Preparation method of adhesive film veneer artificial board

A technology for wood-based panels and plastic films, which is applied in the field of preparation of plastic-film veneer wood-based panels, can solve the problems affecting the normal use of plastic-film veneer wood-based panels, the low bonding force between decorative films and plywood, and the separation of decorative films from plywood. The effect of improving the bonding force, improving the bonding force and improving the utilization rate of the adhesive

Active Publication Date: 2021-10-08
浙江世瑞骐碳科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the interface effect between the adhesive and the board, the binding force between the decorative film and the plywood is low, and the decorative board is prone t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of preparation method of film veneer wood-based panel, comprises the following steps:

[0030] (A): Wetting the decorative film with a sodium carbonate solution with a mass fraction of 5%, after wetting for 10 minutes, cleaning and drying to obtain a pretreatment film;

[0031] (B): The adhesive polyurethane was scraped onto the surface of the pretreatment film with a thickness of 10 μm, and heated at 40°C for 3 minutes to obtain an adhesive film;

[0032] (C): The surface of the plywood is sprayed with a silane coupling agent solution with a mass fraction of 0.5%. The silane coupling agent solution is prepared by dissolving methoxysilane in methanol. After the surface of the plywood is dried, a pretreated plywood is obtained;

[0033] (D) The adhesive film was preheated at 60°C for 200s and then pasted to the surface of the pretreated plywood to obtain an adhesive film-faced wood-based panel.

[0034] Adhesive effective utilization rate test method: choose a co...

Embodiment 2

[0037] A kind of preparation method of film veneer wood-based panel, comprises the following steps:

[0038](A): Wetting the decorative film with a sodium bicarbonate solution with a mass fraction of 10%, after wetting for 15 minutes, cleaning and drying to obtain a pretreatment film;

[0039] (B): The adhesive polyurethane was scraped onto the surface of the pretreatment film with a thickness of 200 μm, and heated at 80° C. for 20 minutes to obtain an adhesive film;

[0040] (C): The surface of the plywood is sprayed with a silane coupling agent solution with a mass fraction of 1.0%. The silane coupling agent solution is prepared by dissolving ethoxysilane in ethanol. After the surface of the plywood is dried, a pretreated plywood is obtained;

[0041] (D) The adhesive film was pretreated at 180°C for 30s and then attached to the surface of the pretreated plywood to obtain an adhesive film-faced wood-based panel.

[0042] Adhesive effective utilization rate test method: choo...

Embodiment 3

[0045] A kind of preparation method of film veneer wood-based panel, comprises the following steps:

[0046] (A): Wetting the decorative film with a triethanolamine solution with a mass fraction of 10%, after wetting for 20 minutes, cleaning and drying to obtain a pretreatment film;

[0047] (B): The adhesive polyurethane was scraped onto the surface of the pretreatment film with a thickness of 100 μm, and heated at 50° C. for 6 minutes to obtain an adhesive film;

[0048] (C): The surface of the plywood is sprayed with a silane coupling agent solution with a mass fraction of 1.0%. The silane coupling agent solution is prepared by dissolving ethoxysilane in ethanol. After the surface of the plywood is dried, a pretreated plywood is obtained;

[0049] (D) The adhesive film was pretreated at 120°C for 100s and then attached to the pretreated plywood surface to obtain an adhesive film-faced wood-based panel.

[0050] Adhesive effective utilization rate test method: choose a comm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of an adhesive film veneer artificial board. The preparation method of the adhesive film veneer artificial board comprises the following steps that firstly, a decorative film is pretreated to obtain a pretreated film, an adhesive is blade-coated on the surface of the pretreated film, and an adhesive film is obtained by heating; and then a plywood is pretreated, the pretreated plywood is obtained, the adhesive film is heated and attached to the surface of the pretreated plywood, and the adhesive film veneer artificial board is obtained. According to the preparation method of a veneer artificial board adhesive film, a decorative film and the plywood are pretreated, and meanwhile, the binding force of the adhesive film and the plywood is increased by 0.1-0.3 MPa through the coating technology of preheating and pressurizing; in addition, the adhesive is coated on the decorative film in a blade coating manner, so that the utilization rate of the adhesive can be increased by 40-60%.

Description

technical field [0001] The invention relates to the technical field of veneered wood-based panels, in particular to a method for preparing an adhesive film veneered wood-based panel. Background technique [0002] Facing wood-based panels are widely used in furniture, cabinets and fixed wardrobes, floors, wooden doors and other decoration fields, and are important raw materials for the custom wooden furniture industry. At present, the wood-based panel facing materials on the market mainly include various impregnated film papers and polymer film non-paper-based facing materials. Among them, PVC polymer decorative film is very popular among consumers because of its realistic texture and delicate touch, which can meet the individual needs of different consumers for furniture. [0003] The preparation method of the present facing wood-based panel is mainly to spray the adhesive on the plywood, then stick the PVC decorative film with pattern on the plywood, after the adhesive dri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27D1/08B44C5/04C09J5/02
CPCB27D1/08B44C5/043C09J5/02
Inventor 高静华杨马晓侠
Owner 浙江世瑞骐碳科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap