Preparation method of polyester-polyamide knitted elastic fibers

An elastic fiber, polyester-nylon technology, applied in the field of polyester-nylon knitted elastic fiber preparation, can solve the problems of easy wrinkling of nylon fabrics, low water absorption and moisture regain of polyester fabrics, etc. Effect

Inactive Publication Date: 2021-01-15
苏州昌如泰纺织股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The strength of polyester fiber is nearly 1 times higher than that of cotton and 3 times higher than that of wool, so the polyester fabric is strong and durable; but the water absorption and moisture regain of polyester fabric is low
Nylon has good strength and wear resistance, ranking first among all fibers, but nylon fabric has excellent elasticity and elastic recovery, and its nylon fabric is easy to wrinkle during wearing; with the improvement of people's living standards, people The requirements for wearing comfort are greatly improved, but the existing polyester fabrics and nylon fabrics cannot meet people's needs for clothing; for this reason, the application proposes a preparation method for polyester nylon knitted elastic fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of preparation method of polyester nylon knitted elastic fiber proposed by the present invention comprises the following specific steps:

[0031] S1, take by weight antibacterial agent, surfactant, microporous additive, maleic anhydride graft compatibilizer, lubricant and fire retardant, obtain mixture A; Mixture A is divided into mixture A1 by weight and mixture A2;

[0032] S2. Weighing the polyester slices by weight, then adding the polyester slices into the mixture A1 and heating to obtain the polyester mixed melt B1;

[0033] Weighing the cotton fiber slices by weight, then adding the cotton fiber chips into the mixture A2 and heating to obtain the cotton fiber mixed melt C1;

[0034] S3, spinning the prepared polyester mixed molten liquid B1, and obtaining polyester elastic fiber B2 after cooling;

[0035] Spinning the prepared cotton blended molten liquid C1, and obtain cotton elastic fiber C2 after cooling;

[0036] S4, twisting the polyester elastic f...

Embodiment 2

[0051] A kind of preparation method of polyester nylon knitted elastic fiber proposed by the present invention comprises the following specific steps:

[0052] S1, take by weight antibacterial agent, surfactant, microporous additive, maleic anhydride graft compatibilizer, lubricant and fire retardant, obtain mixture A; Mixture A is divided into mixture A1 by weight and mixture A2;

[0053] S2. Weighing the polyester slices by weight, then adding the polyester slices into the mixture A1 and heating to obtain the polyester mixed melt B1;

[0054] Weighing the cotton fiber slices by weight, then adding the cotton fiber chips into the mixture A2 and heating to obtain the cotton fiber mixed melt C1;

[0055]S3, spinning the prepared polyester mixed molten liquid B1, and obtaining polyester elastic fiber B2 after cooling;

[0056] Spinning the prepared cotton blended molten liquid C1, and obtain cotton elastic fiber C2 after cooling;

[0057] S4, twisting the polyester elastic fi...

Embodiment 3

[0072] A kind of preparation method of polyester nylon knitted elastic fiber proposed by the present invention comprises the following specific steps:

[0073] S1, take by weight antibacterial agent, surfactant, microporous additive, maleic anhydride graft compatibilizer, lubricant and fire retardant, obtain mixture A; Mixture A is divided into mixture A1 by weight and mixture A2;

[0074] S2. Weighing the polyester slices by weight, then adding the polyester slices into the mixture A1 and heating to obtain the polyester mixed melt B1;

[0075] Weighing the cotton fiber slices by weight, then adding the cotton fiber chips into the mixture A2 and heating to obtain the cotton fiber mixed melt C1;

[0076] S3, spinning the prepared polyester mixed molten liquid B1, and obtaining polyester elastic fiber B2 after cooling;

[0077] Spinning the prepared cotton blended molten liquid C1, and obtain cotton elastic fiber C2 after cooling;

[0078] S4, twisting the polyester elastic f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A preparation method of polyester-polyamide knitted elastic fibers comprises the following specific steps of S1, weighing an antibacterial agent, a surfactant, a microporous additive, a maleic anhydride grafted compatilizer, a lubricant and a flame retardant in parts by weight to obtain a mixture A, and dividing the mixture A into a mixture A1 and a mixture A2 in parts by weight; S2, weighing polyester slices and polyamide slices in parts by weight, respectively adding the polyester slices and the polyamide slices into the mixture A1 and the mixture A2, and heating to obtain polyester mixed molten liquid B1 and polyamide mixed molten liquid C1; S3, spinning and cooling to obtain polyester elastic fibers B2 and polyamide elastic fibers C2; S4, twisting the polyester elastic fibers B2 and the polyamide elastic fibers C2 to obtain polyester-polyamide elastic fibers; and S5, pressurizing and preserving heat of the polyester-nylon elastic fibers, and sequentially conducting cooling, oiling,drying, stretching, oiling and winding into a drum to obtain a finished product of the polyester-nylon elastic fibers. The preparation process is simple, the process is controllable, and the polyester-polyamide elastic fibers with excellent performance can be prepared.

Description

technical field [0001] The invention relates to the technical field of composite fibers, in particular to a preparation method of polyester-nylon knitted elastic fibers. Background technique [0002] The strength of polyester fiber is nearly 1 times higher than that of cotton and 3 times higher than that of wool, so polyester fabric is strong and durable; however, polyester fabric has low water absorption and moisture regain. Nylon has good strength and wear resistance, ranking first among all fibers, but nylon fabric has excellent elasticity and elastic recovery, and its nylon fabric is easy to wrinkle during wearing; with the improvement of people's living standards, people The requirements for wearing comfort are greatly improved, but the existing polyester fabrics and nylon fabrics cannot meet people's needs for clothing; therefore, the application proposes a preparation method of polyester nylon knitted elastic fibers. Contents of the invention [0003] (1) Purpose o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/32D02G3/04D01D1/04D01D5/088D01F1/07D01F1/10D01F6/30D01F6/92
CPCD01D1/04D01D5/088D01F1/07D01F1/10D01F1/103D01F6/30D01F6/92D02G3/045D02G3/328D10B2331/02D10B2331/04
Inventor 石国卿
Owner 苏州昌如泰纺织股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com