A treatment agent for purifying liquefied petroleum gas and its preparation method

A liquefied petroleum gas and treatment agent technology, which is applied in the petroleum industry, gas fuel, fuel, etc., can solve the problems of cumbersome process and unsatisfactory purification effect, and achieve the effect of simple process, simple use method and good purification effect

Active Publication Date: 2022-05-13
ZHEJIANG MEIFU PETROCHEMICAL CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The patented process is cumbersome and can only achieve desulfurization, and the purification effect is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A treatment agent for purifying liquefied petroleum gas and its preparation method
  • A treatment agent for purifying liquefied petroleum gas and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A preparation method for a treatment agent for liquefied petroleum gas purification, the specific steps are as follows:

[0039] (1) earlier take manganese nitrate, antimony nitrate and titanium tetrachloride as raw material, make manganese, antimony doped titanium dioxide;

[0040] (2) Then manganese and antimony doped titanium dioxide are modified on the surface by polyethyleneimine to obtain a modified material;

[0041] (3) The modified material is then reacted with epoxidized cellulose to obtain a composite material;

[0042] (4) Add composite material to the modified bentonite premix again, ultrasonically oscillate evenly, polymerize, and dry to obtain the treatment agent;

[0043] Among them, the modified bentonite premix is ​​obtained by using bentonite as a raw material, which is modified by γ-methacryloxypropyltrimethoxysilane first, and then uniformly mixed with acrylamide and water.

[0044] The specific method of step (1) is as follows: first 1kg manganese ...

Embodiment 2

[0056] A preparation method for a treatment agent for liquefied petroleum gas purification, the specific steps are as follows:

[0057] (1) earlier take manganese nitrate, antimony nitrate and titanium tetrachloride as raw material, make manganese, antimony doped titanium dioxide;

[0058] (2) Then manganese and antimony doped titanium dioxide are modified on the surface by polyethyleneimine to obtain a modified material;

[0059] (3) The modified material is then reacted with epoxidized cellulose to obtain a composite material;

[0060] (4) Add composite material to the modified bentonite premix again, ultrasonically oscillate evenly, polymerize, and dry to obtain the treatment agent;

[0061] Among them, the modified bentonite premix is ​​obtained by using bentonite as a raw material, which is modified by γ-methacryloxypropyltrimethoxysilane first, and then uniformly mixed with acrylamide and water.

[0062] The specific method of step (1) is as follows: first 1kg manganes...

Embodiment 3

[0074] A preparation method for a treatment agent for liquefied petroleum gas purification, the specific steps are as follows:

[0075] (1) earlier take manganese nitrate, antimony nitrate and titanium tetrachloride as raw material, make manganese, antimony doped titanium dioxide;

[0076] (2) Then manganese and antimony doped titanium dioxide are modified on the surface by polyethyleneimine to obtain a modified material;

[0077] (3) The modified material is then reacted with epoxidized cellulose to obtain a composite material;

[0078] (4) Add composite material to the modified bentonite premix again, ultrasonically oscillate evenly, polymerize, and dry to obtain the treatment agent;

[0079] Among them, the modified bentonite premix is ​​obtained by using bentonite as a raw material, which is modified by γ-methacryloxypropyltrimethoxysilane first, and then uniformly mixed with acrylamide and water.

[0080] The specific method of step (1) is as follows: first 1kg manganes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a treatment agent for liquefied petroleum gas purification and a preparation method thereof. First, manganese nitrate, antimony nitrate and titanium tetrachloride are used as raw materials to prepare manganese and antimony doped titanium dioxide; then manganese and antimony are mixed with manganese and antimony. Hetero-titanium dioxide is surface-modified with polyethyleneimine to obtain a modified material; then the modified material is reacted with epoxidized cellulose to obtain a composite material; the composite material is then added to the modified bentonite premix, ultrasonically oscillated uniformly, and polymerized Reaction, drying, and that's it. The treating agent can realize one-step purification of liquefied petroleum gas, has simple process and good purification effect.

Description

technical field [0001] The invention relates to a liquefied petroleum gas purification material, in particular to a treatment agent for liquefied petroleum gas purification and a preparation method thereof. It belongs to the technical field of liquefied petroleum gas. Background technique [0002] The production methods of liquefied petroleum gas mainly include oilfield associated gas or natural gas extraction, and oil refining extraction. In addition to its main components such as propane, propylene and butane, it often contains more impurities, such as H 2 S, COS, CS 2 , mercaptan, sulfide and disulfide, etc., are poisonous and harmful, seriously pollute the environment and damage human health, and can also cause catalyst poisoning, corrosion of equipment, etc. during the production process, which in turn produces more impurities, resulting in the quality of liquefied petroleum gas not meeting the requirements Related standards. [0003] In addition, the moisture in the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10L3/12
CPCC10L3/12
Inventor 程键雄刘丰敏胡敏达王裕振
Owner ZHEJIANG MEIFU PETROCHEMICAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com