High-toughness and high-cohesiveness C60 strength fiber concrete and preparation method thereof

A fiber-reinforced concrete, high-adhesion technology, applied in the field of building materials, can solve the problem of inability to achieve toughening effect, and achieve the effects of improving friction and mechanical bite force, enhancing adhesion and increasing strength

Pending Publication Date: 2021-06-25
XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, due to the presence of cracks of different sizes in concrete, adding a single fiber often cannot achieve the best toughening effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness and high-cohesiveness C60 strength fiber concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0080] 1) Add 7 parts by mass of water reducer to two-thirds of the total water, which is recorded as mixed solution 1; add 6.5 parts of shrinkage reducer and 1.8 parts of defoamer to the total water of three One-third of the water is recorded as mixed solution 2, and the total amount of water is 165 parts;

[0081] 2) 4.7 parts of ramie fiber, 1015 parts of gravel, 719 parts of river sand, 350 parts of cement, 113 parts of fly ash, 45 parts of straw ash, 14 parts of silica fume, 2.5 parts of nano silicon, 8 parts of basalt fiber, 17.3 parts CaCO 3 Whiskers were divided into three parts according to the mass fraction, and then a part of ramie fiber, basalt fiber, CaCO 3 Sprinkle the whiskers evenly in the disc mixer, then place a portion of crushed stone, river sand, cement, fly ash, straw ash, silica fume, and nano-silicon in the disc mixer in order, and stir for 1 min;

[0082] 3) In the same way, add the other two ingredients into the pan mixer and stir evenly;

[0083] ...

Embodiment 2

[0089] 1) Add 7.5 parts by mass of water reducer to two-thirds of the total water, which is recorded as mixed solution 1; add 6.8 parts of shrinkage reducer and 2 parts of defoamer to the total water of three One-third of the water is recorded as mixed solution 2, and the total amount of water is 160 parts;

[0090] 2) Mix 4.7 parts of ramie fiber, 1015 parts of gravel, 719 parts of river sand, 350 parts of cement, 110 parts of fly ash, 50 parts of straw ash, 16 parts of silica fume, 1.5 parts of nano silicon, 8 parts of basalt fiber, 17.4 parts CaCO 3 Whiskers were divided into three parts according to the mass fraction, and then a part of ramie fiber, basalt fiber, CaCO 3 Sprinkle the whiskers evenly in the disc mixer, then place a portion of crushed stone, river sand, cement, fly ash, straw ash, silica fume, and nano-silicon in the disc mixer in order, and stir for 1 min;

[0091] 3) In the same way, add the other two ingredients into the pan mixer and stir evenly;

[00...

Embodiment 3

[0098] 1) Add 7 parts by mass of water reducer to two-thirds of the total water, which is recorded as mixed solution 1; add 6.6 parts of shrinkage reducer and 1.7 parts of defoamer to the total water of three One-third of the water is recorded as mixed solution 2, and the total amount of water is 165 parts;

[0099] 2) 4.5 parts of ramie fiber, 1015 parts of gravel, 719 parts of river sand, 350 parts of cement, 115 parts of fly ash, 40 parts of straw ash, 14 parts of silica fume, 1.5 parts of nano silicon, 7.8 parts of basalt fiber, 17.1 parts CaCO 3 Whiskers were divided into three parts according to the mass fraction, and then a part of ramie fiber, basalt fiber, CaCO 3Sprinkle the whiskers evenly in the disc mixer, then place a portion of crushed stone, river sand, cement, fly ash, straw ash, silica fume, and nano-silicon in the disc mixer in order, and stir for 1 min;

[0100] 3) In the same way, add the other two ingredients into the pan mixer and stir evenly;

[0101]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-toughness and high-cohesiveness C60 strength fiber concrete and a preparation method thereof. The concrete is prepared from cement, river sand, broken stone, fly ash, straw ash, silica fume, nano silicon, water, a water reducing agent, an exciting agent, a defoaming agent, a shrinkage reducing agent, ramie fibers, basalt fibers and CaCO3 whiskers according to the mixing ratio of (340-350): 719: 1015: (108-115): (40-50): (13-16): (1.5-3): (160-165): (6.5-7.5): (11.5-12.5): (1.6-2): (5.8-6.8): (4.5-4.7): (7.8-8): (17.1-17.4). Through a layered stirring method, all the materials are uniformly mixed at intervals, and discharging, forming and curing are performed. The compression resistance, the fracture resistance, the splitting tensile strength, the toughness, the durability and the like of the concrete can be effectively improved, and the bonding strength and the cooperative deformation capacity between the concrete and the profile steel are enhanced.

Description

technical field [0001] The invention belongs to the field of building materials, and is a kind of ramie fiber, basalt fiber, CaCO 3 Whiskers, straw ash, fly ash, silica fume, and nano-silicon concrete with high toughness, high cohesion, high durability, and high volume stability, specifically related to a high-toughness, high-cohesion C60 strength concrete Fiber concrete and its preparation method. Background technique [0002] In structural design, considering the requirements of use function, component stiffness and convenient construction, it is usually necessary to use different grades of concrete for different stress situations to meet the required compressive, flexural and splitting tensile strength of the component when it is loaded. And to ensure the bond strength of concrete and steel working together. Concrete materials with different grades have different modulus of elasticity and different deformation properties. Therefore, if the strength index is too large or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2201/50C04B2201/10C04B2111/00017C04B18/248C04B14/02C04B14/06C04B18/08C04B18/101C04B18/146C04B14/46C04B14/383C04B22/143C04B22/124C04B24/122C04B2103/302C04B2103/50C04B2103/0068
Inventor 郑山锁阮升郑跃周炎董立国姬金铭张晓宇杨路王斌李亚辉曹琛郑捷温桂峰张晓辉
Owner XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com