Processing method for penetration printing of polyester fabric

A technology for polyester fabrics and processing methods, which is applied in the fields of dyeing, textiles and papermaking, and dry-cleaning fiber products, and can solve the problems that polyester thin fabrics cannot achieve penetration printing, polyester thin fabrics are difficult to penetrate printing, and have insufficient hygroscopicity and permeability. And other problems, to achieve the effect of consistent color, high printing clarity, and improved hydrophilicity

Pending Publication Date: 2021-02-26
浙江灏宇科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the poor hydrophobicity of polyester and other thin chemical fiber fabrics, the hygroscopicity and permeability during printing are insufficient, resulting in the infiltration printing of polyester thin fabrics. Therefore, the penetration printing of polyester thin fabrics has always been a difficult problem in the industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A processing method for polyester fabric permeation printing, comprising the steps of:

[0015] a. The polyester fabric after desizing is carried out grafting pretreatment and water washing; the grafting process is: adopt the mixture of methacrylic acid and methyl methacrylate to carry out grafting reaction on polyester fabric, adopt alkyl glucoside, citric acid, superhydrogen Ammonium sulfate or potassium persulfate are used as assistants to assist grafting;

[0016] The mass ratio of methacrylic acid and methyl methacrylate is 2:3, and the total amount is 40% of the polyester fabric weight; the amount of alkyl glucoside is 5g / L, the amount of citric acid is 2g / L, and the amount of formic acid is 1g / L , the amount of ammonium persulfate is 5% of the total amount of methacrylic acid and methyl methacrylate, the above additives are mixed evenly, and the bath ratio is 1:15; the weight of polyester fabric is 90g / m 2 .

[0017] Add polyester fabric, then heat up to 80°C a...

Embodiment 2

[0021] A processing method for polyester fabric permeation printing, comprising the steps of:

[0022] a. The polyester fabric after desizing is carried out grafting pretreatment and water washing; the grafting process is: adopt the mixture of methacrylic acid and methyl methacrylate to carry out grafting reaction on polyester fabric, adopt alkyl glucoside, citric acid, superhydrogen Potassium sulfate assists grafting as auxiliary agent;

[0023] The mass ratio of methacrylic acid and methyl methacrylate is 3:2, and the total amount is 60% of the polyester fabric weight; the amount of alkyl glucoside is 10g / L, the amount of citric acid is 4g / L, and the amount of formic acid is 2g / L , the amount of potassium persulfate is 8% of the total amount of methacrylic acid and methyl methacrylate, the above additives are mixed evenly, the bath ratio is 1:20; the weight of polyester fabric is 140g / m 2 .

[0024] Add polyester fabric, then heat up to 85°C at a rate of 1°C / min and react ...

Embodiment 3

[0028] A processing method for polyester fabric permeation printing, comprising the steps of:

[0029] a. The polyester fabric after desizing is carried out grafting pretreatment and water washing; the grafting process is: adopt the mixture of methacrylic acid and methyl methacrylate to carry out grafting reaction on polyester fabric, adopt alkyl glucoside, citric acid, superhydrogen Ammonium sulfate is used as auxiliary agent to assist grafting;

[0030] The mass ratio of methacrylic acid and methyl methacrylate is 2.2:1, and the total amount is 45% of the polyester fabric weight; the amount of alkyl glucoside is 6g / L, the amount of citric acid is 3g / L, and the amount of formic acid is 2g / L , the amount of ammonium persulfate is 6% of the total amount of methacrylic acid and methyl methacrylate, the above additives are mixed evenly, and the bath ratio is 1:16; the weight of polyester fabric is 120g / m 2 .

[0031] Add polyester fabric, then heat up to 82°C at a rate of 1°C / m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a processing method for penetration printing of polyester fabric. The processing method comprises the following step: performing grafting pretreatment and water washing on thedesized polyester fabric. The grafting process comprises the following step: carrying out a grafting reaction on the polyester fabric by adopting a mixture of methacrylic acid and methyl methacrylate,wherein alkyl glycoside, citric acid, ammonium persulfate or potassium persulfate are used as auxiliary agents for assisting grafting. The polyester fabric is subjected to grafting pretreatment, so that the hydrophilicity of the fabric is improved, and preconditions are provided for penetration printing; and in addition, during printing, N-octyl pyrrolidone is adopted, so that polyester fibers can be plasticized, fiber pores are enlarged, and high-temperature migration of dye is facilitated. The invention can solve the technical problem that how to enable fabric printing to achieve consistentcolor of front and back sides and high definition.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a processing method for polyester fabric penetration printing. Background technique [0002] Printing refers to the use of dyes or paints to form patterns and characters on the surface of fabrics. The pattern and color of general fabric printing are mainly on the front side, and there are no special requirements on the back side. But as people's requirements for fashion, personality and aesthetic textiles increase, the demand for high-permeability printed fabrics increases, especially double-sided printed fabrics. At present, with the development of electronic technology, some manufacturers use high-precision digital printing twice to realize double-sided printing, but this printing method requires high equipment, long production cycle and high production risk. The traditional screen printing process realizes the high-penetration printing process on some thin natur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06P3/54D06P1/642D06P1/48D06P1/16D06M14/14D06L1/12
CPCD06P3/54D06P1/6426D06P1/48D06P1/16D06M14/14D06L1/12
Inventor 王灏洁章金芳陈万明张永高徐华君张忠王力史元庆
Owner 浙江灏宇科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com