Medical organosilicon rubber composition

A technology of silicone rubber and composition, applied in the field of silicone rubber, can solve problems such as poor mechanical properties, bacterial reproduction of silicone rubber, and difficulty in materials having mechanical properties

Inactive Publication Date: 2020-06-16
孟令芝
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a material for medical catheters, in addition to silicone rubber, soft polyvinyl chloride is generally used. Compared with polyvinyl chloride materials, silicone rubber has excellent biological adaptability and flexibility, but its mechanical properties, especially tensile strength and tear Insufficient cracking strength
In addition, as a medical material, there may be a large number of bacteria on the surface of silicone rubber, which may even cause infection
[0003] CN104448443A discloses a corrosion-resistant medical rubber and its preparation method, which uses styrene-butadiene rubber, fluorosilicone rubber, and EPDM rubber, but the preparation method does not use a vulcanizing agent, and the obtained material is difficult to have good mechanical properties
[0004] CN10444828A discloses a kind of antibacterial drug-loaded microsphere silicone rubber composite material. The method adopts silicone rubber matrix and PLGA drug-loaded microspheres to mix evenly. The prepared composite material has good antibacterial properties, but its mechanical properties are relatively poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medical organosilicon rubber composition
  • Medical organosilicon rubber composition
  • Medical organosilicon rubber composition

Examples

Experimental program
Comparison scheme
Effect test

Synthetic example 1

[0099] 65 parts by weight of fumed silica (specific surface area 250m 2 / g, the product of Cabot Company of the United States) into the reaction kettle, add 650 parts by weight of deionized water and stir evenly, heat to 75°C with an oil bath, adjust the pH value of the solution to 3.5 with dilute sulfuric acid, add the mass of white carbon black 3-(trimethoxy-silyl)propyldimethyloctadecylammonium chloride with a content of 10%, the reaction time is 2.5 hours, suction filtration, and drying to obtain medical antibacterial filler.

Synthetic example 2

[0101] 70 parts by weight of fumed silica (specific surface area 250m 2 / g, the product of Cabot Company of the United States) into the reaction kettle, add 700 parts by weight of deionized water and stir evenly, heat to 80°C with an oil bath, adjust the pH value of the solution to 3.5 with dilute sulfuric acid, add the mass of white carbon black 3-(triethoxy-silyl)propyl dimethyl octadecyl ammonium chloride with a content of 12%, the reaction time is 3 hours, suction filtration, and drying to obtain medical antibacterial filler.

Synthetic example 3

[0103] 70 parts by weight of fumed silica (specific surface area 250m 2 / g, the product of Cabot Company of the United States) into the reaction kettle, add 700 parts by weight of deionized water and stir evenly, heat to 80°C with an oil bath, adjust the pH value of the solution to 4 with dilute sulfuric acid, add the mass of white carbon black 3-(trimethoxy-silyl)propyldimethyloctadecylammonium chloride with a content of 10%, the reaction time is 3.5 hours, suction filtration, and drying to obtain medical antibacterial filler.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a medical organosilicon rubber composition, which is prepared from (i) organopolysiloxane containing two or more unsaturated groups, (ii) polyhydrosiloxane, (iii) a medical antibacterial filler, (iv) a platinum catalyst and (V) an inhibitor. The composition is prepared by uniformly mixing the materials and then heating and curing at 130-200 DEG C. According to the composition, the medical antibacterial filler is used as a reinforcing filler; the medical antibacterial filler can improve the mechanical property and antibacterial property of the medical organosilicon rubber composition at the same time, and the composition can be used for preparing medical hoses and catheters and has huge application prospects in other fields.

Description

technical field [0001] The invention relates to the field of silicone rubber, in particular to a medical silicone rubber composition and a preparation method thereof. Background technique [0002] Silicone rubber is physiologically inert and less reactive when in contact with biological tissues, so it is widely used in the medical industry, such as medical hoses, catheters, etc. As a material for medical catheters, in addition to silicone rubber, soft polyvinyl chloride is generally used. Compared with polyvinyl chloride materials, silicone rubber has excellent biological adaptability and flexibility, but its mechanical properties, especially tensile strength and tear Insufficient crack strength. In addition, as a medical material, there may be a large number of bacteria on the surface of silicone rubber, which may even cause infection. [0003] CN104448443A discloses a corrosion-resistant medical rubber and a preparation method thereof, which uses styrene-butadiene rubber...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/07C08L83/05C08K9/06C08K3/36C08K5/544
CPCC08K3/36C08K5/544C08K9/06C08L83/04C08L2203/18C08L2205/025
Inventor 孟令芝
Owner 孟令芝