Antistatic adhesive tape and preparation method thereof

An antistatic and tape technology, applied in adhesives, epoxy resin adhesives, conductive adhesives, etc., can solve problems such as affecting the service life of electronic devices, neglecting environmental protection problems of tapes, etc., achieving fast curing, good bonding performance, good adhesion The effect of thermal stability

Inactive Publication Date: 2021-04-23
湖南省和祥润新材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the rapid development of electronic science and technology, the application of adhesive tape in the field of electronic industry has also developed by leaps and bounds. However, due to the limitations of traditional adhesive tape processing methods, various adhesive tapes have a certain amount of static electricity to varying degrees, which makes the surface of the substrate adsorbed. Dust or other particles, thereby affecting the service life of related electronic devices
Simultaneously because adhesive tape is a kind of chemical synthesis material, the processing method of prior art is mainly devoted to the improvement to the function of adhesive tape, and the environmental protection problem of adhesive tape is often ignored by people.
[0003] But at present, the application of tapes in these industries has the following problems: due to the inherent physical and chemical properties of the tape itself, various tapes have a certain amount of static electricity to varying degrees, so that dust or other particles are adsorbed on the surface of the substrate, which affects the relevant Lifespan of Electronic Devices

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of antistatic adhesive tape, comprises substrate, is coated on the cured adhesive layer on the substrate and is coated on the release film on described cured adhesive layer; Described cured adhesive layer comprises according to the raw material of weight part: 10 parts of ethyl silicate paint, 80 parts of epoxy resin, 3 parts of silicone rubber, 60 parts of bonding resin, 3 parts of photoinitiator, 4 parts of curing crosslinking agent, 61 parts of antistatic adhesive, 10 parts of toughening agent part, 20 parts of polyester emulsion, 5 parts of platinum catalyst emulsion; described antistatic adhesive comprises according to the raw material of weight part: 30 parts of acrylic resin pressure-sensitive adhesive, 5 parts of silver-nickel-zinc powder, 3 parts of dispersant, antistatic agent 8 parts, 15 parts of organic solvents.

[0024] The preparation method of described antistatic adhesive tape, concrete steps are as follows:

[0025] (1) take the raw material of...

Embodiment 2

[0034] A kind of antistatic adhesive tape, comprises substrate, is coated on the cured adhesive layer on the substrate and is coated on the release film on described cured adhesive layer; Described cured adhesive layer comprises according to the raw material of weight part: 12 parts of ethyl silicate paint, 85 parts of epoxy resin, 3.5 parts of silicone rubber, 65 parts of bonding resin, 3.5 parts of photoinitiator, 4.5 parts of curing crosslinking agent, 65.5 parts of antistatic adhesive, 11 parts of toughening agent part, 22 parts of polyester emulsion, 6 parts of platinum catalyst emulsion; the raw material of described antistatic adhesive comprises according to weight part: 32 parts of acrylic resin pressure-sensitive adhesive, 5.5 parts of silver-nickel-zinc powder, 3.5 parts of dispersant, 8.5 parts of antistatic agent Parts, 16 parts of organic solvents.

[0035] The preparation method of described antistatic adhesive tape, concrete steps are as follows:

[0036] (1) t...

Embodiment 3

[0045] A kind of antistatic adhesive tape, comprises substrate, is coated on the cured adhesive layer on the substrate and is coated on the release film on described cured adhesive layer; Described cured adhesive layer comprises according to the raw material of weight part: 15 parts of ethyl silicate paint, 90 parts of epoxy resin, 4 parts of silicone rubber, 70 parts of bonding resin, 4 parts of photoinitiator, 5 parts of curing crosslinking agent, 72 parts of antistatic adhesive, 12 parts of toughening agent part, 25 parts of polyester emulsion, 8 parts of platinum catalyst emulsion; described antistatic adhesive comprises according to the raw material of weight part: 35 parts of acrylic resin pressure-sensitive adhesive, 6 parts of silver nickel zinc powder, 4 parts of dispersant, antistatic agent 9 parts Parts, 18 parts of organic solvents.

[0046] The preparation method of described antistatic adhesive tape, concrete steps are as follows:

[0047] (1) take the raw materia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an antistatic adhesive tape and a preparation method thereof. The antistatic adhesive tape comprises a base material, a curing bonding layer coated on the base material and a release film coated on the curing bonding layer; the curing bonding layer is prepared from the following raw materials by weight: an ethyl silicate coating, epoxy resin, organic silicon rubber, bonding resin, a photoinitiator, a curing cross-linking agent, an antistatic adhesive, a toughening agent, a polyester emulsion and a platinum catalyst emulsion; the antistatic adhesive comprises the following raw materials by weight: an acrylic resin pressure-sensitive adhesive, silver-nickel-zinc powder, a dispersing agent, an antistatic agent and an organic solvent. Through reasonable formula design, the prepared adhesive tape integrates excellent antistatic performance and conductive performance, has the advantage of good bonding performance, has good antistatic performance and thermal stability, can be kept unchanged for several years at room temperature or higher temperature, is not influenced by environmental humidity, the anti-static effect can be normally achieved at high temperature, curing is fast, and safety and reliability are achieved.

Description

technical field [0001] The invention relates to the technical field of adhesive tape production, in particular to an antistatic adhesive tape and a preparation method thereof. Background technique [0002] With the rapid development of electronic science and technology, the application of adhesive tape in the field of electronic industry has also developed by leaps and bounds. However, due to the limitations of traditional adhesive tape processing methods, various adhesive tapes have a certain amount of static electricity to varying degrees, which makes the surface of the substrate adsorbed. dust or other particles, thereby affecting the service life of related electronic devices. Simultaneously because adhesive tape is a kind of chemical synthesis material, the processing method of prior art is mainly devoted to the improvement to the function of adhesive tape, and the environmental protection problem of adhesive tape is often ignored by people. [0003] But at present, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/25C09J7/30C09J9/02C09J163/00C09J183/04C09J133/04C09J167/00C09J201/00C09J11/04
CPCC08K2003/0806C08K2003/0862C08K2003/0893C08K2201/001C08L2201/04C08L2205/035C09J9/02C09J11/04C09J163/00C09J2479/086C09J7/25C09J7/30C08L83/04C08L33/04C08L67/00C08L101/00C08K3/08
Inventor 廖平湘
Owner 湖南省和祥润新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap