High-damping composite foam and preparation method thereof
A composite foam, high damping technology, applied in the field of composite foam, can solve the problems of composite foam vibration damage, reduce service life, etc., achieve the effect of reducing water pressure shock resistance, improving service life, and simple molding process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] Embodiment 1: see figure 1 , a high damping composite foam, comprising a first hollow microbead foam layer 1, a second hollow microbead foam layer 2, a rubber damping layer arranged in the middle of the first hollow microbead foam layer 1 and the second hollow microbead foam layer 2 The support layer 3, the rubber damping support layer 3 is zigzag, and the elastic body 4 is filled in the zigzag gap, and the first hollow microbead foam layer 1, the second hollow microbead foam layer 2 and the rubber damping support layer 3 are integrally cured forming.
[0029] The first hollow microsphere foam layer 1 and the second hollow microsphere foam layer 2 are prepared by resin, hollow glass microspheres, curing agent, accelerator, and diluent in a mass ratio of 100:20:50:3:12. become.
[0030] The resin is one or more of epoxy resin system, phenolic resin system, unsaturated resin system and other resins with bonding effect, and the density of the hollow glass microspheres is...
Embodiment 2
[0032] Embodiment 2: the preparation method of the high damping composite foam described in embodiment 1 may further comprise the steps:
[0033] ① Mix resin, hollow glass microspheres, curing agent, accelerator, and diluent in a mass ratio of 100:20:50:3:12 to obtain mixed slurry A;
[0034] ② Spread the mixed slurry A in the mold, and then lay a layer of rubber damping support layer B on its surface;
[0035] ③Fill the elastic body C in the zigzag gap of the rubber damping support layer B;
[0036] ④ Then continue to coat the mixed slurry A on the surface of the rubber damping support layer B;
[0037] ⑤ Lay in the manner of A-B-C-A in turn until the composite foam D of the required thickness is obtained.
[0038] ⑥Put the mold in an oven to heat up and cure to obtain a high-damping composite foam.
[0039] In step ⑥, the curing process is firstly curing at 50°C for 1 hour, then holding at 110°C for 1.5 hours, and finally holding at 150°C for 2 hours.
Embodiment 3
[0040] Embodiment 3: a kind of preparation method of high damping composite foam, comprises the following steps:
[0041] ① Mix resin, hollow glass microspheres, curing agent, accelerator, and diluent in a mass ratio of 100:10:10:1:10 to obtain mixed slurry A;
[0042] ② Spread the mixed slurry A in the mold, and then lay a layer of rubber damping support layer B on its surface;
[0043] ③Fill the elastic body C in the zigzag gap of the rubber damping support layer B;
[0044] ④ Then continue to coat the mixed slurry A on the surface of the rubber damping support layer B;
[0045]⑤ Lay in the manner of A-B-C-A in turn until the composite foam D of the required thickness is obtained.
[0046] ⑥Put the mold in an oven to heat up and cure to obtain a high-damping composite foam.
[0047] In step ⑥, the curing process is to firstly cure at 40°C for 1.5 h, then hold at 100°C for 2 h, and finally hold at 140°C for 3 h.
[0048] Among them, the resin is an epoxy resin system, and...
PUM
Property | Measurement | Unit |
---|---|---|
density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com