Oil shale semicoke adsorption inhibitor and application thereof in concrete preparation

An oil shale semi-coke and inhibitor technology, which is applied to the application of the adsorption inhibitor in the preparation of concrete, in the field of oil shale semi-coke adsorption inhibitor, can solve the problem of concrete workability, poor workability and limitation Resource utilization of oil shale semi-coke, affecting on-site pouring construction and other issues, to achieve the effect of reasonable formula design, high-value utilization of resources, and easy processing

Active Publication Date: 2022-02-18
GANSU ZHITONG TECH ENG DETECTION CONSULTING CO LTD
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most of the oil shale semi-coke is stacked at home and abroad, which not only occupies a large amount of available arable land, but also pollutes water resources, deteriorates water quality, and causes waste of resources
As an additional product of oil shale, oil shale semi-coke is also often used as concrete material for construction. However, in practical applications, it is found that oil shale semi-coke powder is loose and porous and has strong water absorption. The superplasticizer added in the concrete preparation process has strong adsorption, which not only increases the dosage of the superplasticizer, but also deteriorates the workability and workability of the concrete, which in turn affects the on-site pouring construction, which greatly Limit resource utilization of oil shale semi-coke

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oil shale semicoke adsorption inhibitor and application thereof in concrete preparation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The oil shale semi-coke adsorption inhibitor provided in this example is prepared by mixing 52 parts by weight of anti-corrosion rheology agent, 5 parts of methanol, 2 parts of sulfonated melamine, 5 parts of EDTA, 30 parts of sodium perfluorosilicon with A mixture with a mass ratio of polymethyl vinyl siloxane of 5:1 and 6 parts of stearate are sequentially added to the mixing container, and the mixture is fully stirred to obtain the result.

[0027] The content of the adsorption inhibitor in the oil shale semi-coke is 0.05%.

Embodiment 2

[0029] The oil shale semi-coke adsorption inhibitor provided in this example is composed of 50.5 parts by weight of anti-corrosion rheology agent, 10 parts of methanol, 1.5 parts of sulfonated melamine, 3 parts of EDTA, 25 parts of organosilicon compound (methyl benzene) Sodium silicolate, sodium perfluorosiliconate and cyclopentyl methacrylate-cubic oligomeric silsesquioxane nanocomposite in a mass ratio of 2:2:1), 10 parts of stearate were added in turn and mixed In a container, stir well.

[0030] The content of the adsorption inhibitor in the oil shale semi-coke is 0.08%.

Embodiment 3

[0032] The oil shale semi-coke adsorption inhibitor provided in this example is composed of 50.5 parts by weight of anti-corrosion rheology agent, 15 parts of methanol, 1.5 parts of sulfonated melamine, 3 parts of EDTA, and 25 parts of organosilicon compound (methyl methacrylate). Sodium silicolate, sodium high fluorosiliconate and cyclopentyl methacrylate-cubic oligomeric silsesquioxane nanocomposite in a mass ratio of 2:1:2), 5 parts of stearate were added in turn and mixed In a container, stir well.

[0033] The content of the adsorption inhibitor in the oil shale semi-coke is 0.10%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sand rateaaaaaaaaaa
Login to view more

Abstract

The invention discloses an oil shale semicoke adsorption inhibitor and application thereof in concrete preparation. The adsorption inhibitor is prepared by the following steps: sequentially adding 50-52.5 parts by weight of an anti-corrosion rheological agent, 5-20 parts by weight of methanol, 0.5-2 parts by weight of sulfonated melamine, 2-5 parts by weight of EDTA, 20-30 parts by weight of an organosilicon compound and 5-10 parts by weight of stearate into a mixing container, and fully and uniformly stirring, wherein the anti-corrosion rheological agent is a 'microbead' water-reducing active micro aggregate. The adsorption inhibitor is doped into the industrial solid waste oil shale semi-coke powder, so that the problems of strong water absorption, high water reducing agent adsorption and the like of the oil shale semi-coke are solved, the use amount of the water reducing agent is reduced in concrete production, and the obtained concrete is good in workability and workability; and due to a certain dispersing and grinding-aiding effects, the power consumption during grinding can be reduced; and finally, large-dosage resource utilization of the oil shale semi-coke in the cement-based concrete is realized, and high-value resource utilization of the oil shale semi-coke is realized.

Description

technical field [0001] The invention relates to the technical field of industrial solid waste utilization, in particular to the resource utilization technology of oil shale semi-coke as a concrete material, in particular to an oil shale semi-coke adsorption inhibitor, and the invention also relates to the use of the adsorption inhibitor in concrete application in preparation. Background technique [0002] Oil shale, also known as oil mother shale, is a kind of sedimentary rock containing combustible organic matter with high ash content. It belongs to fossil fuels like coal, oil and natural gas. It is a non-renewable resource and primary energy. Oil shale will produce a large amount of by-product waste in the process of dry distillation, namely oil shale semi-coke, which is a low-quality fuel with high ash content and low calorific value, and contains water-soluble phenol, sulfide, polycyclic aromatic hydrocarbons and other toxic pollution. If not handled properly, it will c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/42
CPCC04B40/0039C04B18/082C04B24/026C04B24/22C04B24/123C04B24/42C04B24/085C04B18/0481Y02W30/91C04B28/02C04B18/08C04B24/02C04B24/223C04B24/08C04B40/0028C04B18/125C04B20/026C04B24/20C04B28/026C04B2103/0079C04B2103/61C04B2111/26
Inventor 牛敏敏冯月娥何艳张会平李亚飞
Owner GANSU ZHITONG TECH ENG DETECTION CONSULTING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap