Preparation method of ionic electroactive driver based on carboxylated bacterial cellulose

A bacterial cellulose and driver technology, applied in circuits, conductive materials, conductive materials, etc., can solve the problems that the research on ion-type driving materials has not yet been reported, and achieve good degradability, strong mechanical properties, and improve the effect of high price.

Inactive Publication Date: 2021-03-12
ZHEJIANG SCI-TECH UNIV
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Studies on carboxylated bacterial cellulose-based ionotropic driving materials have not been reported yet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of ionic electroactive driver based on carboxylated bacterial cellulose
  • Preparation method of ionic electroactive driver based on carboxylated bacterial cellulose
  • Preparation method of ionic electroactive driver based on carboxylated bacterial cellulose

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The preparation method of the ionic electroactive driver based on carboxylated bacterial cellulose comprises the following steps:

[0043] 1) Preparation of carboxylated bacterial cellulose dispersion:

[0044] Add 2g bacterial cellulose to 100ml deionized water and stir evenly;

[0045] Oxidation of bacterial cellulose: take the above suspension, add 0.016g of TEMPO (2,2,6,6-4 methylpiperidine-1-oxyl radical), 0.1g NaBr (sodium bromide) and 3.1 The g mass fraction is 12% NaClO (sodium hypochlorite) solution, and then add 0.5mol / L NaOH (sodium hydroxide) solution to keep the pH value at 10.5; / L HCl (hydrogen chloride) solution to adjust the pH value to 7; deionized water was used to centrifuge the resulting suspension several times to obtain a bacterial cellulose dispersion.

[0046] 2) Preparation of carboxylated bacterial cellulose-polypyrrole dispersion:

[0047] Take the above bacterial cellulose dispersion, add 1.0g FeCl and 1ml pyrrole while stirring, and keep...

Embodiment 2

[0053] The preparation method of the ionic electroactive driver based on carboxylated bacterial cellulose comprises the following steps:

[0054] 1) Preparation of carboxylated bacterial cellulose dispersion:

[0055] Add 1g bacterial cellulose to 100ml deionized water and stir evenly;

[0056] Oxidation of bacterial cellulose: take the above suspension, add 0.99g of NaBr solution, 0.014g of TEMPO solution and 3.0g of NaClO solution with a mass fraction of 12%, and then add 0.5mol / L of NaOH solution to make the pH The value was maintained at 10.4; when the pH value did not drop further, 0.5 mol / L HCl solution was added to adjust the pH value to 7; the resulting suspension was centrifuged several times with deionized water to obtain a bacterial cellulose dispersion.

[0057] 2) Preparation of carboxylated bacterial cellulose-polypyrrole dispersion:

[0058] Get above-mentioned bacterial cellulose dispersion, add 0.95g FeCl3 and 1ml pyrrole while stirring, under slow stirring,...

Embodiment 3

[0064] The preparation method of the ionic electroactive driver based on carboxylated bacterial cellulose comprises the following steps:

[0065] 1) Preparation of carboxylated bacterial cellulose dispersion:

[0066] Add 1g bacterial cellulose to 100ml deionized water and stir evenly;

[0067] Oxidation of bacterial cellulose: take the above suspension, add 0.11g of NaBr solution, 0.018g of TEMPO and 3.1g of NaClO solution with a mass fraction of 12%, and then add 0.5mol / L of NaOH solution to make the pH value Maintain at 10.6; when the pH value does not drop further, add 0.5 mol / L HCl solution to adjust the pH value to 7; centrifuge the resulting suspension several times with deionized water to obtain a bacterial cellulose dispersion.

[0068] 2) Preparation of carboxylated bacterial cellulose-polypyrrole dispersion:

[0069] Get above-mentioned bacterial cellulose dispersion, add 1.05g FeCl3 and 1ml pyrrole while stirring, under slow stirring, keep reaction 30min. It was...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of intelligent materials. The invention aims to provide a preparation method of an ionic electroactive driver based on carboxylated bacterial cellulose, and the driver is low in cost, excellent in performance and good in reliability. According to the technical scheme, the preparation method of the ionic electroactive driver based on carboxylated bacterial cellulose comprises the following steps: 1) preparing a bacterial cellulose dispersion liquid; 2) preparing a bacterial cellulose-polypyrrole dispersion liquid; 3) preparing a bacterial cellulose-polypyrrole-ionic liquid composite membrane; and 4) laying an electrode layer to prepare the bacterial cellulose-based ionic driver.

Description

technical field [0001] The invention belongs to the field of intelligent materials and relates to electroactive ion polymer materials, in particular to a method for preparing an ion electroactive driver based on carboxylated bacterial cellulose Background technique [0002] Electroactive polymers are a new type of intelligent polymer materials, which can change the internal structure under the action of an external electric field, and produce various forms of mechanical responses such as stretching, bending, tightening or expansion, and have extremely strong electrical and mechanical properties. Simultaneously realize multiple functions such as driving and sensing. According to the different actuation mechanism, it can be divided into electronic type and ionic type. Among them, ionic polymer metal composites (IPMC), a typical material in ionic electroactive polymers, are widely used. [0003] IPMC is generally a composite material obtained by depositing platinum, gold and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J7/044C08J5/18C08L1/04C08L79/04H01B1/12
CPCC08J7/044C08J7/0427C08J5/18H01B1/122H01B1/127C08J2301/04C08J2479/04C08J2379/04C08J2401/04C08J2465/00C08J2425/18
Inventor 王帆王姚枫
Owner ZHEJIANG SCI-TECH UNIV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com