A kind of composite osteochondral scaffold and its preparation method and application

A technology of osteochondral and cartilage layers, applied in the field of 3D printing materials, can solve problems such as differences in mechanical and biological properties, single biological scaffold, and single structure of materials

Active Publication Date: 2022-05-13
SHANGHAI UNIV +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the existing bioscaffolds printed by 3D are single material and single structure
However, cartilage and subchondral bone have different structures, and there are large differences in their mechanical and biological properties. Traditional scaffolds with a single material and a single structure are difficult to meet the repair requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite osteochondral scaffold and its preparation method and application
  • A kind of composite osteochondral scaffold and its preparation method and application
  • A kind of composite osteochondral scaffold and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The present invention also provides a method for preparing the composite osteochondral scaffold described in the above technical solution, comprising the following steps:

[0043] Using fused deposition modeling process to 3D print polyetheretherketone into subchondral bone layer;

[0044] Coating a biocompatible solution on the surface of the subchondral bone layer by a hydrothermal method to form a biocompatible layer;

[0045] Using an electrospinning process to 3D print a fibrous film-like transition layer on the surface of the biocompatible layer;

[0046] A cartilage layer with a network structure is 3D printed on the surface of the transition layer by an extrusion molding process, and the extruded raw material contains cartilage matrix and biological factors, and the cartilage matrix is ​​a hydrogel material.

[0047] The invention utilizes a fused deposition modeling process to 3D print polyetheretherketone into a subchondral bone layer. In the present inventi...

Embodiment 1

[0073] CT scans the point cloud data of the articular cartilage defect, converts the point cloud data obtained from the CT scan into a solid model through reverse design, and builds a three-dimensional model of the defect with reference to the complete cartilage tissue structure, and adds boundary conditions to the obtained model, and conducts limited Meta-analysis to obtain its stress-strain distribution; according to the stress-strain distribution, the path planning for 3D printing of the subchondral bone model is carried out;

[0074] Nozzle I (nozzle diameter: 0.4mm) is loaded with polyether ether ketone, and the nozzle I moves in the three directions of x, y, and z, and cooperates with the rotation of the B-axis and C-axis of the receiving platform to print according to the planned printing path (the temperature of the fusion deposition 395°C) subchondral bone layer to obtain a reticular subchondral bone layer with a pore size of 800 μm;

[0075] Dissolve 3.75g of disodium ...

Embodiment 2

[0079] The composite osteochondral scaffold was prepared according to the method of Example 1, except that the temperature of the hydrothermal reaction was 180°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
thicknessaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of 3D printing materials, and in particular relates to a composite osteochondral scaffold and its preparation method and application. The invention provides a composite osteochondral scaffold, which sequentially includes a subchondral bone layer, a fibrous membranous transition layer and a cartilage layer with a mesh structure from bottom to top; the material of the subchondral bone layer is polyether ether ketone, The surface of the subchondral bone layer is coated with a biocompatible layer; the material of the cartilage layer includes cartilage matrix and biological factors, and the cartilage matrix is ​​a hydrogel material; the cartilage layer contains biological factors. The biological factors contained in the cartilage layer are conducive to the growth of cartilage; the transition layer can realize the exchange of nutrients between the cartilage layer and the subchondral layer, and at the same time make the cartilage layer and the subchondral bone layer have a relatively independent development environment to avoid fibrosis. The composite osteochondral support provided by the invention can be well integrated with surrounding tissues, and can realize the integrated repair of cartilage and subchondral bone.

Description

technical field [0001] The invention belongs to the technical field of 3D printing materials, and in particular relates to a composite osteochondral scaffold and its preparation method and application. Background technique [0002] Articular cartilage lesions are a common clinical disease, most of which are caused by trauma, tumors, accidents, etc. Because cartilage tissue lacks blood vessels, nerves, and undifferentiated cells, its ability to repair itself is limited. From the perspective of anatomical structure, cartilage and subchondral bone are closely connected. Usually, most articular cartilage lesions will affect the subchondral bone, and cartilage and subchondral bone affect each other in terms of biological functions. Therefore, when performing tissue repair, it is necessary to Consider both at the same time. [0003] Currently commonly used solutions include microfracture, autologous cartilage transplantation, and allogeneic cartilage transplantation. Among them...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/18A61L27/50A61L27/52A61L27/54A61L27/36B33Y70/10B33Y80/00B33Y10/00A61F2/28
CPCA61L27/18A61L27/50A61L27/52A61L27/54A61L27/3654A61L27/3612B33Y70/10B33Y80/00B33Y10/00A61F2/28A61L2430/06A61L2400/12A61L2300/414C08L61/16
Inventor 胡庆夕王亚豪王国印张海光
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products