Blending aid composition, synthetic resin, and polyolefin film/sheet

A synthetic resin and composition technology, applied in the field of polyolefin film processing, can solve problems such as easy delamination, poor adhesion of plating and coating, and achieve low odor function, high metallic luster, and excellent barrier properties

Active Publication Date: 2022-04-08
SHANGHAI ROYAL NEW MATERIALS TECH CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a kind of compounding aid composition and synthetic resin and polymer in order to overcome the poor coating and coating adhesion of the film surface treatment layer of the packaging material existing in the prior art, and the defect problem of easy delamination. Olefin film / sheet, the polyolefin film / sheet has good adhesion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blending aid composition, synthetic resin, and polyolefin film/sheet
  • Blending aid composition, synthetic resin, and polyolefin film/sheet
  • Blending aid composition, synthetic resin, and polyolefin film/sheet

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] According to the present invention, figure 1 It is a schematic flow diagram of the preparation method of the compounding aid composition of the present invention, such as figure 1 As shown, the preparation method for preparing a compounding aid by using the compounding aid composition of the present invention comprises: drying, mixing and stirring the compounding aid composition (antioxidant, stabilizer and adhesion enhancer) , granulation / cutting, sieving, cooling, shaping, and packaging to obtain the compounding aid. Preferably, the mixing and stirring is carried out under high-speed stirring conditions.

[0032] Wherein, the drying conditions include: temperature 25-50° C., time ≥ 4 hours.

[0033] Stirring conditions include: mixing and stirring with a low-speed mixer for 15-30 minutes.

[0034] The conditions for sieving include: using a vibrating sieve with a sieve aperture of ≤5mm for sieving.

[0035] The conditions of setting treatment include: setting with...

Embodiment 1

[0063] This example is intended to illustrate synthetic resin and polyolefin films / sheets prepared using the compounding aid composition of the present invention.

[0064] Compounding Auxiliary Composition:

[0065] The antioxidant is a compound of hydroxylamine antioxidant and phosphite antioxidant, with a weight ratio of 1:1;

[0066] The stabilizer is hydrotalcite, D 50 ≤150nm, MgO / Al 2 o 3 3:1;

[0067] Adhesion enhancers are specifically: ɑ-nucleating agent (brand is NX8000K), β-nucleating agent (brand is MT205-B), petroleum resin (specifically hydrogenated C9) and synergistic anti-blocking agent (specifically silicon dioxide) compound , The weight ratio of α-nucleating agent, β-nucleating agent, petroleum resin and synergistic opening agent is 0.005:0.005:1:0.5.

[0068] Wherein, based on the total weight of the compounding aid composition, the content of the antioxidant is 10% by weight, the content of the stabilizer is 10% by weight, and the content of the adhesio...

Embodiment 2

[0075] This example is intended to illustrate synthetic resin and polyolefin films / sheets prepared using the compounding aid composition of the present invention.

[0076] Synthetic resin and polyolefin film / sheet are prepared according to the same method as in Example 1, except that:

[0077] Compounding Auxiliary Composition:

[0078] The antioxidant is a compound of hydroxylamine antioxidant and phosphite antioxidant, with a weight ratio of 1:1;

[0079] The stabilizer is hydrotalcite, D 50 ≤150nm, MgO / Al 2 o 3 3:1;

[0080] The adhesion enhancer is specifically a compound of α-nucleating agent (specifically NX8000K), β-nucleating agent (specifically MT205-B), petroleum resin (specifically hydrogenated C9) and synergistic anti-blocking agent (specifically silicon dioxide), The weight ratio of α-nucleating agent, β-nucleating agent, petroleum resin and synergistic opening agent is 0.005:0.005:1:0.5.

[0081] Wherein, based on the total weight of the compounding aid com...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of polyolefin film processing, and discloses a mixed additive composition, synthetic resin and a polyolefin film / sheet. The mixed additive composition comprises one or more of an antioxidant, a stabilizer and an adhesion enhancer, and the adhesion enhancer is selected from one or more of an alpha nucleating agent, a beta nucleating agent, an optional elastomer, petroleum resin and a synergistic anti-blocking agent; on the basis of the total weight of the blending auxiliary agent composition, the content of the antioxidant is 0.005-10 wt%, the content of the stabilizer is 0.005-10 wt%, and the content of the adhesion enhancer is 80-99.99 wt%. The polyolefin film / sheet has good adhesive force.

Description

technical field [0001] The invention relates to the technical field of polyolefin film processing, in particular to a compounding aid composition, synthetic resin and polyolefin film / sheet. Background technique [0002] Materials are the material basis of human production. Polymer materials are widely used in the packaging industry to prevent the penetration of oxygen, water vapor, and carbon dioxide to keep food, fruits, and vegetables fresh. The growth rate of film production and consumption has been increasing in recent years. With the improvement of people's living standards and the diversification of aesthetics, consumers and producers are pursuing the ultimate in packaging quality and visual effects. [0003] For food preservation, fragrance preservation, and safety considerations, the functional requirements for packaging materials such as puncture resistance and barrier properties are getting higher and higher. It is hoped that external tastes and substances will no...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08K5/17C08K5/524C08K3/22C08K5/05C08K5/1575C08K5/098C08L57/02C08K3/36C08L23/12C08L23/14C08L23/08C08L23/06C08L23/20C08L23/00C08J5/18
Inventor 韦丽明
Owner SHANGHAI ROYAL NEW MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap