Graphene composite sand-in-sand multicolor paint and preparation method thereof

A graphene composite and colorful paint technology, applied in the field of paint, can solve the problems of shortened service life, limited application scope, poor scrub resistance, etc., and achieves the effect of prolonging service life, improving mechanical properties and low cost

Active Publication Date: 2020-05-01
NINGBO MORSH TECH
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the colorful coatings on the market have problems such as water resistance, alkali resistance, poor scrub resistan

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene composite sand-in-sand multicolor paint and preparation method thereof
  • Graphene composite sand-in-sand multicolor paint and preparation method thereof
  • Graphene composite sand-in-sand multicolor paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A graphene composite sand-in-sand multi-color paint, mainly composed of protective colloid solution, base paint solution and continuous phase solution, the mass ratio of protective colloid solution, basic paint solution and continuous phase solution is 1:2:3, wherein the protective colloid The solution is composed of the following raw materials and their mass percentages: deionized water 95%, protective rubber powder 4.8%, bactericidal preservative 0.2%; the base paint solution is composed of the following raw materials and their mass percentages: deionized water 31.05%, cellulose 0.7% , 0.2% graphene, 0.5% defoamer, 0.4% dispersant, 0.7% film-forming aid, 0.7% antifreeze, 0.15% pH regulator, 5% protective gel solution, 0.3% thickener, bactericidal preservative 0.3%, film-forming resin 15%, curing agent 2%, colored sand 43%; the continuous phase solution consists of the following raw materials and their mass percentages: deionized water 10%, cellulose 0.15%, graphene 0.2...

Embodiment 2

[0042] A kind of graphene composite sand-in-sand colorful coating, mainly is made up of protective colloid solution, basic paint solution and continuous phase solution, and the mass ratio of protective colloid solution, basic paint solution and continuous phase solution is 1:1:3, wherein protective colloid The solution is composed of the following raw materials and their mass percentages: 96% deionized water, 4% protective rubber powder; the base paint solution is composed of the following raw materials and their mass percentages: 40% deionized water, 0.3% cellulose, 0.05% graphene, 0.1% defoamer, 0.05% dispersant, 0.4% film-forming aid, 0.2% antifreeze, 0.05% pH regulator, 2% protective glue solution, 0.1% bactericidal preservative, 10% film-forming resin, colored sand 46.75 %; The continuous phase solution is composed of the following raw materials and their mass percentages: 11.43% deionized water, 0.05% cellulose, 0.05% graphene, 0.05% dispersant, 0.05% leveling agent, 0.2%...

Embodiment 3

[0049] A kind of graphene composite sand-in-sand colorful coating, mainly is made up of protective colloid solution, basic paint solution and continuous phase solution, and the mass ratio of protective colloid solution, basic paint solution and continuous phase solution is 1:2:5, wherein protective colloid The solution is composed of the following raw materials and their mass percentages: deionized water 90%, protective rubber powder 9.2%, bactericidal preservative 0.8%; the base paint solution is composed of the following raw materials and their mass percentages: deionized water 25%, cellulose 1% , 0.5% graphene, 0.8% defoamer, 0.8% dispersant, 1% film-forming aid, 1.2% antifreeze, 0.3% pH regulator, 8% protective gel solution, 0.8% thickener, bactericidal preservative 0.5%, film-forming resin 20%, curing agent 4%, colored sand 36.1%; the continuous phase solution consists of the following raw materials and their mass percentages: deionized water 20%, cellulose 0.3%, graphene ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a graphene composite sand-in-sand multicolor paint and a preparation method thereof, and is characterized in that the graphene composite sand-in-sand multicolor paint is mainlycomposed of a protective glue solution, a base paint solution and a continuous phase solution, the mass ratio of the protective glue solution to the base paint solution to the continuous phase solution is 1:2:3, and the protective glue solution is composed of deionized water, protective glue powder and a bactericidal preservative; the base paint solution is prepared from deionized water, cellulose, graphene, a defoaming agent, a dispersing agent, a coalescing agent, an anti-freezing agent, a pH regulator, a protective glue solution, a thickening agent, a bactericidal preservative, film-forming resin, a curing agent and color sand; the continuous phase solution is prepared from deionized water, cellulose, graphene, a dispersing agent, an antifoaming agent, a leveling agent, a coalescing agent, an anti-freezing agent, a sterilization preservative, a pH regulator, film-forming resin and colored sand. The graphene composite sand-in-sand multicolor paint and the preparation method thereofhave the advantage that the water resistance, the alkali resistance, the scrub resistance and the fusion degree of colored points after coating of the coating can be improved.

Description

technical field [0001] The invention belongs to the field of coatings, in particular to a graphene composite sand-in-sand colorful coating and a preparation method thereof. . Background technique [0002] With the rapid development of the economy and the continuous improvement of living standards, people are not satisfied with simple decoration of their living space, and various materials are applied to architectural decoration, including the application of natural stone. In particular, a large number of rough stones are applied to architectural decoration. Compared with other stone-like materials: real stone paint, rock flake paint, water-in-water, and sand-in-water, sand-in-sand presents a more realistic visual effect of lychee surface and fire surface. Compared with the current products on the market, the effect of imitating the "concave-convex surface" of stone materials is not ideal. Compared with other imitation stone materials, it has certain advantages in color sta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/06C04B26/32C04B26/08C04B18/02C04B111/82C04B111/20C04B111/27
CPCC04B18/022C04B26/06C04B26/08C04B26/32C04B2111/00482C04B2111/20C04B2111/27C04B2111/82C04B24/383C04B14/024C04B2103/408C04B24/42C04B24/32C04B24/16C04B24/02C04B24/045C04B24/023C04B24/121C04B2103/0068C04B14/06C04B18/027C04B2103/44C04B22/00C04B2103/54
Inventor 王仕新付绪兵
Owner NINGBO MORSH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap