A ultra -high -strength corrosion resistance alloy and manufacturing method

A corrosion-resistant alloy and ultra-high-strength technology, applied in the field of alloy manufacturing, can solve problems such as short service life, insufficient strength index, and insufficient stress corrosion resistance

Active Publication Date: 2022-08-05
江苏汉青特种合金有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0028] In order to achieve the above purpose, the present invention strives to propose an ultra-high-strength corrosion-resistant alloy with significantly improved service life in the above-mentioned environment, fundamentally solving the problem of GH4169 and Inconel 625 due to resistance Insufficient stress corrosion resistance or short service life due to insufficient strength indicators

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A ultra -high -strength corrosion resistance alloy and manufacturing method
  • A ultra -high -strength corrosion resistance alloy and manufacturing method
  • A ultra -high -strength corrosion resistance alloy and manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0092] The development of the HQ9725 alloy in the present invention includes the optimal design of the chemical composition and the optimal design of the production process route.

[0093] 1. Chemical composition design of HQ9725 alloy

[0094] Compared with the traditional GH4169 and Inconel 625 alloys, the HQ9725 alloy produced by the invention has a more optimized composition, and the designed Ti / Al ratio ranges from 4.0 to 6.0, and the best is 5.0, which further improves the strength of the alloy; bold and innovative design, adding Zr, the control range is 0.01 -0.08%, the best 0.02%, add Y, the control range is 0.01-0.08%, the best 0.02%, see Table 2 for details.

[0095] Table 2 Compositional design comparison (percentage, %)

[0096]

[0097] In the following, the preferred solution of HQ9725 alloy is taken as an example to illustrate its specific manufacturing process, and based on this, the comprehensive performance is compared with the traditional GH4169 and Inco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of alloy manufacturing, and in particular relates to an ultra-high-strength corrosion-resistant alloy and a manufacturing method, in particular to a Cr-Ni-Mo-Nb corrosion-resistant alloy having both ultra-high strength and excellent stress corrosion properties and the Alloy production technology. The alloys of the present invention include the elements nickel, carbon, silicon, manganese, sulfur, chromium, molybdenum, iron, aluminum, titanium, niobium, zirconium, yttrium. The alloy prepared by the present invention is in high pressure H 2 S. High pressure CO 2 And in the chloride ion environment, it not only has very high strength, but also has excellent stress corrosion resistance, can be used to manufacture key components of oilfield drilling and production equipment, and has a long service life.

Description

technical field [0001] The invention belongs to the technical field of alloy manufacturing, and in particular relates to a Cr-Ni-Mo-Nb corrosion-resistant alloy with both ultra-high strength and excellent stress corrosion resistance and a production technology of the alloy. Background technique [0002] The application of steel in offshore oil engineering, marine ships, offshore engineering, seawater desalination, salt industry equipment, acid-resistant equipment, oil drilling and other scenarios are all faced with water-containing H 2 S, chloride ion, high pressure CO 2 , oxygen-enriched environment, processing residual stress, external stress and other environmental influences, there is a tendency or result of stress corrosion cracking. For this reason, some mature varieties have been developed at home and abroad, such as GH4169, Inconel 625 and so on. [0003] But there are still some problems, such as GH4169 due to the high pressure H 2 S. High pressure CO 2 , In the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C19/05C22C1/03C22B9/18C22F1/10
CPCC22C19/055C22C1/023C22C1/03C22B9/18C22F1/10
Inventor 陈刚
Owner 江苏汉青特种合金有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com