Production process of ice oxygen bar cool-feel bacteriostatic water-repellent fabric

A production process, oxygen bar technology, applied in the directions of adding compressed water, fabric surface trimming, and improving hand-feeling fibers, etc., can solve the problems of single-function fabrics, unsuitable for summer sportswear, etc., achieve smooth hand feel, inhibit bacterial growth, and good The effect of antibacterial health properties

Inactive Publication Date: 2020-05-08
JIANGSU DONGYUAN TEXTILE SCI & TECH IND
View PDF13 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The weather is hot in summer, and people urgently need multi-functional, fashionable sportswear suitable for outdoor sports in summer. Therefore, not only fabrics are required to be comfortable, smooth, moisture-wicking, skin-friendly, but also cool and water-repellent. Traditional clothing fabrics have single functions and are not suitable for making summer sportswear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The production process of ice oxygen bar cool antibacterial and water-repellent fabric is as follows: weaving→pretreatment→dyeing→dehydration→cutting→drying→setting→preshrinking→finished product,

[0018] (1) During weaving: the fabric is woven from 40S blended yarn and 30D spandex yarn on a 34-inch 32G single-sided circular knitting machine according to the weaving method of weft flat stitch. The grammage of the woven fabric is 160g / m 2 , the blended yarn is made of viscose fiber, cotton and ice oxygen bar fiber. The mass proportion of each component in the fabric is: viscose fiber accounts for 49.4%, cotton fiber accounts for 29.4%, ice oxygen bar fiber accounts for 19.2%, spandex yarn 2%;

[0019] (2) During pre-treatment: firstly pre-set the woven fabric on the setting machine to ensure the dimensional stability of the fabric, the pre-setting temperature is 185°C, and the pre-setting speed is 23m / min; then dye the machine with a bath ratio of 1:8 Put the dyeing va...

Embodiment 2

[0026] The production process of ice oxygen bar cool antibacterial and water-repellent fabric is as follows: weaving→pretreatment→dyeing→dehydration→cutting→drying→setting→preshrinking→finished product,

[0027] (1) During weaving: the fabric is woven from 32S blended yarn and 20D spandex yarn on a 34-inch 32G single-jersey circular knitting machine according to the weaving method of weft flat stitch. The grammage of the woven fabric is 155g / m 2 , the blended yarn is made of viscose fiber, cotton and ice oxygen bar fiber. The mass proportion of each component in the fabric is: viscose fiber accounts for 49.6%, cotton fiber accounts for 29.6%, ice oxygen bar fiber accounts for 19.8%, spandex yarn 1%;

[0028] (2) During pre-treatment: first pre-set the woven fabric on the setting machine to ensure the dimensional stability of the fabric, the pre-setting temperature is 180°C, and the pre-setting speed is 18m / min; then dye the machine with a bath ratio of 1:8 Put the dyeing vat...

Embodiment 3

[0035] The production process of ice oxygen bar cool antibacterial and water-repellent fabric is as follows: weaving→pretreatment→dyeing→dehydration→cutting→drying→setting→preshrinking→finished product,

[0036] (1) During weaving: the fabric is woven from 36S blended yarn and 25D spandex yarn on a 34-inch 32G single-sided circular knitting machine according to the weaving method of weft flat stitch. The grammage of the woven fabric is 165g / m 2 , the blended yarn is made of viscose fiber, cotton and ice oxygen bar fiber. The mass proportion of each component in the fabric is: viscose fiber accounts for 49.5%, cotton fiber accounts for 29.5%, ice oxygen bar fiber accounts for 19.5%, spandex yarn 1.5%;

[0037] (2) During pre-treatment: first pre-set the woven fabric on the setting machine to ensure the dimensional stability of the fabric. The pre-setting temperature is 190°C and the pre-setting speed is 28m / min; then dye the machine with a bath ratio of 1:8 Put the dyeing vat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a production process of an ice oxygen bar cool-feel bacteriostatic water-repellent fabric. The fabric is woven by blended yarns with the fineness of 32-40S and 20-30D spandex yarns on a knitted single-side circular knitting machine according to a weft plain stitch weaving mode, wherein the blended yarns are woven by viscose fibers, cotton and ice oxygen bar fibers in a blending mode, and the production process comprises the steps of weaving, pretreating, dyeing, dewatering, slitting, drying, shaping, preshrinking and finished product obtaining. According to theproduction process, the blended yarns woven by viscose fibers, cotton and ice oxygen bar fibers in a blending mode and the spandex yarns are selected to weave the fabric, so that the fabric not only has the hygroscopicity of viscose and cotton, but also has the low-temperature cool sense characteristics of the ice oxygen bar fiber, the fabric has excellent moisture absorption and sweat dischargingperformance, even in a humid environment, also can keep the skin dry and comfortable, thereby effectively inhibiting the growth of bacteria, and the fabric has good bacteriostasis and health care performance; and the outer layer of the fabric is subjected to water repellent finishing, so that the fabric water repellent effect is relatively high.

Description

technical field [0001] The invention relates to the field of fabric production technology, in particular to the production technology of antibacterial and water-repellent fabric with cool feeling in ice oxygen bar. Background technique [0002] With the rapid economic development in the 21st century, more and more people accept the concept of outdoor sports as a healthy life, and the styles and functions of outdoor sportswear are becoming more and more diverse. The weather is hot in summer, and people urgently need multi-functional, fashionable sportswear suitable for outdoor sports in summer. Therefore, not only fabrics are required to be comfortable, smooth, moisture-wicking, skin-friendly, but also cool and water-repellent. Traditional clothing fabrics have single functions and are not suitable for making summer sportswear. Contents of the invention [0003] The technical problem to be solved by the present invention is: to provide a production process of ice oxygen ba...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/14D06C7/02D06C21/00D06M15/256D06P1/38D06P1/673D06P3/85D06M101/06D06M101/38
CPCD04B1/14D06C7/02D06C21/00D06M15/256D06M2101/06D06M2101/38D06M2200/12D06M2200/50D06P1/38D06P1/6735D06P3/828D10B2201/02D10B2201/24D10B2331/10D10B2401/13D10B2501/04
Inventor 董涛涛李娟李慧兰徐仁琴尹巍巍
Owner JIANGSU DONGYUAN TEXTILE SCI & TECH IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap