Ternary system lead scandium niobate-lead magnesium niobate-lead titanate ceramic and preparation method thereof

A technology of lead scandium niobate and lead magnesium niobate, applied in the field of inorganic non-metallic functional materials, can solve the problems of low phase transition temperature, poor performance consistency, low coercive field, etc., and achieve the effect of high sensitivity

Inactive Publication Date: 2020-02-28
XIAN TECHNOLOGICAL UNIV
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the invention is to provide a ternary lead scandate-lead magnesium niobate-lead titanate ceramic and its preparation method to solve the problem of the low triangular-tetragonal phase transition temperature of piezoelectric materials used in current medical ultrasonic transducers, Problems such as low persistent field and poor performance consistency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ternary system lead scandium niobate-lead magnesium niobate-lead titanate ceramic and preparation method thereof
  • Ternary system lead scandium niobate-lead magnesium niobate-lead titanate ceramic and preparation method thereof
  • Ternary system lead scandium niobate-lead magnesium niobate-lead titanate ceramic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A ternary lead scandate-lead magnesium niobate-lead titanate ceramics, the chemical formula of which is: 0.15Pb(Sc 1 / 2 Nb 1 / 2 )O 3 -0.48Pb(Mg 1 / 3 Nb 2 / 3 )O 3 -0.37PbTiO 3 .

[0032] The preparation method of the ceramic material comprises the following steps:

[0033] (1) with analytically pure Sc 2 o 3 and Nb 2 o 5 The powder is used as the raw material, and the precursor ScNbO is synthesized by the solid state reaction method 4 ; to analyze pure MgO and Nb 2 o 5 The powder is used as the raw material, and the precursor MgNb is synthesized by the solid state reaction method 2 o 6 ;

[0034] (2) with analytically pure PbO, TiO 2 , ScNbO 4 and MgNb 2 o 6 Powder is the raw material, according to the chemical formula 0.15Pb(Sc 1 / 2 Nb 1 / 2 )O 3 -0.48Pb(Mg 1 / 3 Nb 2 / 3 )O 3 -0.37PbTiO 3 Weigh raw materials;

[0035] (3) Put the powder weighed in step (2) into a ball mill jar, use absolute ethanol as the medium, ZrO 2 The ball is a grinding ball, wh...

Embodiment 2

[0049] A ternary lead scandate-lead magnesium niobate-lead titanate ceramics, the chemical formula of which is: 0.15Pb(Sc 1 / 2 Nb 1 / 2 )O 3 -0.49Pb(Mg 1 / 3 Nb 2 / 3 )O 3 -0.36PbTiO 3 .

[0050] The preparation method of the ceramic material comprises the following steps:

[0051] (1) with analytically pure Sc 2 o 3 and Nb 2 o 5 The powder is used as the raw material, and the precursor ScNbO is synthesized by the solid state reaction method 4 ; to analyze pure MgO and Nb 2 o 5 The powder is used as the raw material, and the precursor MgNb is synthesized by the solid state reaction method 2 o 6 ;

[0052] (2) with analytically pure PbO, TiO 2 , ScNbO 4 and MgNb 2 o 6 Powder is the raw material, according to the chemical formula 0.15Pb(Sc 1 / 2 Nb 1 / 2 )O 3 -0.48Pb(Mg 1 / 3 Nb 2 / 3 )O 3 -0.37PbTiO 3 Weigh raw materials;

[0053] (3) Put the powder weighed in step (2) into a ball mill jar, use absolute ethanol as the medium, ZrO 2 The ball is a grinding ball, wh...

Embodiment 3

[0064] A ternary lead scandate-lead magnesium niobate-lead titanate ceramics, the chemical formula of which is: 0.15Pb(Sc 1 / 2 Nb 1 / 2 )O 3 -0.47Pb(Mg 1 / 3 Nb 2 / 3 )O 3 -0.38PbTiO 3 .

[0065] The preparation method of the ceramic material comprises the following steps:

[0066] (1) with analytically pure Sc 2 o 3 and Nb 2 o 5 The powder is used as the raw material, and the precursor ScNbO is synthesized by the solid state reaction method 4 ; to analyze pure MgO and Nb 2 o 5 The powder is used as the raw material, and the precursor MgNb is synthesized by the solid state reaction method 2 o 6 ;

[0067] (2) with analytically pure PbO, TiO 2 , ScNbO 4 and MgNb 2 o 6 Powder is the raw material, according to the chemical formula 0.15Pb(Sc 1 / 2 Nb 1 / 2 )O 3 -0.47Pb(Mg 1 / 3 Nb 2 / 3 )O 3 -0.38PbTiO 3 Weigh raw materials;

[0068] (3) Put the powder weighed in step (2) into a ball mill jar, use absolute ethanol as the medium, ZrO 2 The ball is a grinding ball, wh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
piezoelectric charge coefficientaaaaaaaaaa
piezoelectric charge coefficientaaaaaaaaaa
Curie pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a ternary system lead scandium niobate-lead magnesium niobate-lead titanate ceramic and a preparation method thereof. The chemical formula of the ceramic material is xPb(Sc1 / 2Nb1 / 2)O3-yPb(Mg1 / 3Nb2 / 3)O3-zPbTiO3, wherein x is greater than or equal to 0.1 mol and less than or equal to 0.28 mol, y is greater than or equal to 0.32 mol and less than or equal to 0.57 mol, z is greater than or equal to 0.33 mol and less than or equal to 0.40 mol, and the sum of x, y and z is 1. The preparation method provided by the invention adopts a traditional two-step solid-phase reactionmethod for synthesis. The ceramic material has piezoelectric constant d33 of 720 pC / N, the radial electromechanical coupling coefficient kp of about 0.65, thickness electromechanical coupling coefficient kt of 0.6, the trigonal-tetragonal phase transition temperature Trt of 90 DEG C to 150 DEG C, the Curie temperature Tc of larger than 170 DEG C and the coercive field of 10 kV / mm, and can meet therequirements of an ultrasonic transducer for broadband, high sensitivity, temperature, electric field stability and performance consistency.

Description

technical field [0001] The invention relates to the field of inorganic non-metal functional materials, in particular to a ternary lead scandate-lead magnesium niobate-lead titanate ceramic and a preparation method thereof, which are suitable for making high-performance ultrasonic and underwater acoustic transducers. Background technique [0002] Ultrasonic testing, as a non-destructive testing technology, has been widely used in many fields such as medical diagnosis, non-destructive testing, and underwater acoustic sonar. In the field of medical ultrasound, the ultrasonic diagnostic system is a device that sends and receives ultrasonic signals and processes ultrasonic information, and has become an indispensable device for doctors to diagnose diseases. The core component of the ultrasonic diagnostic system is the ultrasonic transducer, whose performance and quality directly affect the performance of the entire system. Medical ultrasonic transducers have the following charac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/472C04B35/499C04B35/622
CPCC04B35/472C04B35/499C04B35/622C04B2235/3206C04B2235/3224C04B2235/3234
Inventor 郭菲菲惠增哲龙伟李晓娟方频阳周宏桥贾博周峰峰
Owner XIAN TECHNOLOGICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com