Nickel-zinc ferrite material and preparation method thereof

A technology of nickel-zinc ferrite and raw materials, which is applied in the direction of magnetic materials, inorganic materials, magnetic objects, etc., can solve the problems of low magnetic permeability, low Curie temperature, low high-frequency impedance, etc., and achieve low production cost, Achieve mass production, the effect of good high-frequency impedance characteristics

Active Publication Date: 2020-05-29
HENGDIAN GRP DMEGC MAGNETICS CO LTD
View PDF25 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to overcome the problems of low magnetic permeability, low high-frequency impedance and low Curie temperature of the existing nickel-zinc ferrite material, the present invention provides a high-performance anti-EMI material with high magnetic permeability, high Bs, and high impedance. Nickel zinc ferrite material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nickel-zinc ferrite material and preparation method thereof
  • Nickel-zinc ferrite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] (1) Ingredients: According to Table 1, Fe 2 o 3 , ZnO, NiO and CuO forms to calculate the ratio, weigh Fe 2 o 3 49.4mol%, NiO 12mol%, ZnO 32mol%, CuO 6.6mol%, as the main components;

[0039] (2) One-time sand milling: add the main component in the sand mill, then add deionized water for mixing and crushing, and the time is 40 minutes; after mixing evenly, carry out spray granulation to obtain spray material;

[0040] (3) pre-burning

[0041] Put the spray material into the rotary kiln pre-calcination furnace, and pre-fire it at 700°C for 5 hours, and the feed rate is 240 kg / hour;

[0042] (4) Secondary sanding

[0043] Add the following additive components by weight percentage of the pre-fired material in the pre-fired material: SiO 2 0.006wt%, CaCO 3 0.15wt%, V 2 o 5 0.08wt%, Bi 2 o 3 0.12wt%, then put the powder into a sand mill and add deionized water for secondary sand milling, the feed rate is 240Kg / hour (calculated as dry powder); the particle size...

Embodiment 2-7

[0051] The difference between Examples 2-7 and Example 1 is that the formulations of the main components are different, as shown in Table 1, and the rest of the processes are identical.

Embodiment 8-9

[0058] The difference between Examples 8-9 and Example 1 is that the formulations of the additives are different, as shown in Table 2, and the rest of the processes are identical.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Curie pointaaaaaaaaaa
Curie pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of soft magnetic ferrite. The invention aims to solve the problems of low magnetic conductivity, low high-frequency impedance and low Curie temperature ofan existing nickel-zinc ferrite material. The invention provides a nickel-zinc ferrite material and a preparation method thereof. The nickel-zinc ferrite material is composed of a main component and an additive, wherein the main component is composed of the following raw materials in mole percentage: 48-49.6 mol% of Fe2O3, 10-14 mol% of NiO, 30-35 mol% of ZnO and the balance being CuO; based on the total mass of the main component, the additive is composed of the following raw materials in percentage by weight: 0.005 to 0.012 wt% of SiO2, 0.08 to 0.2 wt% of CaCO3, 0.05 to 0.35 wt% of V2O5, and0.1 to 0.4 wt% of Bi2O3. All the components of the NiZn ferrite material have a synergistic effect, the NiZn ferrite material can be sintered at the temperature of 1100 DEG C or below, the resistivity of the obtained material is 10<9> Ohm*cm or above, and the insulation effect can be achieved; the initial permeability of the obtained material is 2000, and the material has good high-frequency impedance characteristics and is especially suitable for manufacturing EMI-resistant and common-mode design products. The preparation method has the advantages of easy control of process conditions, low production cost, no special requirements on equipment, and realization of batch production.

Description

technical field [0001] The invention relates to the technical field of soft magnetic ferrite, in particular to an EMI suppression product, which can be widely used in high Bs and high impedance in the fields of communications, automobiles, office automation equipment, electronic data processing equipment, consumer electronic products, and household appliances. Nickel zinc ferrite material and preparation method thereof. Background technique [0002] Due to the characteristics of high magnetic permeability, high resistivity, and high frequency of use, nickel-zinc ferrite is widely used in computers, communications, and consumer electronics. At present, the main problems of NiZn-based ferrite materials in China are as follows: 1) The magnetic permeability of the material reaches more than 1500, the saturation magnetic induction Bs is about 250mT (room temperature), and the Curie temperature Tc is 100°C, which cannot meet the high current. and high-density installation (limite...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/26C04B35/622C04B35/64H01F1/34
CPCC04B35/2633C04B35/265C04B35/622C04B35/64C04B2235/3208C04B2235/3239C04B2235/3279C04B2235/3281C04B2235/3284C04B2235/3298C04B2235/3418C04B2235/6562C04B2235/6565C04B2235/6567C04B2235/6583H01F1/344
Inventor 蒋玉梅朱晓丽陈军林
Owner HENGDIAN GRP DMEGC MAGNETICS CO LTD