A kind of ceramic matrix composite material and its preparation method and application

A composite material and ceramic-based technology, applied in the field of low residual Si composite material and its preparation, can solve the problems of poor connection interface, unfavorable friction performance stability, low connection strength, etc., to improve ablation resistance and oxidation resistance , good coordination and synergy, and the effect of overcoming material performance defects

Active Publication Date: 2021-07-27
牟航(岱山)碳陶有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The carbon fiber surface of the material prepared in this patent document has no matrix carbon, but uses SiC and ZrC to directly protect the carbon fiber, and the interfacial bonding performance between the carbon fiber and SiC and ZrC components is poor
Moreover, this method of reacting and preparing TiC crystals is similar to LSI-SiC. The connection interface with CVD-C is not good, the connection strength is low, resulting in large wear, and the TiC phase distribution generated by the reaction is concentrated, which is unfavorable to the stability of friction performance and residual porosity. Most of them are Cu metal single substance, which is used in aerospace structural parts, and there will be a problem of limited high temperature resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ceramic matrix composite material and its preparation method and application
  • A kind of ceramic matrix composite material and its preparation method and application
  • A kind of ceramic matrix composite material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A ceramic matrix composite material of the present invention, comprising the following components in mass fraction:

[0039] Carbon Fiber: 22.7%,

[0040] CVD-C: 28.8%,

[0041] CVD-SiC: 13.0%,

[0042] PIP-SiC: 17.8%,

[0043] GSI-SiC: 7.9%,

[0044] TiC: 7.4%, and

[0045] Residual Si: 2.4%.

[0046] A preparation method of the ceramic matrix composite material of this embodiment, comprising the following steps:

[0047] (1) Deposit C layer: use carbon fiber to make a single layer of 0° non-weft cloth, 90° non-weft cloth and tire net, in order of 0° no weft cloth-tire net-90° no weft cloth-tire net Circular superimposition for laying, and then stitching by needle punching, introducing carbon fiber bundles perpendicular to the laying direction to obtain a three-dimensional needle punched carbon fiber preform with a density of 0.53g / cm 3 . The three-dimensional needle-punched carbon fiber preform was deposited and densified by chemical vapor deposition. The carb...

Embodiment 2

[0059] A kind of ceramic matrix composite material of the present invention, the mass percent of material constituent is as follows:

[0060] Carbon Fiber: 22.5%,

[0061] CVD-C: 27.4%,

[0062] CVD-SiC: 19.1%,

[0063] PIP-SiC: 10.4%,

[0064] GSI-SiC: 8.9%,

[0065] TiC: 9.2%, and

[0066] Residual Si: 2.5%.

[0067] A preparation method of the ceramic matrix composite material of this embodiment, comprising the following steps:

[0068] (1) Deposit C layer: use carbon fiber to make a single layer of 0° non-weft cloth, 90° non-weft cloth and tire net, in order of 0° no weft cloth-tire net-90° no weft cloth-tire net Circularly superimposed for laying, and then stitched by needle punching, introducing carbon fiber bundles perpendicular to the laying direction to obtain a three-dimensional needle-punched carbon fiber prefabricated body of 0.53g / cm 3 . The three-dimensional needle-punched carbon fiber preform was deposited and densified by chemical vapor deposition. The ...

Embodiment 3

[0078] A kind of carbon ceramic material of the present invention, the mass percent of material constituent is as follows:

[0079] Carbon Fiber: 22.5%,

[0080] CVD-C: 24.0%,

[0081] CVD-SiC: 10.1%,

[0082] PIP-SiC: 24.8%,

[0083] GSI-SiC: 7.8%,

[0084] TiC: 8.3%, and

[0085] Residual Si: 2.5%.

[0086] A preparation method of the ceramic matrix composite material of this embodiment, comprising the following steps:

[0087] (1) Deposit C layer: use carbon fiber to make a single layer of 0° non-weft cloth, 90° non-weft cloth and tire net, in order of 0° no weft cloth-tire net-90° no weft cloth-tire net Circularly superimposed for laying, and then stitched by needle punching, introducing carbon fiber bundles perpendicular to the laying direction to obtain a three-dimensional needle-punched carbon fiber prefabricated body of 0.53g / cm 3 . The three-dimensional needle-punched carbon fiber preform was deposited and densified by chemical vapor deposition. The carbon sou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
bending strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic matrix composite material and its preparation method and application. The ceramic matrix composite material includes the following components in mass fraction: carbon fiber is 20% to 30%, CVD‑C is 20% to 40%, CVD‑SiC 10%-25% for PIP-SiC, 5%-25% for GSI-SiC, 5%-15% for GSI-SiC, 5%-15% for TiC and less than 3% residual Si. The preparation method sequentially includes depositing a C layer on a carbon fiber preform, depositing a SiC layer, preparing SiC by impregnating and cracking a precursor, impregnating pitch-carbonization, preparing TiC and vapor phase siliconizing. The ceramic matrix composite material of the present invention has the advantages of excellent friction and wear properties, mechanical properties and thermal properties, and the content of each component can be flexibly designed and adjusted according to actual needs, which meets the requirements for material properties in the fields of high-performance braking and aerospace structural parts requirements.

Description

technical field [0001] The invention belongs to the field of composite material preparation, and relates to a ceramic-based composite material and its preparation method and application, in particular to a low-residual Si composite material containing multiple ceramic substrates and its preparation method and application. Background technique [0002] With the rapid development of economy and technology, a lot of preparation technology and application research of C / C-SiC composite materials have been carried out at home and abroad in recent years. C / C-SiC ceramic composite materials have the advantages of low density, thermal shock resistance, wear resistance, corrosion resistance, oxidation resistance, friction performance insensitivity to external environmental media (such as mold, oil, moisture, etc.) and long life. As the main heat-resistant material, C / C-SiC ceramic composite material combines the basic advantages of carbon fiber and silicon carbide, and is widely used ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/83C04B35/573C04B35/622C04B35/80
CPCC04B35/573C04B35/622C04B35/83C04B2235/3843C04B2235/428C04B2235/48C04B2235/483C04B2235/614C04B2235/616C04B2235/656C04B2235/6567C04B2235/77C04B2235/96C04B2235/9607C04B2235/9684
Inventor 龙宪海周峰匡湘铭汪莉何家琪王成华
Owner 牟航(岱山)碳陶有限公司