Addition type silk-screen silica gel and preparation method thereof
An addition-type, silica gel technology, applied in the direction of adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve problems such as large fiber gaps, difficult bonding, and poor adhesion on the surface of the substrate to increase bonding Strength, easy construction and operation, and the effect of increasing thixotropy
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0036] Component A: 123.5 parts of base rubber, 100 parts of second vinyl silicone oil, 137 parts of hydrogen-containing silicone oil, 21 parts of tackifier, 15 parts of acetylenic alcohol; Component B: 10 parts of castor catalyst, third vinyl silicone oil 100 parts of silicone oil.
[0037] Wherein, the mass ratio of component A and component B is 10:1.
[0038] Wherein, the viscosity of the tackifier is 2000 mPa·s, and the hydroxyl group content in the tackifier is 6%.
[0039] Among them, the tackifier includes γ-glycidyl etheroxypropyl trimethoxysilane (KH560), hydroxyl-terminated vinyl silicone oil and butyl titanate. The use of coupling agent as the adhesion promoter of the silica gel system can increase the bonding strength of the silica gel system, making the silica gel have good adhesion to nylon, polyester and other fabrics with smooth surfaces.
[0040] Further, in the tackifier, calculated in parts by weight, the content of the above-mentioned components is: 10 p...
Embodiment 2
[0058]Component A: 108.5 parts of base rubber, 90 parts of the second vinyl silicone oil, 130 parts of hydrogen-containing silicone oil, 20 parts of tackifier, 10 parts of acetylenic alcohol; Component B: 5 parts of castor catalyst, the third vinyl 90 parts of silicone oil.
[0059] Wherein, the mass ratio of component A and component B is 50:1.
[0060] Wherein, the viscosity of the tackifier is 2500 mPa·s, and the hydroxyl content of the tackifier is 8%.
[0061] Wherein, in the tackifier, calculated in parts by weight, the content of the above components is: 8 parts of γ-glycidyloxypropyltrimethoxysilane, 8 parts of vinyl silicone oil terminated by hydroxyl groups, and 4 parts of butyl titanate.
[0062] Wherein, in the base rubber material, calculated according to parts by weight, the content of the above components is: 90 parts of the first vinyl silicone oil, 10 parts of reinforcing filler, 0.5 parts of hexamethyldisilazane, and 8 parts of water.
[0063] Wherein, the ...
Embodiment 3
[0068] Component A: 140 parts of base rubber, 110 parts of second vinyl silicone oil, 140 parts of hydrogen-containing silicone oil, 25 parts of tackifier, 20 parts of acetylenic alcohol; Component B: 15 parts of castor catalyst, third vinyl silicone oil 110 parts of silicone oil.
[0069] Wherein, the mass ratio of component A and component B is 100:1.
[0070] Wherein, the viscosity of the tackifier is 3000 mPa·s, and the hydroxyl content of the tackifier is 10%.
[0071] Wherein, in the tackifier, calculated in parts by weight, the content of the above-mentioned components is: 10 parts of γ-glycidyloxypropyltrimethoxysilane, 10 parts of hydroxyl-terminated vinyl silicone oil, and 5 parts of butyl titanate.
[0072] Wherein, in the base rubber material, calculated according to parts by weight, the content of the above components is: 110 parts of the first vinyl silicone oil, 15 parts of reinforcing filler, 3 parts of hexamethyldisilazane, and 12 parts of water.
[0073] Wh...
PUM
Property | Measurement | Unit |
---|---|---|
Viscosity | aaaaa | aaaaa |
Viscosity | aaaaa | aaaaa |
Specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com