High-density fiberboard with antibacterial function and manufacturing process of high-density fiberboard

A high-density fiberboard, functional technology, applied in the field of fiberboard materials, can solve the problems of poor antibacterial effect and non-persistence of high-density fiberboard

Pending Publication Date: 2021-07-30
佳诺威集团股份有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problem that the antibacterial effect of high-density fiberboard in the prior art is not good, and it is not durable, and the high-density fiberboard with antibacterial function and its manufacturing process proposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-density fiberboard with antibacterial function and manufacturing process of high-density fiberboard

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A high-density fiberboard with antibacterial function proposed by the present invention includes the following raw materials in parts by weight: 30 parts of wood chips, 30 parts of straw, 15 parts of polyethylene-maleic anhydride copolymer, polyparaphenylene benzobisoxazole fiber 10 parts, 4 parts of solid paraffin, 3 parts of adhesive, 3 parts of antibacterial agent, 1 part of carboxymethyl cellulose, and 2 parts of methyltetrahydrophthalic anhydride.

[0027] Among them, the adhesive is a mixture of soybean protein, polyurethane and polyacrylic acid in a mass ratio of 1:5:2. The specific preparation process is as follows: after blending soybean protein, polyurethane and polyacrylic acid in a mass ratio of 1:5:2, , and at a temperature of 20°C, stir and mix for 10 minutes to obtain the adhesive.

[0028] The antibacterial agent is composed of the following raw materials in parts by weight: 15 parts of salicylic acid, 3 parts of N-acetylacetanilide, 0.1 part of 5-carbox...

Embodiment 2

[0035] A high-density fiberboard with antibacterial function proposed by the present invention comprises the following raw materials in parts by weight: 35 parts of sawdust, 35 parts of straw, 18 parts of polyethylene-maleic anhydride copolymer, polyparaphenylene benzobisoxazole fiber 12 parts, 6 parts of solid paraffin, 3.5 parts of adhesive, 4 parts of antibacterial agent, 1.5 parts of carboxymethyl cellulose, 3 parts of methyl tetrahydrophthalic anhydride.

[0036] Among them, the adhesive is a mixture of soybean protein, polyurethane and polyacrylic acid in a mass ratio of 1:5:2. The specific preparation process is as follows: after blending soybean protein, polyurethane and polyacrylic acid in a mass ratio of 1:5:2, , and at a temperature of 30°C, stir and mix for 12 minutes to obtain the adhesive.

[0037] The antibacterial agent consists of the following raw materials in parts by weight: 18 parts of salicylic acid, 4 parts of N-acetoacetanilide, 0.15 parts of 5-carboxyp...

Embodiment 3

[0044] A high-density fiberboard with antibacterial function proposed by the present invention includes the following raw materials in parts by weight: 40 parts of wood chips, 40 parts of straw, 20 parts of polyethylene-maleic anhydride copolymer, polyparaphenylene benzobisoxazole fiber 15 parts, 7 parts of solid paraffin, 4 parts of adhesive, 5 parts of antibacterial agent, 2 parts of carboxymethyl cellulose, 3.5 parts of methyl tetrahydrophthalic anhydride.

[0045] Among them, the adhesive is a mixture of soybean protein, polyurethane and polyacrylic acid in a mass ratio of 1:5:2. The specific preparation process is as follows: after blending soybean protein, polyurethane and polyacrylic acid in a mass ratio of 1:5:2, , and at a temperature of 35°C, stir and mix for 15 minutes to obtain the adhesive.

[0046] The antibacterial agent consists of the following raw materials in parts by weight: 20 parts of salicylic acid, 5 parts of N-acetylacetanilide, 0.2 part of 5-carboxype...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of fiberboard materials, particularly relates to a high-density fiberboard with an antibacterial function and a manufacturing process of the high-density fiberboard, and solves the problems that in the prior art, the antibacterial effect of a high-density fiberboard is poor and not lasting. The high-density fiberboard with an antibacterial function comprises the following raw materials in parts by weight: 30-50 parts of wood chips, 30-50 parts of straws, 15-25 parts of a polyethylene-maleic anhydride copolymer, 10-20 parts of poly (p-phenylene benzobisoxazole) fibers, 4-10 parts of solid paraffin, 3-5 parts of an adhesive, 3-7 parts of an antibacterial agent, 1-3 parts of carboxymethylcellulose and 2-5 parts of methyl tetrahydrophthalic anhydride. The high-density fiberboard with the antibacterial function is scientific in formula, rigorous in proportion, simple in preparation process and mild in preparation condition, and the obtained high-density fiberboard with the antibacterial function has excellent antibacterial performance and mechanical performance, almost does not release formaldehyde in the using process, is safe and environmentally-friendly and can be widely applied.

Description

technical field [0001] The invention relates to the technical field of fiberboard materials, in particular to a high-density fiberboard with antibacterial function and a manufacturing process thereof. Background technique [0002] In recent years, with the rapid development of the construction industry, wooden flooring has gradually become one of the important materials for interior decoration due to its natural environmental protection and superior texture. As an important product in wood flooring, laminate flooring is favored by the market because of its wear resistance, aesthetics and good stability. At present, the reinforced composite floor mainly uses medium and high-density fiberboard as the base material, and the high-density fiberboard is made of wood fiber or straw fiber and adhesive. Adhesives are mainly urea-formaldehyde resins, phenolic resins, etc., and auxiliary materials are generally insect repellents of chemically synthesized materials. The high-density b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27N1/02B27N3/04B27N3/12B27N3/18
CPCB27N1/0209B27N3/04B27N3/12B27N3/18B27N3/183
Inventor 孙志强牟辉邵亚沈信荣
Owner 佳诺威集团股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com