High-strength anti-freezing grouting material for building and preparation method thereof

A kind of grouting material and construction technology, which is applied in the field of high-strength frost-resistant building grouting materials, can solve the problems of not being able to effectively resist the force of water for a long time, the base masonry and the grouting material not being closely bonded, and affecting the use effect, etc. Achieve the effect of enhancing toughness, convenient construction, and avoiding corrosion of steel bars

Pending Publication Date: 2021-07-23
菏泽永民新型建筑材料股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] During the use of the grouting materials in the prior art, the flexural strength is low, the volume shrinkage is relatively large, and microcracks are prone to occur, resulting in the lack of close contact between the base masonry and the grouting material during use, and at the same time, it cannot be effective for a long time. Resisting the force of water will lead to leakage again in the later stage, and the anti-freezing effect is poor, thus affecting its use effect. Therefore, we propose a high-strength anti-freezing building grouting material and its preparation to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength anti-freezing grouting material for building and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0026] In order to more clearly understand the above objects, features and advantages of the present invention, the present invention will be further described below in conjunction with the accompanying drawings and embodiments. It should be noted that, in the case of no conflict, the embodiments of the present application and the features in the embodiments can be combined with each other.

[0027] In the following description, many specific details are set forth in order to fully understand the present invention. However, the present invention can also be implemented in other ways than described here. Therefore, the present invention is not limited to the specific embodiments disclosed below. limit.

[0028] Embodiments, as can be seen from the description and the accompanying drawings of the division of labor, this program provides a high-strength frost-resistant building grouting material, including the following ingredients in parts by weight, 40-50 parts of cement, 50-60...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength anti-freezing grouting material for buildings, which comprises the following components in parts by weight: cement, quartz sand, carbide slag, waterborne epoxy resin, calcium nitrate, calcium lignosulphonate, a defoaming agent, an expanding agent, a retarder, steel fibers, a reactive diluent and water. The prepared grouting material has the characteristics of high strength, high corrosion resistance and high durability, the Portland cement and the sulfate cement are used as main components of the material, the carbide slag and the epoxy resin are crushed through a crushing process and added into the grouting material, the grouting material has the characteristic of high strength, and the toughness of the grouting material is enhanced by adding the steel fibers; according to the high-strength anti-freezing grouting material for the building, the breaking strength, the impact resistance and the anti-freezing effect of the grouting material are improved, the original high permeability of the grouting material is reserved due to the addition of the reactive diluent, and the high-strength anti-freezing grouting material for the building has high strength and high fluidity and can adapt to different grouting thicknesses by adjusting the proportion and the doping amount of the powder.

Description

technical field [0001] The invention belongs to the technical field of grouting materials, and in particular relates to a high-strength frost-resistant building grouting material. Background technique [0002] Grouting material is a kind of material that can exist in liquid form after being mixed with water, and is convenient to use hydraulic pressure, air pressure or electrochemical principles to inject into the inner space of cracks, cracks, pores and other internal spaces of the corresponding medium, and has the ability to cement and solidify, so that the leakage channel of the medium can be blocked. Materials with improved physical properties and mechanical properties. At present, cement-based grouting materials are a kind of grouting materials that are widely used and widely used. [0003] During the use of the grouting materials in the prior art, the flexural strength is low, the volume shrinkage is relatively large, and microcracks are prone to occur, resulting in the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/70
CPCC04B28/04C04B2111/70C04B22/142C04B14/06C04B18/0481C04B24/281C04B24/42C04B14/48C04B24/18C04B22/085C04B24/023C04B24/06C04B2103/0068
Inventor 王换新叶秋合
Owner 菏泽永民新型建筑材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction