Forming method of high-speed tool steel bar

A high-speed tool steel and forming method technology, applied in the direction of metal extrusion dies, etc., can solve the problems that the process method and equipment configuration cannot meet the product quality requirements, low production efficiency, discontinuous production, etc.

Pending Publication Date: 2021-12-31
HANDAN XINXING SPECIAL TUBING CO LTD
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the common problem in the existing rod and wire production lines is that the wire rods of different specifications are all produced on one line, resulting in discontinuous production and low production efficiency. The equipment configuration cannot meet the product quality requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Forming method of high-speed tool steel bar
  • Forming method of high-speed tool steel bar
  • Forming method of high-speed tool steel bar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The present invention will be described in detail below in conjunction with the embodiments and the accompanying drawings. The protection scope of the present invention is not limited to the embodiments, and any changes made by those skilled in the art within the scope defined in the claims also belong to the protection scope of the present invention.

[0028] The high-speed tool steel bar stock of the present invention is formed by a hot extrusion method, and the production system for forming the high-speed tool steel bar stock is used for forming production. The material of high-speed tool steel is W6Mo5Cr4V2 in GB / T9943, and the bar product specification is φ120mm (outer diameter).

[0029] Production systems for high-speed tool steel bar forming such as figure 1 As shown, it includes machining equipment 1, double alloy billet preparation equipment 2, double alloy billet processing equipment 3, resistance furnace 4, electromagnetic induction furnace 5, extrusion mac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a forming method of a high-speed tool steel bar. The forming method comprises the following forming steps: (1) calculating the size of a double-alloy blank; (2) smelting a high-speed tool steel casting blank; (3) producing an austenitic steel seamless steel pipe; (4) performing sawing and segmenting; (5) machining the raw materials; (6) preparing a double-alloy blank; (7) vacuumizing the double-alloy blank; (8) processing the double-alloy blank; (9) heating to 1120 DEG C; (10) performing electromagnetic induction heating at 1150-1160 DEG C; (11) performing double-alloy extrusion forming; (12) performing annealing; (13) performing pressure straightening; and (14) removing outer austenitic steel, and manufacturing the high-speed tool steel bar. The double-layer blank is prepared and formed through the hot extrusion process, the defects that high-speed steel is high in heat dissipation speed, poor in plasticity and prone to oxidation at high temperature, and extrusion cracking is caused are overcome, and the qualified rate of products is increased.

Description

technical field [0001] The invention belongs to the technical field of steel forming production, and relates to a forming method of high-speed tool steel bars. Background technique [0002] Due to the existence of coarse network eutectic carbides in the high-speed steel ingot after smelting, the steel becomes brittle. This kind of coarse eutectic carbide cannot be eliminated by heat treatment, but can only be broken by plastic deformation. High-speed steel has high alloy content, poor thermoplasticity, and narrow thermal processing temperature range. The existing mature manufacturing technology is: using forging technology, through upsetting and elongation to break the carbides, and realize the small size and uniform distribution of the carbides to obtain the material. High hardness and good toughness. However, the forging process produces a small amount of deformation in a single pass, and requires multiple processing times to reach the finished product size. The producti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B21C25/02B21C29/04
CPCB21C25/02B21C29/04Y02P10/25
Inventor 王锦永齐希伦刘静张艳
Owner HANDAN XINXING SPECIAL TUBING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com