Nano-composite gel matrix multi-layer fabric stab-resistant composite material and preparation method thereof

A nano-composite, multi-layer fabric technology, used in textiles, papermaking, fiber processing, etc., can solve the problem of not being recycled, and achieve the effects of good stab resistance, excellent self-healing function, and excellent comfort.

Active Publication Date: 2021-07-23
TIANJIN POLYTECHNIC UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above methods have a common disadvantage that they cannot be recycled

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano-composite gel matrix multi-layer fabric stab-resistant composite material and preparation method thereof
  • Nano-composite gel matrix multi-layer fabric stab-resistant composite material and preparation method thereof
  • Nano-composite gel matrix multi-layer fabric stab-resistant composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment a～f

[0056] A method for preparing a nanocomposite hydrogel, comprising the steps of:

[0057] 1) Under a nitrogen atmosphere, in a flask, uniformly disperse polyether F127 in anhydrous dichloromethane, then inject triethylamine and acryloyl chloride into the flask with a syringe, stir at 25°C for 24 hours, filter to remove triethyl Precipitate triethylammonium chloride salt of amine and acryloyl chloride reaction, obtain filtrate, put into excessive methyl tert-butyl ether and precipitate five times (the step of putting into excessive ether every time is: put into excessive Methyl tert-butyl ether, filtered to obtain a precipitate.), to obtain a white precipitate, filtered again (400 mesh) to purify, room temperature 20 ~ 25 ° C vacuum drying for 24 hours to obtain polyether F127 diacrylate, wherein, according to In parts by mass, the ratio of polyether F127, anhydrous dichloromethane, triethylamine and acryloyl chloride is 10:136.8:0.35:0.39, and in parts by mass, the ratio of me...

Embodiment 1～7

[0061] A preparation method of a nanocomposite gel matrix multilayer fabric stab-resistant composite material, comprising the following steps:

[0062] 1) Under a nitrogen atmosphere, in a flask, uniformly disperse polyether F127 in anhydrous dichloromethane, then inject triethylamine and acryloyl chloride into the flask with a syringe, stir at 25°C for 24 hours, filter to remove triethyl Precipitate triethylammonium chloride salt of amine and acryloyl chloride reaction, obtain filtrate, put into excessive methyl tert-butyl ether and precipitate five times (the step of putting into excessive ether every time is: put into excessive Methyl tert-butyl ether, filtered to obtain a precipitate.) to obtain a white precipitate, filtered again to purify polyether F127 diacrylate (400 mesh), and vacuum dried at room temperature 20-25°C for 24 hours to obtain polyether F127 diacrylate Acrylate, wherein, by mass parts, the ratio of polyether F127, anhydrous dichloromethane, triethylamine ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nano-composite gel matrix multi-layer fabric stab-resistant composite material and a preparation method thereof. The preparation method comprises the following steps of dissolving polyether F127 diacrylate in a solvent, performing stirring for at least 12 hours, adding hydroxyapatite nanoparticles under the stirring condition, adjusting the temperature to 0-10 DEG C, adding a monomer, an initiator and an accelerant, introducing nitrogen for at least 15 minutes to carry out nitrogen bubbling to obtain nano-composite hydrogel, stacking a plurality of layers of aramid fabrics impregnated with the nano-composite hydrogel together, and performing standing in a vacuum environment for at least 24 hours to obtain the nano-composite gel matrix multi-layer fabric stab-resistant composite material. After the stab-resistant material formed by combining the nano-composite hydrogel and the fabrics is damaged, the damage of fibers cannot be recovered, and the hydrogel in the fabrics can be partially self-repaired, so that the self-healed nano-composite gel matrix multi-layer fabric stab-resistant composite material still has a certain stab-resistant effect.

Description

technical field [0001] The invention belongs to the technical field of textile materials, and in particular relates to a nanocomposite gel matrix multilayer fabric stab-proof composite material and a preparation method thereof. Background technique [0002] Stab-resistant materials are mainly divided into hard, semi-rigid and soft materials. Rigid composite materials increase the risk of injury due to poor flexibility and comfort. Because stab-resistant materials are more in line with current needs, scholars at home and abroad pay more and more attention to the research of stab-resistant materials. Currently, there are three approaches to improve the stab resistance of soft materials: one is to weave high-count, high-density high-performance yarns and then stack them by lamination or needling. The other is to compound the fabric with resin, and fill the gaps between the interweaving points of the fabric with resin to increase the friction between the yarns and improve its ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M17/00D06N3/04D06N3/00
CPCD06M17/00D06N3/042D06N3/0006D06N3/0034D06N2201/0272
Inventor 李婷婷韩笑邢梦帆高波林佳弘楼静文
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com