PC/ABS composite material with high chemical resistance and preparation method thereof

A composite material and chemical-resistant technology, applied in the polymer field, can solve the problems of material heat resistance, impact strength reduction, thermal cracking loss, processability loss, etc. Effect

Active Publication Date: 2021-03-12
FINE BLEND POLYMER SHANGHAI CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, at present, there is no good solution to solve the solvent resistance problem of PC / ABS, adding chemical-resistant components, such as high crystallinity materials (PBT , PA, etc.) to improve the chemical resistance of the material, but too much addition of the third component will often lead to a decrease in the heat resistance and impact strength of the material; the end-capping method is used to improve the chemical resistance of PC , such as isocyanates, oxazolines, epoxies and dianhydrides
By reacting with the polymer end group by stepwise polymerization, the end group of PC is reduced, thereby improving its chemical resistance, but the problem it brings is the loss of processability. Due to the poor processability of high-viscosity PC, the apparent Poor, its residual internal stress will also become a weak point of chemical resistance, which often needs to increase the processing temperature, resulting in thermal cracking loss

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PC/ABS composite material with high chemical resistance and preparation method thereof
  • PC/ABS composite material with high chemical resistance and preparation method thereof
  • PC/ABS composite material with high chemical resistance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 11

[0045] In Example 11, ABS comes from Gaoqiao Petrochemical, including 15wt% butadiene, 25wt% acrylonitrile, and a weight-average molecular weight of 140,000; the rest of the raw materials are the same as in Table 1. The test methods in Table 3 are consistent with those in Table 2.

[0046] In summary, the PC / ABS composite material prepared by the present invention is easy to process, has excellent mechanical properties and high chemical resistance, and has excellent electrical and mechanical properties.

[0047] The existing technology chooses high AN content to improve chemical corrosion resistance and oil resistance, but it leads to the problem of poor compatibility due to the large difference in solubility parameters, and the serious decline in mechanical properties; the existing technology adds anti-chemical components, such as high crystallization However, too much addition of the third component will often lead to a decrease in the heat resistance and impact strength of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a PC / ABS composite material with high chemical resistance and a preparation method thereof. The composite material comprises the following components in percentage by weight: 60-85% of polycarbonate; 15-40% of ABS; 0.5-5% of a compatilizer; and 3-10% of a rheology modifier. The preparation method comprises the following steps: mixing the components in the raw materials according to a certain ratio at room temperature, and carrying out melt extrusion through double screws to prepare the PC / ABS composite material which is easy to process, excellent in mechanical propertiesand high in chemical resistance, and the preparation method of the PC / ABS composite material. The prepared composite material is excellent in mechanical property and easy to process, meanwhile, excellent chemical resistance is kept, and the product is excellent in appearance.

Description

technical field [0001] The invention belongs to the field of macromolecules, and in particular relates to a PC / ABS composite material with easy processing, excellent mechanical properties and high chemical resistance and a preparation method thereof. Background technique [0002] PC / ABS combines the comprehensive characteristics of both PC (polycarbonate) and ABS (polyacrylonitrile-butadiene-styrene), which improves fluidity and processing performance compared with PC, and reduces product stress Sensitivity, and has more excellent thermal stability than ABS. Therefore, it can be used in many fields such as household appliances, office equipment, communication equipment, photographic equipment, medical equipment, construction and lighting appliances, aerospace, electronic computers, and optical fibers. Especially in high-strength, high-heat-resistant parts such as automotive interiors, exteriors, and lights, it has been widely used. [0003] In recent years, the PC / ABS mark...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L55/02C08L25/14C08L25/12
CPCC08L69/00C08L2205/025C08L2205/02C08L2205/035C08L2205/08C08L55/02C08L25/14C08L25/12
Inventor 段浩朱从山司胜仁
Owner FINE BLEND POLYMER SHANGHAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products