Environment-friendly foam preparation and preparation method thereof

A foam and preparation technology, applied in the field of preparation of environmentally friendly foam preparations, can solve the problems of high cost and environmental pollution of environmentally friendly foam preparations, and achieve the effects of good foaming ability, good corrosion resistance and long shelf life

Inactive Publication Date: 2020-03-31
陕西速源节能科技有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide an environmentally friendly foam preparation, which solves the problem that the pollution of the foam preparation in the prior art will cause great pollution to the environmen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] The present invention also provides a kind of preparation method of environmental protection foam preparation, comprises the following steps:

[0023] Step 1, according to the weight ratio of 1:2:3:4, take respectively sodium α-methyl sulfopalmitate, modified silicone resin polyether emulsion, coconut oil fatty acid diethanolamide and methyl cellulose, and place In the flask, and stir at a speed of 100-200r / min until the mixture is uniform, and the foam stabilizer is obtained;

[0024] Step 2, weigh the following raw materials according to the weight ratio in decibels: sodium lauryl sulfate 5-15%, octylphenol polyoxyethylene ether 2-6%, alkylphenol polyoxyethylene ether 2-6%, methyl iso 0.2-2% thiazolinone, 0.2-1% sodium ethylenediamine tetramethylene phosphonate, 0.2-2% fatty acid diethanolamide, the balance is deionized water, and the water temperature is 30-40°C;

[0025] Step 3, stir and mix the raw materials weighed in step 2 at a speed of 50-100r / min, and slowly ...

Embodiment 1

[0027] Step 1, according to the weight ratio of 1:2:3:4, take respectively sodium α-methyl sulfopalmitate, modified silicone resin polyether emulsion, coconut oil fatty acid diethanolamide and methyl cellulose, and place In the flask, and stir at a speed of 10r / min until uniformly mixed to obtain a foam stabilizer;

[0028] Step 2, weigh the following raw materials according to the weight ratio in decibels: 5% sodium lauryl sulfate, 2% octylphenol polyoxyethylene ether, 2% alkylphenol polyoxyethylene ether, 0.2% methylisothiazolinone, Sodium ethylenediamine tetramethylene phosphonate 0.2%, fatty acid diethanolamide 0.2%, the balance is deionized water, and the water temperature is 30°C;

[0029] Step 3, stir and mix the raw materials weighed in step 2 at a speed of 50 r / min, and slowly add 4% of the foam stabilizer prepared in step 1 according to the weight ratio during the stirring process, and let stand for 20 minutes to obtain an environmentally friendly foam preparation. ...

Embodiment 2

[0031] Step 1, take by weight 1:2:3:4 sodium α-methyl sulfopalmitate, modified silicone resin polyether emulsion, coconut oil fatty acid diethanolamide and methyl cellulose respectively, and place In the flask, and stir at a speed of 200r / min until uniformly mixed to obtain a foam stabilizer;

[0032] Step 2, weigh the following raw materials according to the weight ratio in decibels: 15% sodium lauryl sulfate, 6% octylphenol polyoxyethylene ether, 6% alkylphenol polyoxyethylene ether, 2% methylisothiazolinone, Sodium ethylenediamine tetramethylene phosphonate 1%, fatty acid diethanolamide 2%, the balance is deionized water, and the water temperature is 40°C;

[0033] Step 3, stir and mix the raw materials weighed in step 2 at a speed of 100 r / min, and slowly add 10% of the foam stabilizer prepared in step 1 according to the weight ratio during the stirring process, and let stand for 50 minutes to obtain an environmentally friendly foam preparation.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of environment-friendly product preparation, and provides an environment-friendly foam preparation. The environment-friendly foam preparation is prepared from the following raw materials in percentage by weight: 5-15% of lauryl sodium sulfate, 2-6% of octaphenyl polyoxyethyiene, 2-6% of alkylphenol ethoxylate, 4-10% of a foam stabilizer, 0.2-2% of a preservative, 0.2-1% of a stabilizer, 0.2-2% of a foam aid and the balance of water. All the raw materials are green and environmentally friendly and have biodegradability. The environment-friendly foampreparation has high temperature resistance, the highest temperature can reach 150 DEG C, the high salinity resistance is achieved, the highest salinity can reach 300 g/L, the high oil resistance is achieved, and the highest condensate oil content can reach 30%. Good foaming capability, foam stabilizing capability and liquid carrying capability are achieved. The environment-friendly shield foamingagent disclosed by the invention is stable in quality and good in corrosion resistance, is not influenced by the storage temperature and storage time, and has a relatively long shelf life. The preparation method is simple to operate, easy to prepare and suitable for large-scale production.

Description

technical field [0001] The invention belongs to the technical field of preparation of environment-friendly products, relates to an environment-friendly foam preparation, and also relates to a preparation method of the environment-friendly foam preparation. Background technique [0002] With the rapid development of society and economy and the continuous acceleration of urbanization, the development and utilization of urban underground space has become one of the important directions for the sustainable development of our society. The construction of underground transportation facilities has entered a stage of rapid development. In the shield construction technology of underground engineering that has attracted much attention, the earth pressure balance shield has been widely used due to its advantages of wide application range and low cost, and has become the mainstream of tunnel technology. When excavating in the mode of earth pressure balance, such as in the sand layer, gr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01F17/00B01F17/02B01F17/42C09K8/035C09K23/00C09K23/02C09K23/42
CPCC09K8/035C09K23/00C09K23/018
Inventor 白明明
Owner 陕西速源节能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap