surface coating functions comprises the following raw materials, by weight, 5.0%-20.0% of ethylene glycol, 5.0%-20.0% of triisopropanolamine, 5.0%-20.0% of triethanolamine, 35.0%-70.0% of liquid paraffin and 15.0%-50.0% of kerosene. Compared with the prior art, the steel slag modifier are compounded by the raw materials, the stirring temperature, the stirring speed and the stirring time are controlled, a steel slag compounding agent with the structural grinding aid and surface coating functions is obtained, and the obvious effects on improving the grindability and dispersibility of steel slag are achieved. According to the steel slag modifier with the structural grinding aid and surface coating functions and the preparation method thereof, the energy consumption of steel slag grinding can be reduced, the production process is environment-friendly and pollution-free, furthermore, the components are simple, the cost is low, the unification of economy and environment friendliness is realized, the economic benefit and social benefit are obvious, and the popularization and application of steel slag ultrafine powder are facilitated.

Description

technical field [0001] The invention belongs to the technical field of steel slag grinding, and in particular relates to a steel slag modifier with the functions of structural grinding aid and surface wrapping and a preparation method thereof. Background technique [0002] Steel slag is solid waste produced in the steelmaking process, accounting for about 10% to 15% of steelmaking output. The main mineral phase of steel slag is a solid solution formed by tricalcium silicate, dicalcium silicate, calcium magnesium olivine, calcium aluminate ferrite and oxides of silicon, magnesium, iron, manganese and phosphorus, and also contains a small amount of free calcium oxide and metal iron etc. The existence of the above mineral phases leads to poor grindability and poor compatibility of steel slag, which greatly limits the utilization of steel slag and leads to the accumulation of a large amount of steel slag, which not only occupies valuable land, but also pollutes the surrounding ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B02C23/06C09K3/14
CPCB02C23/06C09K3/14
Inventor 张耀辉刘自民李帮平张浩龙红明饶磊桂满城马孟臣
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap