A smelting method for producing φ12-25mmhrb500e straight bars by microalloying

A smelting method and microalloying technology, applied in the field of metallurgy, can solve problems such as brittle fracture of steel bars and increased quality risks

Active Publication Date: 2022-06-21
XINJIANG BAYI IRON & STEEL
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Adding Cr and Mn at the same time can improve the strength, but it will also cause non-ferrite pearlite structure in the steel structure, which will easily cause brittle fracture of the steel bar when it is bent, and increase the quality risk

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A smelting method for producing φ12-25mmhrb500e straight bars by microalloying
  • A smelting method for producing φ12-25mmhrb500e straight bars by microalloying

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027]A smelting method for producing Φ12-25mmHRB500E straight steel bars by microalloying. %, P: ≤0.04%, N: 0.01~0.015%, Ti: 0.03~0.05%, V: 0.05~0.07%, Cr: 0.1~0.3%, the sum of the mass percentages of Cr+Mn ≤1.55%, Ceq ≤0.54%; smelting method: adding pre-deoxidized composite slag lotion in converter tapping, the mass percentage composition of the slag lotion is: fluorite 5-10%, calcium carbide 65-75%, limestone 15-25%; Ti, V-composite micro-alloying smelting process technology and process steps, control the timing of adding Ti iron and the application of new materials to increase N in molten steel, that is, the application of high-nitrogen composite strengtheners, control high Si content, add Cr, reduce Mn, and realize Ti, V composite micro Alloy production of small size Φ12-25mmHRB500E straight steel bars: the carbon content at the end of the converter is less than or equal to 0.06%, and the amount of pre-deoxidized composite slag lotion is 2.0 kg / t; The dosage of agent add...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
strong bend ratioaaaaaaaaaa
Login to View More

Abstract

The invention discloses a smelting method for producing Φ12-25mm HRB500E straight steel bar by microalloying. The chemical composition of the steel bar is: C: 0.19-0.25%, Si: 0.60-0.80%, Mn: 1.10-1.4%, S: ≤0.04%, P: ≤0.04%, N: 0.01~0.015%, Ti: 0.03~0.05%, V: 0.05~0.07%, Cr: 0.1~0.3%, the sum of the mass percentages of Cr+Mn≤1.55% , Ceq≤0.54%; smelting method: add pre-deoxidation composite slag lotion to the converter tapping, the mass percentage composition of the slag lotion is: 5‑10% fluorite, 65‑75% calcium carbide, 15‑25% limestone; converter Add pre-deoxidation composite slag lotion after tapping, and then add silicon-manganese alloy, ferrosilicon, and high-carbon ferrochromium alloy in sequence. All alloys must be added at 1 / 3 of tapping, and all alloys should be added at 3 / 4 of tapping. Finished, the high nitrogen composite strengthener is added after the addition of the converter alloy, the addition amount is 0.6-0.8kg / t, and its composition: N 12-20%, Ti 18-25%, after the titanium-iron and vanadium-nitrogen alloys are added Carry out soft blowing, the soft blowing effect can be as large as 100-200mm in diameter of exposed molten steel after breaking the steel slag.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and relates to a smelting method for producing Φ12-25mm HRB500E straight steel bars by microalloying with Ti, V, N and Cr that meets the requirements of the GB / T1499.2-2018 standard. Background technique [0002] HRB500E is a steel grade specified in GB / T1499.2-2018 "Reinforced Concrete Reinforced Steel Part 2: Hot-Rolled Ribbed Steel Bar", formerly known as Grade 4 threaded steel bar, is a kind of high-strength earthquake-resistant steel bar, which is currently used in high-rise buildings and ultra-high-rise buildings. High-strength steel bars used in high-rise buildings. In GB / T1499.2-2018, the upper limit of C, Si, Mn, P, S elements and the upper limit of Ceq (carbon equivalent) are specified, and V, Nb, Ti and other elements can be added as needed; the N content in the steel is also specified. It should be no more than 0.012%. If there is a sufficient amount of N binding elements in the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/28C22C38/24C22C33/06C21C7/00
CPCC22C38/02C22C38/04C22C38/001C22C38/28C22C38/24C22C33/06C21C7/0006
Inventor 陈海军宋维兆王建新
Owner XINJIANG BAYI IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com