Sizing material for improving stripping performance and construction applicability of S-CLF YC type coiled material

An applicability and sizing technology, which is applied in the direction of asphalt material adhesives, adhesives, adhesive types, etc., can solve the problems of unsatisfactory peel strength, etc., to solve the defects of peel strength, improve peel performance, and facilitate construction Effect

Pending Publication Date: 2022-04-26
苏州卓宝科技有限公司 +1
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the above problems, the present invention studies the composition and construction process of the existing waterproof coiled material, and finds that asphalt, oil, SBS, butyl rubber, SBR, lignin, tackifying resin and stone powder are compounded within a specific range The glue obtained during the process can improve the defect that the peeling strength between the membrane and the post-cast concrete does not meet the requirements, and make the appearance of the S-CLF YC waterproof membrane smooth, and it is not easy to cause the sandy surface and yellowing of the membrane under high temperature conditions. phenomenon occurs, while ensuring that other properties meet the requirements of the standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sizing material for improving stripping performance and construction applicability of S-CLF YC type coiled material
  • Sizing material for improving stripping performance and construction applicability of S-CLF YC type coiled material
  • Sizing material for improving stripping performance and construction applicability of S-CLF YC type coiled material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0069] Preparation of butyl rubber

[0070] Heat 42kg of 150# aromatic hydrocarbon oil to 155°C, add 35kg of 1502 styrene-butadiene rubber and 5kg of SBS, then stir at a speed of 1000rpm for 30min, then increase the temperature of the mixed system to 180°C and stir at a speed of 1500rpm for 3h, then Add 2kg of wax powder and stir at a speed of 1500rpm for 0.5h, then grind until the system has no particles, finally add 16kg of 200 mesh talc powder and stir for 1h to make the system evenly mixed, and cool to room temperature to obtain butyl rubber.

preparation Embodiment 1

[0074] The specific composition of each raw material of the sizing material is shown in Table 1 below, and its preparation method includes the following steps.

[0075] (1) Mix the oil and asphalt evenly at 120°C;

[0076] (2) Heating the mixture obtained in the step (1) to 160° C., then adding SBS under agitation and mixing uniformly;

[0077] (3) Continue to add butyl rubber, SBR, lignin, tackifying resin and filler and stir for 100 minutes at a temperature of 165°C to make it evenly mixed;

[0078] (4) Grinding the mixed system obtained in the step (3) to a particle size of 0.3mm and continuing to stir for 5min;

[0079] (5) Add talcum powder to the mixed system after grinding in the step (4) and stir for 60 minutes to make the system evenly mixed, then cool down to room temperature and finally discharge to obtain the rubber compound of the present invention, which is recorded as A1.

preparation Embodiment 2

[0081] The specific composition of each raw material of the sizing material is shown in Table 1 below, and its preparation method includes the following steps.

[0082] (1) Mix the oil and asphalt evenly at 120°C;

[0083] (2) Heating the mixture obtained in the step (1) to 165° C., then adding SBS under agitation and mixing uniformly;

[0084] (3) Continue to add butyl rubber, SBR, lignin, tackifying resin and filler and stir for 120min at a temperature of 165°C to make it evenly mixed;

[0085] (4) Grinding the mixed system obtained in the step (3) to a particle size of 0.3 mm and continuing to stir for 10 min;

[0086] (5) Add talcum powder to the mixed system after grinding in the step (4) and stir for 60 minutes to make the system evenly mixed, then cool down to room temperature and finally discharge to obtain the rubber compound of the present invention, which is recorded as A2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
number average molecular weightaaaaaaaaaa
Login to view more

Abstract

The invention discloses a sizing material for improving the stripping performance and construction applicability of an S-CLF YC type coiled material. The sizing material obtained by compounding asphalt, an oil product, SBS, butyl rubber, SBR, lignin, tackifying resin and stone powder in a specific range can overcome the defect that the stripping strength of the coiled material and post-cast concrete does not meet the requirement. And the S-CLF YC type waterproof coiled material is smooth in appearance, the phenomena of sand surface and yellowing of the coiled material under a high-temperature condition are not easily caused, and meanwhile, it is ensured that other properties meet the standard requirements. The performance of the coiled material is improved, and the market competitiveness of the product is improved.

Description

technical field [0001] The invention belongs to the technical field of building material production, and in particular relates to a rubber material for improving the stripping performance and construction applicability of S-CLF YC type coils. In addition, the present invention also relates to a preparation method of the rubber compound. Background technique [0002] Waterproof membranes have developed very rapidly since the 1980s. Because of their advantages such as light weight, high tensile strength, high elongation, good weather resistance, large operating temperature range, and low pollution, they have gradually become very common in modern buildings. One of the most popular building materials, it is mainly used for building walls, roofs, tunnels, roads, landfills, etc., and can resist external rainwater and groundwater leakage. It is used as a link between the engineering foundation and the building. The leak-free connection is the first barrier for the waterproofing o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J195/00C09J11/08
CPCC09J195/00C09J11/08C08L2201/08C08L91/00C08L23/22C08L97/005C08L57/02
Inventor 吴帅王聪迪曹进明缪线生
Owner 苏州卓宝科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap