Hot bath forming process of high-corrosion-resistance and easy-to-weld hot-pressing part

A forming process and component technology, which is applied in the field of hot bath forming process of high corrosion resistance and easy to weld hot-pressed components, can solve the problems of difficult control of pre-cooling temperature, difficulty in uniform and controllable cleaning of extremely thin surface oxide layer, and achieve Reduce processing and manufacturing costs, reduce mold damage, and improve tissue performance

Active Publication Date: 2021-12-07
SD STEEL RIZHAO CO LTD
View PDF10 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The purpose of the present invention is to overcome the deficiencies in the prior art, especially the extremely thin surface oxide layer is difficult to uniform and controllable cleaning, the pre-cooling temperature is difficult to control, etc., so as to provide a hot bath forming of high corrosion resistance and easy welding hot-pressed parts Proce

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot bath forming process of high-corrosion-resistance and easy-to-weld hot-pressing part
  • Hot bath forming process of high-corrosion-resistance and easy-to-weld hot-pressing part
  • Hot bath forming process of high-corrosion-resistance and easy-to-weld hot-pressing part

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A hot-bath forming process for high-corrosion-resistant and easy-to-weld hot-pressed parts, such as figure 1 shown, including the following steps:

[0044] S1, 1.5mm thick galvanized hot-formed steel sheet (matrix composition includes C 0.18-0.21wt%, Si 0.05-0.2wt%, Mn 1.5-2.2wt%, Cr 0-0.3wt%, Mo 0-0.25wt% , Ti 0.02-0.04wt%, Nb 0-0.1wt%, B 0.002-0.006wt%, P 0-0.020wt%, S 0-0.003wt%, Al 0.02-0.06wt%, N 0-0.006wt%; Double GI surface galvanized 150g / m 2 , one side thickness 11um) transferred to 890 ℃ box-type heating furnace, heat preservation 5min, complete austenitization; the oxygen content (volume fraction) of the atmosphere in the heating furnace is 20%.

[0045] S2. After the heating is completed, the plate is transferred to the boiling water tank, immersed in boiling water for even cleaning and cooling, the depth is 3-1000mm, and the boiling water temperature is 100°C; the residence time of the steel plate in the boiling water is 6s.

[0046] S3. Since the mold i...

Embodiment 2

[0050] A hot bath forming process for highly corrosion-resistant and easy-to-weld hot-pressed parts, comprising the following steps:

[0051] S1, plate thickness 1.5mm galvanized hot-formed steel sheet (matrix composition includes C 0.05-0.35wt%, Si 0.05-0.2wt%, Mn 0.5-2.5wt%, Cr 0-0.3wt%, Mo 0-0.25wt% , Ti 0.02-0.04wt%, Nb 0-0.2wt%, V 0-0.2wt%, B 0.002-0.006wt%, P 0-0.020wt%, S 0-0.003wt%, Al 0.02-0.06wt%, N 0-0.006wt%, the remaining elements are Fe; double GA surface galvanized 150g / m 2 , thickness 11um on one side) was transferred to a 900°C box-type heating furnace and held for 5 minutes to complete austenitization; the oxygen content (volume fraction) of the atmosphere in the heating furnace was 20%.

[0052] S2. After the heating is completed, the plate is transferred to the boiling water tank, immersed in boiling water to wash evenly and cool down. The depth of the plate is 3-1000mm, and the boiling water temperature is 80°C; the residence time of the steel plate in th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a hot bath forming process of a high-corrosion-resistance and easy-to-weld hot-pressing part, and relates to the field of thin plate hot stamping and sheet metal part manufacturing. The process comprises the following steps of S1, heating a plated hot-formed steel plate in a heating furnace until the plated hot-formed steel plate is in a complete austenitizing state; S2, transferring the heated plated hot-formed steel plate into a boiling water tank, immersing the plated hot-formed steel plate in boiling water, and cleaning an oxide layer; S3, forming the coating hot forming steel plate under the combined action of boiling water, an upper mold and a lower mold, carrying out pressure maintaining and quenching, obtaining a part; and S4, taking out the part to perform air blowing or drying treatment in a drying furnace, and moisture in a plating layer of the part is removed. According to the process, the plate is immersed in the boiling water, a surface oxide layer is uniformly and controllably removed by virtue of bubbles generated between the boiling water and a hot plate, the forming temperature of the plate is uniformly and accurately controlled, and meanwhile, forming and quenching are performed in the boiling water, so that the production quality of parts can be improved, the service life of a mold is prolonged, and the production cost is saved.

Description

technical field [0001] The invention relates to the field of hot stamping of thin plates and the manufacture of sheet metal parts, in particular to a hot-bath forming process for high-corrosion-resistant and easy-to-weld hot-pressed parts. Background technique [0002] The main process in the hot stamping forming process is: blank heating - stamping forming and quenching - laser trimming, shot blasting. Hot stamping technology has been widely used due to the advantages of small forming force, small part springback and high strength after forming. Edges will corrode ahead of time, especially lower body parts such as sill beams. [0003] Due to the low melting point of the galvanized layer (the melting point of pure Zn is only about 400°C), the austenitization temperature of the base material is high (850-900°C); and in the direct thermoforming process, the lower the coating temperature, the better (650°C below), and the higher the substrate temperature, the better (above 75...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B08B3/10B08B3/12B21D22/02C21D1/18C21D8/02C22C38/02C22C38/04C22C38/06C22C38/22C22C38/24C22C38/26C22C38/28C22C38/32C23C8/10C23C8/80C23F17/00C23G1/19
CPCB08B3/106B21D22/022B08B3/12C23F17/00C23C8/10C23C8/80C23G1/19C21D1/18C22C38/02C22C38/04C22C38/22C22C38/28C22C38/26C22C38/24C22C38/32C22C38/06C21D8/0205C21D8/0247
Inventor 刘培星郝亮陈钢高兴昌高鹏金光宇侯晓英汤化胜孙卫华
Owner SD STEEL RIZHAO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap