Skin-friendly antibacterial baby underwear fabric and preparation method thereof
A technology for baby underwear and fabrics, which is applied in the field of skin-friendly and antibacterial baby underwear fabrics and its preparation, can solve the problems of being difficult to be skin-friendly, breathable, antibacterial, and uniform in moisture permeability, and the functionality of baby underwear fabrics is not very ideal, and the like. Achieve the effect of reducing the difficulty of the process, good antistatic effect, good moisture absorption and air permeability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0026] A preparation method of a skin-friendly and antibacterial baby underwear fabric, said method comprising steps as follows:
[0027] (1) In parts by weight, 50 parts of chitosan fibers, 25 parts of ultra-fine denier bamboo fibers and 25 parts of cupro ammonia fibers are blended to form weft yarns, 50 parts of tencel fibers, 20 parts of ultra-fine denier bamboo fibers and 30 parts Soybean protein fiber blending forms warp; Wherein, the fineness of described chitosan fiber, cupro ammonia fiber and tencel fiber is 1.15dtex, the fineness of described superfine denier bamboo fiber is 0.15dtex, the fineness of described soybean protein fiber It is 1.52dtex.
[0028] (2) the warp yarn and the weft yarn are used as the fabric weave with plain weave, with warp density 460 / 10cm, the density weaving of weft density 320 / 10cm forms the woven fabric;
[0029] (3) In parts by weight, 8 parts of water-soluble chitosan with a degree of deacetylation of 75% and 5 parts of Sappanwood extra...
Embodiment 2
[0032] A preparation method of a skin-friendly and antibacterial baby underwear fabric, said method comprising steps as follows:
[0033] (1) by weight, 55 parts of chitosan fibers, 25 parts of ultrafine denier bamboo fibers and 20 parts of cupro ammonia fibers are blended to form weft yarns, 40 parts of tencel fibers, 30 parts of ultrafine denier bamboo fibers and 40 parts Soybean protein fiber blending forms warp yarn; Wherein, the fineness of described chitosan fiber, cupro ammonia fiber and tencel fiber is 1.10dtex, the fineness of described superfine denier bamboo fiber is 0.15dtex, the fineness of described soybean protein fiber is 1.48dtex.
[0034] (2) described warp yarn and weft yarn take plain weave as fabric structure, with warp density 480 / 10cm, the density weaving of weft density 320 / 10cm forms the woven fabric;
[0035] (3) In parts by weight, 10 parts of water-soluble chitosan with a degree of deacetylation of 80% and 8 parts of hematoxylin extract were dissol...
Embodiment 3
[0038] A preparation method of a skin-friendly and antibacterial baby underwear fabric, said method comprising steps as follows:
[0039] (1) By weight, 60 parts of chitosan fibers, 30 parts of ultrafine denier bamboo fibers and 30 parts of cupro ammonia fibers are blended to form weft yarns, 60 parts of tencel fibers, 20 parts of ultrafine denier bamboo fibers and 40 parts Soybean protein fiber blending forms warp yarn; Wherein, the fineness of described chitosan fiber, cupro ammonia fiber and tencel fiber is 1.25dtex, the fineness of described superfine denier bamboo fiber is 0.18dtex, the fineness of described soybean protein fiber is 1.50dtex.
[0040] (2) the warp yarn and the weft yarn are used as the fabric weave with plain weave, with warp density 560 / 10cm, the density weaving of weft density 380 / 10cm forms the woven fabric;
[0041] (3) In parts by weight, 15 parts of water-soluble chitosan with a degree of deacetylation of 75% and 8 parts of Sappanwood extract were ...
PUM
| Property | Measurement | Unit |
|---|---|---|
| Fineness | aaaaa | aaaaa |
| Fineness | aaaaa | aaaaa |
| Fineness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to View More