A nitrogen-doped molybdenum disulfide/graphene composite material

A molybdenum disulfide and composite material technology, applied in structural parts, electrical components, battery electrodes, etc., can solve the problems of low nitrogen doping content of nitrogen doping precursors, complex equipment, low product utilization rate, etc., and achieve difficult particle accumulation. , The effect of uniform nitrogen doping and fast heating

Active Publication Date: 2021-07-09
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems in the preparation of nitrogen-doped molybdenum disulfide / graphene composite materials in the prior art, the equipment is complicated, the process is cumbersome, the operation is complicated and time-consuming, the product utilization rate is low, the raw material is difficult to obtain, and the nitrogen-doped precursor is lost in a large amount during the nitrogen doping process. Due to the low nitrogen doping content and the aggregation and accumulation of nanoparticles during the long-term heat treatment of active components and graphene, the present invention provides an efficient, fast, and large-scale synthesis of high nitrogen content doped molybdenum disulfide / graphene The method of composite materials, the obtained material has high nitrogen content, and the utilization rate of raw materials is significantly improved. The product does not need washing, separation, drying and other processes, and can be directly used as a negative electrode material for lithium batteries, with good application performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A nitrogen-doped molybdenum disulfide/graphene composite material
  • A nitrogen-doped molybdenum disulfide/graphene composite material
  • A nitrogen-doped molybdenum disulfide/graphene composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] (1) Weigh 1.0g of graphene oxide and disperse it in 20mL of 37% formaldehyde aqueous solution, place it in an ultrasonic instrument and disperse evenly, record it as dispersion A.

[0039] (2) Weigh 3.0g of melamine and 5.0g of ammonium tetrathiomolybdate and add them into 40mL of deionized water, place them in an ultrasonic instrument and ultrasonically disperse evenly, and record it as dispersion liquid B.

[0040] (3) Mix Dispersion A and Dispersion B, raise the temperature of the water bath to 60°C and stir for 10 minutes. Then triethanolamine was added to the reaction solution to adjust the pH value of the reaction solution system to 8.0, and the mixture was uniformly mixed by ultrasonic, then the reaction solution was poured into a high-pressure reactor, and the temperature was raised to 120° C. for 12 hours to react. Suction filtration, vacuum drying to obtain a black solid powder.

[0041] (4) Put the black solid powder obtained in step (3) into a microwave rea...

Embodiment 2

[0043] (1) Weigh 1.0g graphene oxide and disperse it in 30mL 37% formaldehyde aqueous solution, place it in an ultrasonic instrument and disperse evenly, record it as dispersion liquid A.

[0044] (2) Weigh 5.0g of melamine and 8.0g of ammonium tetrathiomolybdate and add them into 40mL of deionized water, place them in an ultrasonic instrument and ultrasonically disperse evenly, and record it as dispersion liquid B.

[0045] (3) Mix Dispersion A and Dispersion B, raise the temperature of the water bath to 60°C and stir for 10 minutes. Then triethanolamine was added to the reaction solution to adjust the pH value of the reaction solution system to 8.0, and the mixture was uniformly mixed by ultrasonic, then the reaction solution was poured into a high-pressure reactor, and the temperature was raised to 120° C. for 12 hours to react. Suction filtration, vacuum drying to obtain a black solid powder.

[0046] (4) Put the black solid powder obtained in step (3) into a microwave re...

Embodiment 3

[0048] (1) Weigh 1.0g graphene oxide and disperse it in 30mL 37% formaldehyde aqueous solution, place it in an ultrasonic instrument and disperse evenly, record it as dispersion liquid A.

[0049] (2) Weigh 10.0g of melamine and 10.0g of ammonium tetrathiomolybdate and add them into 40mL of deionized water, place them in an ultrasonic apparatus and ultrasonically disperse evenly, and record it as dispersion liquid B.

[0050] (3) Mix Dispersion A and Dispersion B, raise the temperature of the water bath to 70°C and stir for 10 minutes. Then triethanolamine was added to the reaction solution to adjust the pH value of the reaction solution system to 8.0, and the mixture was uniformly mixed by ultrasonic, then the reaction solution was poured into a high-pressure reactor, and the temperature was raised to 120° C. for 12 hours to react. Suction filtration, vacuum drying to obtain a black solid powder.

[0051] (4) Put the black solid powder obtained in step (3) into a microwave r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical conductivityaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

A nitrogen-doped molybdenum disulfide / graphene composite material, which uses formaldehyde as a bridge to make it moderately cross-linked with melamine to form a nitrogen-doped precursor, and then undergoes hydrothermal reaction to make the nitrogen-doped precursor, active components and graphene The interaction is uniformly fused, and then a solvent-free microwave reaction is performed to synthesize a high nitrogen content doped molybdenum disulfide / graphene composite. The composite material of the present invention avoids the loss caused by the sublimation of the nitrogen-doped precursor in the heating process in the traditional nitrogen-doping process during the preparation process, improves the efficiency of nitrogen doping, and the reaction conditions are progressive from mild to strong, and realizes the nitrogen-doped precursor and the active group. The points interact with graphene to fuse uniformly. The prepared nitrogen-doped molybdenum disulfide / graphene composite material has good stability, is not easily denatured in the air, is easy to store, and has a large specific surface area. specific capacity and good cycle stability.

Description

technical field [0001] The invention relates to a nitrogen-doped molybdenum disulfide / graphene composite material, in particular to a molybdenum disulfide / graphene lithium battery negative electrode material doped with high nitrogen content, and provides a preparation method thereof, belonging to nanocomposite materials and applications thereof technology field. Background technique [0002] Graphene is a two-dimensional honeycomb lattice structure carbonaceous material that is tightly packed by a single layer of carbon atoms. Since the discovery by Andre K. Geim of the University of Manchester in 2004, graphite Enenes have received great attention in both experimental and theoretical sciences. Graphene is only one carbon atom thick, making it the thinnest known material, yet extremely strong and hard, stronger than diamond and 100 times stronger than the world's hardest steel. Due to its special nanostructure and excellent performance, it has potential application prospec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/38H01M4/58H01M4/583
CPCH01M4/36H01M4/38H01M4/58H01M4/583Y02E60/10
Inventor 郭金廖莎凌凤香张会成王少军
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com