A kind of low detonation velocity mixed explosive for explosive welding and its preparation method and application

A technology of mixing explosives and explosive welding, which is applied in welding equipment, explosives processing equipment, explosives, etc., to achieve the effects of good safety performance, uniform mixing and easy production

Active Publication Date: 2022-02-08
HUNAN FORHOME COMPOSITE MATERIALS CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is still no low-detonation-velocity explosive suitable for explosive welding of ultra-low melting point metal materials, and the detonation velocity is 1300-1500m / s.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Dry 20kg of calcium carbonate powder with a particle size of 45-55 mesh and 10kg of silicon carbide powder with a particle size of 45-55 mesh, and place it in a resonance mixer with 60kg of antimony-free rock ammonium nitrate explosive, and stir for 20-25min until uniform; before welding After 10 minutes, spread the homogeneous mixture obtained above evenly on the explosive composite substrate, and evenly spray 10kg of pure water to make the drug body wet and loose without agglomeration, and obtain a low-detonation-velocity mixed explosive for explosive welding. After testing, when the charge thickness is 2cm, the packing density is 1.10g / cm 3 , successfully detonated, and the explosives exploded fully and evenly. The measured detonation velocity is 1405m / s.

Embodiment 2

[0036] Dry 20kg of calcium carbonate powder with a particle size of 45-55 mesh and 15kg of silicon carbide powder with a particle size of 45-55 mesh, and place it in a resonance mixer with 60kg of antimony-free rock ammonium nitrate explosive, and stir for 20-25min until uniform; before welding For 10 minutes, spread the homogeneous mixture obtained above evenly on the explosive composite substrate, and evenly spray 5kg of pure water to make the drug body moist and loose without agglomeration, and obtain a low-detonation velocity mixed explosive for explosive welding. After testing, when the charge thickness is 2cm, the packing density is 1.14g / cm 3 , successfully detonated, and the explosives exploded fully and evenly. The measured detonation velocity is 1365m / s.

Embodiment 3

[0038] Dry 15kg of calcium carbonate powder with a particle size of 45-55 mesh and 10kg of silicon carbide powder with a particle size of 45-55 mesh, and place it in a resonance mixer with 70kg of antimony-free rock ammonium nitrate explosive, and stir for 20-25min until uniform; before welding For 10 minutes, spread the homogeneous mixture obtained above evenly on the explosive composite substrate, and evenly spray 5kg of pure water to make the drug body moist and loose without agglomeration, and obtain a low-detonation velocity mixed explosive for explosive welding. After testing, when the charge thickness is 2cm, the packing density is 1.09g / cm 3 , successfully detonated, and the explosives exploded fully and evenly. The measured detonation velocity is 1500m / s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle sizeaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a low-detonation-velocity mixed explosive for explosive welding and its preparation method and application, which is specially used for explosive compounding of low-melting-point metals. The components (mass percentage) of the low-detonation-velocity mixed explosive include: 60-70% antimony-free rock Ammonium nitrate explosive (70-85% ammonium nitrate, 3-6% wood powder, 10-20% modified urea nitrate, 1.5-4% compound modifier), 15-20% calcium carbonate powder, 5-15 % silicon carbide powder and 5‑10% water. The low detonation velocity explosive is prepared by uniformly mixing the above components on site. The explosive of the present invention can significantly reduce the detonation velocity of common antimony-free rock ammonium nitrate explosives and the cost of explosive composite explosives; the present invention is easy to produce and stable in performance, and solves the problem of excessively high detonation velocity and easy destruction when conventional explosives are used to prepare explosive composite plates of low-melting-point metal materials Disadvantages of low melting point materials. Explosives with different detonation velocity requirements can be prepared on site according to different materials, the process is simple, and it is suitable for large-scale application.

Description

technical field [0001] The invention relates to an industrial explosive, in particular to a low-detonation-velocity mixed explosive for explosive welding between low-melting-point metal materials and a preparation method thereof. Background technique [0002] Explosive welding technology uses the energy of explosives, under the action of detonation waves, to collide one metal material (composite plate) obliquely with another metal material (substrate) at high speed to realize the metallurgical combination of the two metals. This technology is widely used in national defense, shipbuilding, petrochemical, metallurgy and other fields. As the energy source of explosive welding, the quality of explosives will directly affect the quality of explosive welding. [0003] The detonation velocity of commonly used explosive welding explosives is generally 1500m / s~3000m / s, and for the explosive compounding of ultra-low melting point materials (such as lead and tin), in order to avoid me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C06B31/28C06B21/00B23K20/08
CPCC06B31/28C06B21/00B23K20/08
Inventor 李慧中张文鼎梁霄鹏曾智恒
Owner HUNAN FORHOME COMPOSITE MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com