Antibacterial polypropylene material and preparation method thereof

An antibacterial polypropylene and polypropylene technology, applied in the field of antibacterial polypropylene material and its preparation, can solve the problems of high price, difficult dispersion, inability to achieve broad-spectrum antibacterial, etc., and achieve the effect of low cost and abundant sources

Active Publication Date: 2021-10-26
HEFEI GENIUS NEW MATERIALS
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, it is necessary for the present invention to provide an antibacterial polypropylene material and a preparation method thereof, adding feldspar inorganic minerals to the polypropylene formulation system, so that the polypropylene material obtains antibacterial properties, and solves the problem of existing antibacterial agents There are technical problems that are expensive, difficult to disperse, and unable to achieve broad-spectrum antibacterial

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] According to parts by weight, 89.9 parts of polypropylene, 3 parts of KAlSi 3 o 8 , 5 parts of vinyl elastomer (POE), 0.2 parts of tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester, 0.3 parts of tris[2,4-di-tert-butyl Base phenyl] phosphite, 1.2 parts of silicone powder and 0.4 parts of polypropylene grafted maleic anhydride were added to the high mixer and dry mixed for 8 minutes, and then the uniform mixture was added to the twin-screw extruder for melt extrusion and granulation , to obtain an antibacterial polypropylene material, wherein the temperature of the first zone of the twin-screw extruder is 170°C, the second zone is 175°C, the third zone is 205°C, the fourth zone is 205°C, and the fifth zone is 195°C.

Embodiment 2

[0027] According to parts by weight, 90.5 parts of polypropylene, 4 parts of NaAlSi 3 o 8 , 5 parts of ethylene-propylene-diene rubber (EPDM), 0.3 parts of tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester, 0.4 parts of three [2,4-di-tert Butylphenyl] phosphite, 1.3 parts of calcium stearate and 0.5 parts of silane coupling agent are added to the high mixer and dry mixed for 6 minutes, and then the uniform mixture is added to the twin-screw extruder to melt and extrude to granulate. An antibacterial polypropylene material was prepared, wherein the temperature of the first zone of the twin-screw extruder was 170°C, that of the second zone was 170°C, that of the third zone was 205°C, that of the fourth zone was 200°C, and that of the fifth zone was 195°C.

Embodiment 3

[0029] According to parts by weight, 87.2 parts of polypropylene, 2.5 parts of CaAl 2 Si 2 o 8 , 4 parts of styrene-butadiene elastomer (SBS) and 4 parts of styrene-butadiene-styrene elastomer (SEBS), 0.2 parts of tetrakis[β-(3,5-di-tert-butyl-4- Add 0.4 parts of tris[2,4-di-tert-butylphenyl] phosphite, 1.4 parts of zinc stearate and 0.3 parts of titanate coupling agent into the high mixer and dry After mixing for 7 minutes, put the uniform mixed material into the twin-screw extruder to melt and extrude to obtain antibacterial polypropylene material. Zone 205°C, Zone 4 200°C, Zone 5 195°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antibacterial polypropylene material and a preparation method thereof. The antibacterial polypropylene material is prepared from 82-96.4 parts by weight of polypropylene, 2-5 parts by weight of an inorganic antibacterial agent, 0-10 parts by weight of a flexibilizer, 0.4-0.9 part by weight of an antioxidant, 1-1.5 parts by weight of a lubricant and 0.2-0.6 part by weight of a coupling agent, and the inorganic antibacterial agent is a feldspar inorganic mineral. The antibacterial polypropylene disclosed by the invention is excellent in antibacterial property, green and environment-friendly, and can realize long-acting antibacterial property.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to an antibacterial polypropylene material and a preparation method thereof. Background technique [0002] As one of the most common general-purpose engineering plastics, polypropylene is widely used in automobiles, electronic appliances, daily consumables, and packaging materials due to its good mechanical properties, aging resistance, and low price. With the development of the plastic industry, plastic products have become an indispensable product in people's life and industrial production. However, when the objective conditions such as temperature and humidity are suitable, harmful microorganisms such as bacteria and mold will breed on plastic products, seriously endangering the human body. Human health, even life-threatening. [0003] The demand for antibacterial polypropylene is also increasing. Since polypropylene itself has no antibacterial properties, antibacter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L23/08C08L23/16C08L53/02C08L51/06C08K13/02C08K3/34
CPCC08L23/12C08L2205/03C08L2205/035C08K2201/014C08L23/0815C08K13/02C08K3/34C08L23/16C08L53/02C08L53/025C08L51/06
Inventor 杨桂生计娉婷姚晨光朱敏廖雄兵赵鑫
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com