Honeycomb aluminum plate based on hot press molding and preparation process thereof

A technology of honeycomb aluminum plate and hot press forming, which is applied in metal material coating process, coating, construction, etc., can solve the problems of insufficient performance of honeycomb aluminum plate, and achieve the effect of avoiding glue cracking, simple process and enhanced performance

Pending Publication Date: 2022-02-08
晋江市新思维环保科技有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The performance of the current honeycomb aluminum panels is generally the same as or close to the requirements of the standard (JG/T334-2012 "Aluminum Honeycomb Composite Panels for Building Exter

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Honeycomb aluminum plate based on hot press molding and preparation process thereof
  • Honeycomb aluminum plate based on hot press molding and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] As an exterior wall honeycomb composite panel, the standard panel size is 1200mm x2400mm, and the thickness is: standard panel 20mm;

[0033] a) Cutting and surface cleaning: take two aluminum plates and aluminum honeycomb cores for size cutting, and after cutting, perform surface grinding and surface cleaning;

[0034] b) Laser cladding: take 100% pure nickel powder for drying treatment, preheat the inner and outer surfaces of the aluminum honeycomb core, the preheating temperature is 60°C, put the above nickel powder into the powder feeder, set the laser Cladding parameters, laser power 3000W, scanning speed 8mm / s, powder feeding rate 20g / min, spot diameter 5mm, lap rate 25%, nickel layer cladding on the inner and outer surfaces of the preheated aluminum honeycomb core, nickel The layer thickness is 5 μm;

[0035] c) Chromizing treatment: get an aluminum plate in step a), carry out chromizing treatment to one surface thereof, the steps of chromizing treatment are:

...

Embodiment 2

[0051] As an exterior wall honeycomb composite panel, the standard panel size is 1000mm x2000mm, and the thickness is: standard panel 20mm;

[0052] a) Cutting and surface cleaning: take two aluminum plates and aluminum honeycomb cores for size cutting, and after cutting, perform surface grinding and surface cleaning;

[0053] b) Laser cladding: take 100% pure nickel powder for drying treatment, preheat the inner and outer surfaces of the aluminum honeycomb core, the preheating temperature is 60°C, put the above nickel powder into the powder feeder, set the laser Cladding parameters, laser power 2500W, scanning speed 6mm / s, powder feeding rate 20g / min, spot diameter 3mm, lap rate 25%, nickel cladding on the inner and outer surfaces of the preheated aluminum honeycomb core, nickel The layer thickness is 8 μm;

[0054] c) Chromizing treatment: get an aluminum plate in step a), carry out chromizing treatment to one surface thereof, the steps of chromizing treatment are:

[0055...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of honeycomb aluminum plates and preparation processes thereof, and particularly relates to a honeycomb aluminum plate based on hot press molding and a preparation process thereof. The honeycomb aluminum plate comprises two aluminum plates and an aluminum honeycomb core sandwiched between the two aluminum plates, and the honeycomb aluminum plate is integrally formed through a hot press molding process. According to the invention, the aluminum honeycomb core is coated with the nickel layer through laser cladding, and the performance of the whole honeycomb aluminum plate is enhanced through paint spraying and chromizing treatment in various procedures of synthesizing the aluminum plate, so that the requirement of meeting more than two times of an outer wall decorative surface of a special building is met; the chromizing liquid adopted for chromizing treatment of the aluminum plate is composed of chromic nitrate, oxalic acid, cobalt salt, sodium dodecyl sulfate and borate, and has the advantages of being environmentally friendly, efficient, capable of saving energy, resistant to hard water and integrated, so that the efficiency of the preparation process is improved, the preparation process is more environmentally friendly, and the process is simpler.

Description

technical field [0001] The invention belongs to the technical field of honeycomb aluminum plate and its preparation process, in particular to a honeycomb aluminum plate based on hot pressing and its preparation process. Background technique [0002] Composite honeycomb panels are generally composed of plates and honeycomb cores, with very high strength and rigidity. It is generally used as a decorative surface for building exterior walls. [0003] The performance of the current honeycomb aluminum panels is generally the same as or close to the requirements of the standard (JG / T334-2012 "Aluminum Honeycomb Composite Panels for Building Exterior Walls", but the exterior wall decoration requirements of some special buildings are more than twice the standard, while the existing technology The performance of the honeycomb aluminum plate is not enough. Contents of the invention [0004] (1) Technical problems to be solved [0005] In order to overcome the defects in the above...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): E04F13/075C23C22/46C23C22/78C23C22/83C23C24/10B21C37/02
CPCE04F13/0875C23C24/106C23C22/78C23C22/46C23C22/83B21C37/02
Inventor 詹景谦
Owner 晋江市新思维环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap