A wear-resistant casting of metal matrix ceramic composite material and its processing technology

A technology of ceramic composite materials and ceramic materials, which is applied in the field of wear-resistant castings and its processing technology, can solve the problems of insufficient strength, poor dispersion effect of metal materials and ceramic materials, and affect the quality of castings, so as to improve the mixing effect and avoid metal cooling Residue, avoiding the effect of frequent maintenance

Active Publication Date: 2021-06-08
马鞍山海华耐磨材料科技有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Metal matrix ceramic composites are composite materials composed of metal materials with good toughness and ceramic materials with good hardness, but in the prior art, due to the poor dispersion effect of metal materials and ceramic materials, metal matrix ceramic composites The prepared castings have insufficient local strength, which affects the quality of the castings. In order to solve the above problems, the present invention provides the following technical solutions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A wear-resistant casting of metal matrix ceramic composite material and its processing technology
  • A wear-resistant casting of metal matrix ceramic composite material and its processing technology
  • A wear-resistant casting of metal matrix ceramic composite material and its processing technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0047] The technical solutions in the embodiments of the present invention will be clearly and completely described below. Obviously, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0048] A metal-matrix ceramic composite material wear-resistant casting prepared by processing the metal-matrix ceramic composite material;

[0049] The metal-based wear-resistant composite material is prepared by processing modified ceramic materials and metal-based materials, wherein the volume ratio of the modified ceramic materials is 20%-80%;

[0050] The metal-based material is steel, aluminum alloy, titanium alloy, zinc alloy, copper alloy or magnesium alloy, and the particle size of the metal-based material is 0.1-3mm;

[0051] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a wear-resistant casting of a metal-based ceramic composite material and a processing technology thereof. The wear-resistant casting is prepared by processing the metal-based ceramic composite material; during processing, ceramic particles are used as a basis for modification treatment and mix the ceramic particles and the metal-based material through the mixing injection molding device. After the modified ceramic material and the metal-based material enter the injection molding reaction cylinder, the mixed material is stirred by the stirring blade at the bottom of the stirring rod, and the power motor Drive the stirring rod to rotate clockwise. When the stirring rod rotates clockwise, the mixed material in the injection molding reaction cylinder is first stirred by the stirring blade at the bottom, and the screw blade at the bottom will convey the mixed material from bottom to top, and the The upper spiral blade returns the mixed material moved to the upper part to the lower part, so that the material is fully mixed in the injection molding reaction cylinder. Compared with the traditional stirring method, the material can be mixed more uniformly.

Description

technical field [0001] The invention belongs to the technical field of new materials, and in particular relates to a wear-resistant casting of a metal matrix ceramic composite material and a processing technology thereof. Background technique [0002] With the continuous development of modern industry, traditional iron and steel materials have been difficult to meet the needs of materials in the field of wear resistance. In the existing technology, metal matrix ceramic composite materials have both the hardness and wear resistance of ceramics and the toughness of metals to solve the problem. It solves the contradiction between high hardness and high toughness in traditional steel materials, and is widely used in many technical fields; [0003] Metal matrix ceramic composites are composite materials composed of metal materials with good toughness and ceramic materials with good hardness, but in the prior art, due to the poor dispersion effect of metal materials and ceramic ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C29/00C22C1/10C22C1/02C22C9/00C22C18/00C22C21/00C22C23/00C22C32/00C22C33/04C22C38/00B22C9/00
CPCB22C9/00C22C1/1036C22C9/00C22C18/00C22C21/00C22C23/00C22C29/005C22C32/00C22C33/04C22C38/00
Inventor 李家宝张桂兵夏平海李剑
Owner 马鞍山海华耐磨材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products