A kind of mercapto-terminated polysiloxane water-based release agent
A water-based mercaptopolysiloxane and mercaptopolysiloxane technology, which is applied in coatings, anti-corrosion coatings, etc., can solve the problems of uniform coating of organic fluoropolymers and uniform coating of organic fluoropolymer emulsions. Wide application and other problems, to achieve the effect of low cost, good mold release effect and good dilution
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0031] 1) Epoxy-terminated dimethyl polysiloxane resin (molecular weight: 500,000-1,000,000 g / mol) and diethanolamine are fed in a molar ratio of 1:4, then excess chloroform is added, and the reaction is carried out at room temperature for 12 hours. Then precipitate in methanol and dry to obtain hydroxydimethylpolysiloxane resin.
[0032] 2) Hydroxydimethylpolysiloxane resin and 4-mercaptobutyric acid are fed in a molar ratio of 1:9, and 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide hydrochloride and 4-Dimethylaminopyridine was used as a catalyst (the molar ratio of the two was 10:1), and excess chloroform was used as a solvent, and the reaction was carried out at room temperature for 24 hours. Then wash with water, wash with 5% sodium bicarbonate aqueous solution, and dry. After removing chloroform with a rotary evaporator, dry in a vacuum oven at 30°C for 24 hours to obtain a mercapto-terminated dimethylpolysiloxane.
[0033] 3) Heat 20 parts of mercaptopolysiloxane obtaine...
Embodiment 2
[0041] 1) Epoxy-terminated dimethylpolysiloxane resin (molecular weight 20000-50000 g / mol) and diethanolamine are fed in a molar ratio of 1:2, then excess chloroform is added, and the reaction is carried out at room temperature for 24 hours. Then precipitate in methanol and dry to obtain hydroxydimethylpolysiloxane resin.
[0042] 2) Hydroxydimethylsiloxane resin and 3-mercaptopropionic acid are fed in a molar ratio of 1:2, and 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide hydrochloride and 4 -Dimethylaminopyridine was used as a catalyst (the molar ratio of the two was 10:1), and excess chloroform was used as a solvent, and the reaction was carried out at room temperature for 24 hours. Then wash with water, wash with 5% aqueous sodium bicarbonate solution, and dry. After removing chloroform with a rotary evaporator, dry in a vacuum oven at 30°C for 24 hours to obtain a mercapto-terminated dimethyl polysiloxane resin.
[0043] 3) Heat 30 parts of mercaptopolysiloxane obtained ...
Embodiment 3
[0051] 1) Epoxy-terminated diphenyldimethylsiloxane resin (molecular weight 2000-4000 g / mol) and diethanolamine are fed in a molar ratio of 1:3, then excess chloroform is added, and the reaction is carried out at room temperature for 2 hours . Then precipitate in methanol and dry to obtain hydroxydiphenyldimethylsiloxane resin.
[0052] 2) Hydroxydiphenyldimethylsiloxane resin and 6-mercaptocaproic acid are fed in a molar ratio of 1:4, and 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide hydrochloric acid is used to Salt and 4-dimethylaminopyridine were used as catalysts (the molar ratio of the two was 10:1), and excess chloroform was used as solvent, and the reaction was carried out at room temperature for 12 hours. Then wash with water, wash with 5% sodium bicarbonate aqueous solution, and dry. After removing chloroform with a rotary evaporator, dry in a vacuum oven at 30°C for 24 hours to obtain a mercapto-terminated diphenyldimethylsiloxane resin.
[0053] 3) Heat 25 parts ...