Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Method for red mud modification and its application in coke removal and desulfurization in organic solid waste pyrolysis gasification process

A technology of pyrolysis and gasification of organic solid waste, applied in chemical instruments and methods, solid waste removal, transportation and packaging, etc., can solve problems such as water and soil pollution, red mud metal waste, etc.

Active Publication Date: 2022-04-22
TSINGHUA UNIV
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the comprehensive utilization rate of red mud in my country is less than 5%, and it is still mainly stored in the form of damming. On the one hand, this has caused a waste of valuable metals in red mud; A large amount of stacking will cause serious water and soil pollution problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for red mud modification and its application in coke removal and desulfurization in organic solid waste pyrolysis gasification process
  • Method for red mud modification and its application in coke removal and desulfurization in organic solid waste pyrolysis gasification process
  • Method for red mud modification and its application in coke removal and desulfurization in organic solid waste pyrolysis gasification process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] 1) The method of modifying red mud includes: weighing 5g of dry red mud powder and placing it in a 100mL beaker, according to the molar content of sodium in the red mud, accurately weigh 1.024g of Add calcium oxide into the beaker, pour 60.2mL deionized water into the beaker according to the solid-to-liquid mass ratio of 1:10, place the beaker containing the mixture of red mud and calcium oxide on a magnetic stirrer, and stir at 100r / min , fully stirred for 30 minutes; then pour the uniformly mixed suspension into a hydrothermal reaction kettle, and put the sealed reaction kettle in an oven at 80°C for 24 hours; then pour the hydrothermally treated product into the rotary evaporator Vacuum drying is carried out in the evaporating flask, the drying temperature is 50°C, and the rotation speed is 100r / min; the dried modified red mud is ground and sieved into particles with a particle size of less than 63 μm, and the modified red mud obtained through this process is named HT...

Embodiment 2

[0056] 1) The method of modifying red mud includes: weighing 4g of dry red mud powder and placing it in a 100mL beaker, and accurately weighing 1.638g of red mud according to the molar content of sodium in the red mud with a sodium / calcium molar ratio of 1:4 Add calcium oxide into the beaker, pour 58.8mL deionized water into the beaker according to the solid-to-liquid mass ratio of 1:10, place the beaker containing the mixture of red mud and calcium oxide on a magnetic stirrer, and stir at 100r / min , fully stirred for 30 minutes; then pour the uniformly mixed suspension into a hydrothermal reaction kettle, and put the sealed reaction kettle in an oven at 80°C for 24 hours; then pour the hydrothermally treated product into the rotary evaporator Vacuum drying is carried out in the evaporating flask, the drying temperature is 50°C, and the rotation speed is 100r / min; the dried modified red mud is ground and sieved into particles with a particle size of less than 63 μm, and the mod...

Embodiment 3

[0059] 1) The method of modifying red mud includes: weighing 3.5g of dry red mud powder and placing it in a 100mL beaker. According to the molar content of sodium in the red mud, accurately weigh 2.151g according to the sodium / calcium molar ratio of 1:6 Add calcium oxide into the beaker, pour 56.4mL deionized water into the beaker according to the solid-to-liquid mass ratio of 1:10, place the beaker containing the mixture of red mud and calcium oxide on a magnetic stirrer, and stir at 100r / min speed, fully stirred for 30 minutes; then pour the uniformly mixed suspension into a hydrothermal reaction kettle, put the sealed reaction kettle in an oven at 80°C for 24 hours; then pour the hydrothermally treated product into a rotary evaporator Vacuum drying is carried out in a evaporating flask, the drying temperature is 50°C, and the rotation speed is 100r / min; the dried modified red mud is ground and sieved into particles with a particle size of less than 63 μm, and the modified re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a red mud modification and a method for removing coke and desulfurization in the pyrolysis gasification process of organic solid waste. The method of modifying red mud includes: mixing red mud, calcium oxide and / or calcium hydroxide, and water and performing hydrothermal reaction; drying the mixed solution after hydrothermal reaction to obtain modified red mud. This method improves the alkaline catalytic activity of the red mud by adding calcium oxide and / or calcium hydroxide to the red mud and strengthening the replacement of sodium through a hydrothermal method. At the same time, the introduction of calcium also improves the desulfurization performance of the red mud, making The modified red mud has the dual functions of catalytic decoking and desulfurization, and its application in the process of pyrolysis and gasification of organic solid waste can not only further increase the production of combustible gases, but also reduce the H produced in the reaction. 2 S and other sulfur-containing gas pollutants have also opened up a new way for the resource utilization of red mud, which is suitable for large-scale promotion.

Description

technical field [0001] The invention belongs to the technical field of organic solid waste pyrolysis, and specifically relates to red mud modification and a method for removing coke and desulfurization in the pyrolysis gasification process of organic solid waste. Background technique [0002] Red mud (red mud, RM) is a solid waste produced in the aluminum smelting industry. According to the red mud obtained without bauxite treatment process, it can be divided into Bayer red mud, sintering red mud, and mixed red mud. Among them, Bayer French red mud contains 10% to 60% Fe 2 o 3 , 5% to 20% Al 2 o 3 , 3% to 20% SiO 2 And some alkali metals, alkaline earth metals. At present, the comprehensive utilization rate of red mud in my country is less than 5%, and it is still mainly stored in the form of damming. On the one hand, this has caused a waste of valuable metals in red mud; A large number of piles will cause serious water and soil pollution problems. Therefore, it is of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B09B3/00B09B3/40B09B3/70
CPCB09B3/00B09B2101/02B09B3/40
Inventor 赵明崔晓敏吕熠
Owner TSINGHUA UNIV
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com