Preparation method of wood fiber powder

A wood fiber powder and wood fiber technology are applied in the field of preparation of wood fiber powder, which can solve the problems of high cost of wood fiber, poor anti-ultraviolet ability, insufficient toughness, etc., and achieve low cost of material selection, high toughness and strength, and simple process. Effect

Pending Publication Date: 2022-03-11
江苏金玉丰新材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies of the prior art, the present invention provides a preparation method of wood fiber powder, which solves the technical problems of high wood fiber cost, poor UV resistance and insufficient toughness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1: wood fiber adopts corn bellflower

[0015] A preparation method of wood fiber powder, comprising the following steps:

[0016] S1: crushing, selecting corn platycodon grandiflorum, and using a crushing mixer to crush and stir, to obtain corn platycodon grandiflorum powder of 30-150 mesh.

[0017] S2: Put 30-150 mesh corn platycodon root powder in the reactor, add calcium hydroxide solvent, brew for 60 minutes, control the temperature at 20°C, stir it with a stirring rod, stir for 20 minutes to make it evenly mixed, and put it in stably 3 parts of whitening agent, 1 part of whitening agent, and 0.5 part of anti-ultraviolet agent. After the reaction, use a filter to filter.

[0018] S3: Place the solvent filtered in the above S2 in a drying equipment for drying treatment, the drying time is 3 hours, dry the wood fiber powder until the moisture content is lower than 2%, and place the resultant in a mold to obtain wood fiber pink.

[0019] Further, when the...

Embodiment 2

[0022] Embodiment 2: wood fiber adopts bamboo

[0023] A preparation method of wood fiber powder, comprising the following steps:

[0024] S1: crushing, selecting bamboo, crushing and stirring with a crushing mixer, and obtaining a powder of 30-150 meshes.

[0025] S2: Put 30~150 powder in the reactor, add calcium hydroxide solvent, brew for 80 minutes, control the temperature at 25°C, stir it with a stirring rod, stir for 22 minutes to make it evenly mixed, and put in the stabilizer 3.5 parts, 1.2 parts of whitening agent, 0.6 parts of anti-ultraviolet agent, filter with filter after reaction.

[0026] S3: Place the solvent filtered in the above S2 in a drying equipment for drying treatment. The drying time is 3.5 hours. Dry the wood fiber powder until the moisture content is lower than 2%, and place the resultant in a mold to obtain a wood fiber powder. fiber powder.

[0027] Further, when the wood fiber is pulverized and stirred, it is soaked and washed three times to re...

Embodiment 3

[0030] Embodiment 3: wood fiber adopts cotton ridge

[0031] A preparation method of wood fiber powder, comprising the following steps:

[0032] S1: crushing, selecting cotton ridges, and using a pulverizer to grind and stir them to obtain 30-150 mesh cotton ridge powder.

[0033] S2: Put 30-150 mesh cotton ridge powder in S1 in the reactor, add calcium hydroxide solvent, brew for 100 minutes, control the temperature at 28°C, stir it with a stirring rod, stir for 25 minutes to make it evenly mixed, Add 4 parts of stabilizer, 1.4 parts of whitening agent, and 0.7 parts of anti-ultraviolet agent. After the reaction, use a filter to filter.

[0034] S3: Place the solvent filtered in the above S2 in a drying device for drying treatment. The drying time is 3.6 hours. Dry the wood fiber powder until the moisture content is lower than 2%, and place the resultant in a mold to obtain a wood fiber powder. fiber powder.

[0035] Further, when the wood fiber is pulverized and stirred, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wood fiber powder preparation method which comprises the following steps: S1, crushing: selecting wood fibers, and crushing and stirring by adopting a crushing stirrer to obtain 30-150-mesh wood powder; s2, 30-150-mesh wood flour is placed in a reactor, a calcium hydroxide solvent is added, soaking is conducted for 60-360 min, the temperature is controlled to range from 20 DEG C to 40 DEG C, stirring is conducted through a stirring rod for 20-30 min so that the wood flour and the calcium hydroxide solvent can be evenly mixed, 3-5 parts of a stabilizer, 1-2 parts of a whitening agent and 0.5-1 part of an anti-ultraviolet agent are added, and filtering is conducted through a filter after reaction; s3, the solvent filtered in the S2 is placed in drying equipment for drying treatment, the drying time is 3-5 h, the wood fiber powder is dried till the water content is lower than 2%, an obtained product is placed in a mold, and the wood fiber powder is obtained. The preparation method of the wood fiber powder is simple in process, simple and convenient in operation process and low in material selection cost, and the prepared wood fibers are resistant to ultraviolet rays and high in toughness strength.

Description

technical field [0001] The invention relates to the technical field of preparation of wood fiber powder, in particular to a preparation method of wood fiber powder. Background technique [0002] Lignocellulosic fiber is an organic flocculent fibrous substance obtained from natural renewable wood through chemical treatment and mechanical processing. It is widely used in concrete mortar, gypsum products, wood pulp sponge, asphalt roads and other fields. Lignocellulosic biomass has many advantages such as large output, abundant sources, low price, renewable, biodegradable, and environmental friendliness, and is an ideal industrial raw material. With the decreasing storage of fossil raw materials such as coal and petroleum, the research on using green and renewable biomass raw materials to replace traditional fossil raw materials as raw materials for industrial production has attracted the attention of countries all over the world. Lignocellulosic fiber is a kind of biomass ene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08K7/04C08H8/00
CPCC08K7/04C08H8/00C08L97/02
Inventor 庞振虎黄淑艳
Owner 江苏金玉丰新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap