Preparation method of polymer/cement composite material structure electrolyte based on synchronous reaction
A technology of cement composite materials and polymers, which is used in the manufacture of hybrid capacitor electrolytes and hybrid/electric double-layer capacitors to solve the problem of interfacial compatibility, broaden application fields, and optimize electrochemical energy storage capacity.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0034] Example 1
[0035] (1) 4 g of Am (i.e., acrylamide) was dissolved in 80 g of deionized water, and stirring was thoroughly stirred at 500 rpm for 1 min at room temperature to obtain a uniform organic polymer monomer aqueous solution;
[0036] (2) 8 g of KOH was added to the aqueous solution of step (1), and stirring was thoroughly stirred at 500 rpm at room temperature to obtain a homogeneous organic polymer monomer electrolyte;
[0037] (3) The 200 g of cement powder and 15 drops of 15 wt% APs were added to the organic polymer monomeric electrolyte of step (2), and the mixture was thoroughly stirred at 200r / min to obtain a plurality of slurrys at 200 r / min;
[0038] (4) Pour the uniform slurry in step (3) into 2 * 2 * 2 cm silica gel molds in the mold, and then put in the cement maintenance chamber (temperature 22 ° C, relative humidity 90%) for 28 days, after demolding Get a cube structure electrolyte for mechanical properties test.
[0039] (5) After inserting the cut...
Example Embodiment
[0040] Example 2
[0041] (1) 10 g of AM was dissolved in 80 g of deionized water, and stirring was stirred at 500 rpm at room temperature to obtain a uniform organic polymer monomer aqueous solution;
[0042] (2) 8 g of KOH was added to the aqueous solution of step (1), and stirring was thoroughly stirred at 500 rpm at room temperature to obtain a homogeneous organic polymer monomer electrolyte;
[0043] (3) The 200 g of cement powder and 15 drops of 15 wt% APs were added to the organic polymer monomeric electrolyte of step (2), and the mixture was thoroughly stirred at 200r / min to obtain a plurality of slurrys at 200 r / min;
[0044](4) Pour the uniform slurry in step (3) into 2 * 2 * 2 cm silica gel molds in the mold, and then put in the cement maintenance chamber (temperature 22 ° C, relative humidity 90%) for 28 days, after demolding Get a cube structure electrolyte for mechanical properties test.
[0045] (5) After inserting the cut foam nickel sheet 1 * 1 * 1 cm silica g...
Example Embodiment
[0046] Example 3
[0047] (1) 20 g of AM was dissolved in 80 g of deionized water, and stirring was thoroughly stirred at room temperature for 1 min to obtain a uniform organic polymer monomer aqueous solution;
[0048] (2) 8 g of KOH was added to the aqueous solution of step (1), and stirring was thoroughly stirred at 500 rpm at room temperature to obtain a homogeneous organic polymer monomer electrolyte;
[0049] (3) 200 g of cement powder and 15 drop of 15 wt% APS aqueous solution was added to the electrolyte of step (2), and the mixture was thoroughly stirred at 200R / min to obtain a small slurry;
[0050] (4) Pour the uniform slurry in step (3) into 2 * 2 * 2 cm silica gel molds in the mold, and then put in the cement maintenance chamber (temperature 22 ° C, relative humidity 90%) for 28 days, after demolding Get a cube structure electrolyte for mechanical properties test.
[0051] (5) After inserting the cut foam nickel sheet 1 * 1 * 1 cm silica gel molds, after pouring the...
PUM
Property | Measurement | Unit |
---|---|---|
Ionic conductivity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap