Antiviral flame-retardant weather-resistant coating

A weather-resistant coating and anti-virus technology, applied in fire-resistant coatings, anti-fouling/underwater coatings, coatings, etc., can solve the problems that the anti-virus effect needs to be further improved, the cell membrane of germs needs to be destroyed, and the comprehensive performance of the coating needs to be further improved. Low preparation cost, good comprehensive performance, improved service life and antiviral persistence

Inactive Publication Date: 2020-05-22
HUNAN CHENLI NEW MATERIAL CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The product of this invention makes full use of the characteristics that the active ingredients of Chinese herbal medicine can inhibit the proliferation of bacteria and fungi, destroy the cell membrane of germs, destroy the shell of viruses and the structure of RNA, etc., combined with modern paint making technology, the active ingredients can be slowly released in the coating and play a long-term role. However, due to the completely different coating environment and human environment, the anti-virus effect needs to be further improved
And the overall performance of the coating needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] An anti-virus, flame-retardant and weather-resistant paint, which is composed of the following components in parts by weight: 2 parts of epoxy hexamethylenetetramine salt, 4-propenylthiosemicarbazide / 1-allyl-3-methyl Imidazole chloride / zeatin nucleoside / isobornyl acrylate copolymer 30 parts, modified Ti-Cu-Hf-O 5 parts, anti-viral Chinese herbal medicine powder 1 part, sepiolite powder 10 parts, cyclohexanone 10 parts, 1 part of sodium hexametaphosphate and 0.5 part of tributyl phosphate.

[0037] The preparation method of the epoxy hexamethylenetetramine salt includes the following steps: adding hexamethylenetetramine and epichlorohydrin to chloroform, then adding sodium hydroxide to it, and stirring at 60°C After reacting for 3 hours, the insoluble matter was removed by filtration, and the chloroform was removed by rotary evaporation to obtain epoxy hexamethylenetetramine salt; the molar ratio of the hexamethylenetetramine, epichlorohydrin, chloroform, and sodium hydroxi...

Embodiment 2

[0045] An anti-viral, flame-retardant and weather-resistant coating consisting of the following components in parts by weight: 3 parts of epoxy hexamethylenetetramine salt, 4-propenylthiosemicarbazide / 1-allyl-3-methyl 33 parts of chloroimidazole / zeatin nucleoside / isobornyl acrylate copolymer, 6 parts of modified Ti-Cu-Hf-O, 1.5 parts of anti-viral Chinese herbal medicine powder, 11 parts of light calcium carbonate, methyl isobutyl 11 parts of ketones, 1.5 parts of sodium polycarboxylate, 0.7 parts of defoamer Deqian 3100.

[0046] The preparation method of the epoxy hexamethylenetetramine salt includes the following steps: adding hexamethylenetetramine and epichlorohydrin to chloroform, then adding potassium hydroxide to it, and stirring at 62°C Reacted for 3.5 hours, then filtered to remove the insoluble matter, and then rotated to remove the chloroform to obtain epoxy hexamethylenetetramine salt; the molar ratio of the hexamethylenetetramine, epichlorohydrin, chloroform, and po...

Embodiment 3

[0054] An anti-virus, flame-retardant and weather-resistant paint, which is composed of the following components in parts by weight: 3.5 parts of epoxy hexamethylenetetramine salt, 4-propenyl thiosemicarbazide / 1-allyl-3-methyl Imidazole chloride / zeatin nucleoside / isobornyl acrylate copolymer 35 parts, modified Ti-Cu-Hf-O 6.5 parts, antiviral Chinese herbal medicine powder 2 parts, titanium dioxide 13 parts, N-methylpyrrolidone 13 parts , 2 parts of sodium hexametaphosphate, 1 part of defoamer BYK088.

[0055] The preparation method of the epoxy hexamethylenetetramine salt includes the following steps: adding hexamethylenetetramine and epichlorohydrin to chloroform, then adding sodium carbonate to it, and stirring and reacting at 65°C After 4 hours, filter to remove insoluble matter, and then rotate to remove chloroform to obtain epoxy hexamethylenetetramine salt; the molar ratio of hexamethylenetetramine, epichlorohydrin, chloroform, and sodium carbonate is 1 :4:18:1.

[0056] Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses antiviral flame-retardant weather-resistant coating. The coating is characterized in that the coating comprises, by weight, 2 to 5 parts of epoxy hexamethylene tetramine salt,30-40 parts of a 4-propenylthiosemicarbazide/1-allyl-3-methylimidazolium chloride/zeatin nucleoside/isobornyl acrylate copolymer, 5-8 parts of modified Ti-Cu-Hf-O, 1-3 parts of antiviral Chinese herbal medicine powder, 10-15 parts of an inorganic filler, 10-15 parts of a solvent, 1-3 parts of a dispersing agent and 0.5-1.5 parts of a defoaming agent. The invention also discloses a preparation method of the antiviral flame-retardant weather-resistant coating. The antiviral flame-retardant weather-resistant coating disclosed by the invention is excellent in comprehensive performance, remarkablein antiviral effect, good in weather resistance and flame resistance, high in bonding strength with a base material and long in service lifetime.

Description

Technical field [0001] The invention relates to the technical field of coatings, in particular to an anti-virus, flame-retardant and weather-resistant coating and a preparation method thereof. Background technique [0002] In recent years, the emergence of highly pathogenic viruses such as influenza virus and enterovirus and some bacteria that are highly resistant to common fungicides have made public places such as hospitals, schools and other crowded places extremely vulnerable to outbreaks. In places with sexual diseases, especially in public health facilities such as hospitals, the possibility of the emergence of viruses and germs is extremely high, which is harmful to public health. Especially with the extensive development of modern industry, the environmental air quality is poor, and the number of people who suffer from viral infections is huge each year. In the season of high incidence of viral infections, students are suspended due to the virus and workers are suspended ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D139/04C09D5/18C09D5/14C09D7/61C09D7/62C09D7/63C08F226/02C08F226/06C08F220/18
CPCC08F220/18C08F226/02C08F226/06C08K2003/2241C08K2003/265C09D5/14C09D5/18C09D139/04C09D7/61C09D7/62C09D7/63C08L99/00C08K13/06C08K9/06C08K3/22C08K5/3477C08K3/346C08K3/26C08K3/34
Inventor 曹冰余香兰
Owner HUNAN CHENLI NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap