Problems solved by technology

The grouting agent prepared by using these raw materials mixed with cement, although the setting time meets the requirements of relevant standards, it is not controlled within a more reasonable range, and the bleeding rate also needs to be further controlled, and its mechanical strength performance is still limited. room for further improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-strength prestressed tunnel grouting agent
  • A high-strength prestressed tunnel grouting agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The high-strength prestressed channel grouting agent provided in this example includes 39wt% of viscosity modifier, 28wt% of coagulation regulator, 22wt% of modified sodium hydroxide powder, 10.5wt% of water reducer, and 0.5wt% of defoamer ;

[0030] Wherein, the concrete preparation method of viscosity modifier is:

[0031] A1. Take superfine calcium carbonate hollow balls and pullulan polysaccharide according to the weight ratio of 1:2, add water 20 times the weight of pullulan polysaccharide and / or welan gum, and stir for 30min under a pressure of 0.2MPa. 800r / min, to obtain a suspension;

[0032] A2. Take the filter residue by membrane filtration, and vacuum-dry to obtain the finished product of the viscosity modifier. The absorbance of the pullulan in the ultrafine calcium carbonate hollow spheres is detected by a spectrophotometer, and compared with the absorbance of the original pullulan, the encapsulation efficiency of the pulland is measured to be 92.93%.

...

Embodiment 2

[0038] The high-strength prestressed channel grouting agent provided in this embodiment includes 42wt% of viscosity modifier, 30wt% of coagulation regulator, 15wt% of modified sodium hydroxide powder, 12.5wt% of water reducer, and 0.5wt% of defoamer The concrete preparation method of viscosity modifier, coagulation regulator is identical with embodiment 1.

Embodiment 3

[0040] The high-strength prestressed channel grouting agent provided in this example includes 34wt% of viscosity modifier, 27wt% of coagulation regulator, 24wt% of modified sodium hydroxide powder, 14.5wt% of water reducer, and 0.5wt% of defoamer The concrete preparation method of viscosity modifier, coagulation regulator is identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength prestressed channel grouting agent, which comprises a viscosity modifier of 34-42wt%, a coagulation regulator of 22-30wt%, a modified sodium hydroxide powder of 15-24wt%, and a water reducing agent of 3.5-14.5 wt%, defoamer 0.5wt%; Wherein, the viscosity modifier is the ultrafine calcium carbonate hollow sphere that inner cavity is embedded with pullulan and / or welan gum; Fine silica hollow spheres; modified sodium hydroxide powder is paraffin-coated sodium hydroxide powder. The grouting agent uses the synergistic effect of the viscosity modifier, the coagulation agent and the modified sodium hydroxide powder to form a gel grid structure in the grouting agent, and fix the other components of the grouting material on the net. In the grid, on the basis of ensuring the ideal construction time and setting time, the mechanical strength performance of the grouting material finally prepared by using this grouting agent is improved to the greatest extent.

Description

technical field [0001] The invention belongs to the field of grouting agents, in particular to a high-strength prestressed tunnel grouting agent. Background technique [0002] Prestressed concrete members have the characteristics of high rigidity, high strength, strong shear resistance and good fatigue resistance, which can effectively reduce the structural section size, reduce self-weight, prevent cracking and reduce deflection. be widely used. Prestressed concrete components need to reserve holes during processing to allow prestressed steel bars to pass through, and fill the holes with grout after prestressing the prestressed steel bars, so that the prestressed steel bars can be combined with the structural concrete. They can give full play to their strengths and obtain excellent mechanical properties and structural properties. The performance indicators of this prestressed channel grouting agent must meet the "Technical Specifications for Highway Bridge and Culvert Cons...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/42C04B24/10C04B24/38C04B22/06C04B20/10C04B103/22C04B103/44
CPCC04B40/0039C04B20/1044C04B2103/22C04B2103/445C04B22/062C04B2103/302C04B24/42C04B28/04C04B22/10C04B24/38C04B22/06C04B24/10
Inventor 汪进国郭偲
Owner 武汉品泰特种建材科技有限公司