Anti-fading plastic for color woven bag production

A fade-resistant, woven bag technology, applied in the field of woven bag production, to achieve the effects of low cost, good fade-resistant effect and good optical performance

Inactive Publication Date: 2020-05-05
福建海嘉包装有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] There is no material in the existing products that is used for the anti-fading plastic of woven bags as a production material. Therefore, a kind of anti-fading plastic for the production of color woven bags is needed to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An anti-fading plastic for the production of color woven bags, characterized in that it comprises the following raw materials in parts by weight: 5 parts of polymethyl methacrylate, 4 parts of polycarbonate, 3 parts of phase solvent, 6 parts of tea polyphenols, acetic acid 3 parts, 5 parts of salt water, 8 parts of mulberry leaf water, 4 parts of sodium silicate, 10 parts of phenolsulfonic acid, 2 parts of composite catalyst; the specific preparation method of the anti-fading plastic is as follows:

[0024] S1, equipment processing and batching: clean the used container equipment with tap water, rinse it again with deionized water, disinfect it with an ethanol solution with a volume fraction of 75% and rinse it with deionized water for later use, and use the above-mentioned raw materials in parts by weight Weigh raw materials;

[0025] S2, mixing materials: polymethyl methacrylate and polycarbonate are mixed and pre-dissolved, and the phase solvent is weighed according ...

Embodiment 2

[0029] An anti-fading plastic for the production of color woven bags, characterized in that it comprises the following raw materials in parts by weight: 15 parts of polymethyl methacrylate, 8 parts of polycarbonate, 7 parts of phase solvent, 8 parts of tea polyphenols, acetic acid 5 parts, 7 parts of salt water, 12 parts of mulberry leaf water, 8 parts of sodium silicate, 12 parts of phenolsulfonic acid, 5 parts of composite catalyst; the specific preparation method of the anti-fading plastic is as follows:

[0030] S1, equipment processing and batching: clean the used container equipment with tap water, rinse it again with deionized water, disinfect it with an ethanol solution with a volume fraction of 75% and rinse it with deionized water for later use, and use the above-mentioned raw materials in parts by weight Weigh raw materials;

[0031] S2, mixing materials: polymethyl methacrylate and polycarbonate are mixed and pre-dissolved, and the phase solvent is weighed accordin...

Embodiment 3

[0035] An anti-fading plastic for the production of color woven bags, characterized in that it comprises the following raw materials in parts by weight: 20 parts of polymethyl methacrylate, 5 parts of polycarbonate, 12 parts of phase solvent, 12 parts of tea polyphenols, acetic acid 8 parts, 9 parts of salt water, 18 parts of mulberry leaf water, 12 parts of sodium silicate, 15 parts of phenolsulfonic acid, 9 parts of composite catalyst; the specific preparation method of the anti-fading plastic is as follows:

[0036] S1, equipment processing and batching: clean the used container equipment with tap water, rinse it again with deionized water, disinfect it with an ethanol solution with a volume fraction of 75% and rinse it with deionized water for later use, and use the above-mentioned raw materials in parts by weight Weigh raw materials;

[0037] S2, mixing materials: polymethyl methacrylate and polycarbonate are mixed and pre-dissolved, and the phase solvent is weighed accor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-fading plastic for color woven bag production, and belongs to the technical field of woven bag production. The anti-fading plastic comprises the following raw materialsby weight: 5-20 parts of polymethyl methacrylate, 4-15 parts of polycarbonate, 3-12 parts of a phase solvent, 6-12 parts of tea polyphenol, 3-8 parts of acetic acid, 5-9 parts of brine, 8-18 parts ofmulberry leaf water, 4-12 parts of sodium silicate, 10-15 parts of phenolsulfonic acid, and 2-9 parts of a composite catalyst. The specific preparation method of the anti-fading plastic comprises thefollowing steps: equipment treatment and burdening: cleaning used container equipment with tap water, and performing washing with deionized water once. The anti-fading plastic has the advantages of the good anti-fading effect, the good optical performance, the good chemical corrosion resistance, no shedding, fading or other phenomena, good chemical stability and strong tinting strength; and the anti-fading plastic is low in material cost and high in environmental protection property, and has an antibacterial effect on fabrics.

Description

technical field [0001] The invention belongs to the technical field of woven bag production, and in particular relates to an anti-fading plastic used in the production of colored woven bags. Background technique [0002] Woven bag, also known as snakeskin bag, is a kind of plastic, used for packaging, and its raw materials are generally various chemical plastic materials such as polyethylene and polypropylene. Woven bags are widely used, mainly used for packaging and packaging of various items, and are widely used in industry. [0003] Due to product resources and price issues, 6 billion woven bags are used for cement packaging in my country every year, accounting for more than 85% of bulk cement packaging. With the development and application of flexible container bags, plastic woven container bags are widely used at sea. Transportation and packaging industrial and agricultural products. In agricultural product packaging, plastic woven bags have been widely used in aquatic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L33/12C08L69/00C08K13/02C08K3/34C08K5/42C08K5/09
CPCC08L33/12C08L2205/03C08L69/00C08K13/02C08K3/34C08K5/42C08K5/09
Inventor 刘祥招刘杰鲍必钻
Owner 福建海嘉包装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com