Carving glue and synthesis process thereof

A technology of synthesis process and mixing equipment, which is applied in the direction of mixers, mixers with rotating stirring devices, cosmetics, etc., can solve the problems of short shelf life of carved glue and easy oxidation of carved glue, and achieve pure color, long shelf life, and improved The effect of production efficiency

Pending Publication Date: 2020-06-12
浙江风尚化妆品有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Manicure is gradually loved and sought after by people. The current conventional manicure is usually to smear multiple layers of nail polish on the manicured nails or to paste nails on the nails; Then carve or paste decorations on the nail polish; during the production process of the existing carved glue, due to the limitation of the production process, the carved glue is easily oxidized, resulting in a short shelf life of the carved glue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carving glue and synthesis process thereof
  • Carving glue and synthesis process thereof
  • Carving glue and synthesis process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of engraved glue and its synthesis process, the engraved glue comprises by mass percentage:

[0034]

[0035]

[0036] The production technology of above-mentioned engraving glue, comprises the following steps:

[0037] S1. Weigh aliphatic urethane acrylic oligomer, epoxy acrylate oligomer, ethoxy ethoxy ethyl acrylate, fumed silica defoamer, 1-hydroxy-cyclohexyl-benzyl Ketones, pigments;

[0038] S2. Put the aliphatic urethane acrylic oligomer and epoxy acrylate oligomer into the stirring equipment, continuously feed nitrogen protective gas, and then the stirring part of the disperser rotates forwardly at a rate of 200r / min and stirs for 20min;

[0039] S3. Put ethoxyethoxyethyl acrylate into the stirring equipment, adjust the stirring parts to rotate in the forward direction, and the rotating speed is 100r / min, and stir for 8min;

[0040] S4. Put fumed silica and 1-hydroxyl-cyclohexyl-benzophenone into the stirring device, reverse rotation and stir for ...

Embodiment 2

[0045] A kind of engraved glue and its synthesis process, the engraved glue comprises by mass percentage:

[0046]

[0047] The production technology of above-mentioned carved glue, comprises the following steps:

[0048] S1. Weigh aliphatic urethane acrylic oligomer, epoxy acrylate oligomer, ethoxy ethoxy ethyl acrylate, fumed silica defoamer, 1-hydroxy-cyclohexyl-benzyl Ketones, pigments;

[0049] S2. Put the aliphatic urethane acrylic oligomer and epoxy acrylate oligomer into the stirring equipment, continuously feed nitrogen protective gas, and then the stirring part of the disperser rotates forward at a rate of 250r / min and stirs for 25min;

[0050] S3. Put ethoxyethoxyethyl acrylate into the stirring equipment, adjust the stirring parts to rotate in the forward direction, and the rotating speed is 125r / min, and stir for 9min;

[0051] S4. Put fumed silica and 1-hydroxyl-cyclohexyl-benzophenone into the stirring device, reverse rotation and stir for 18 minutes;

[0...

Embodiment 3

[0056] A kind of engraved glue and its synthesis process, the engraved glue comprises by mass percentage:

[0057]

[0058] The production technology of above-mentioned engraving glue, comprises the following steps:

[0059] S1. Weigh aliphatic urethane acrylic oligomer, epoxy acrylate oligomer, ethoxy ethoxy ethyl acrylate, fumed silica defoamer, 1-hydroxy-cyclohexyl-benzyl Ketones, pigments;

[0060] S2. Put the aliphatic urethane acrylic oligomer and epoxy acrylate oligomer into the stirring equipment, continuously feed nitrogen protective gas, and then the stirring part of the disperser rotates forward at a rate of 300r / min and stirs for 30min;

[0061] S3. Put ethoxyethoxyethyl acrylate into the stirring equipment, adjust the stirring parts to rotate in the forward direction, and the rotating speed is 150r / min, and stir for 10min;

[0062] S4. Put fumed silica and 1-hydroxyl-cyclohexyl-benzophenone into the stirring device, reverse rotation and stir for 20 minutes; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses carving glue and a synthesis process thereof. The carving glue comprises the following components (by mass) as shown in the specification. The production process of the above carving glue comprises the following steps: S1, weighing the aliphatic polyurethane acrylate oligomer, the epoxy acrylate oligomer, the ethoxyethoxy ethyl acrylate, the fumed silica defoamer, the 1-hydroxy-cyclohexyl-benzophenone and the pigment in proportion; S2, putting the aliphatic polyurethane acrylate oligomer and the epoxy acrylate oligomer into stirring equipment, continuously introducing nitrogen shielding gas, and then stirring for 20-30min by a stirring part of a dispersion machine at a speed of 200-300 r / min; and S3, pouring the ethoxyethoxy ethyl acrylate into the stirring equipment, adjusting the rotating speed of the stirring part to be 100-150 r / min, and stirring for 6-10 min.

Description

technical field [0001] The invention belongs to the technical field of cosmetics production, and in particular relates to carved glue and a synthesis process thereof. Background technique [0002] Manicure is gradually loved and sought after by people. The current conventional manicure is usually to smear multiple layers of nail polish on the manicured nails or to paste nails on the nails; Then carve patterns on the nail polish or affix decorations; in the production process of the existing carved glue, due to the limitation of the production process, the carved glue is easily oxidized, resulting in a short shelf life of the carved glue. Contents of the invention [0003] In order to overcome the deficiencies of the prior art, the invention provides carved glue with a long shelf life and a synthesis process thereof. [0004] In order to achieve the above object, the present invention adopts the following technical solutions: a kind of carved glue and its synthesis process...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)