Flame-retardant polyester film and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A polyester film, flame retardant technology, applied in the field of flame retardant polyester film and its preparation, can solve the problems of affecting the normal use of electronic products, affecting the service life of the film, poor antistatic performance, etc. Improves versatility and reduces brittleness
Pending Publication Date: 2022-06-03
广东卓尔新材料有限公司
View PDF8 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] Chinese Patent No. CN110041672A discloses a flame-retardant polyester film and its preparation method. The flame-retardant polyester film is mainly prepared from the following weight components: 55-65% PET, 30-35% phosphorus-containing flame retardant, 3-5% stabilizer, 0.5-1.0% nano-inorganic substances and 0-4% colorant, although this kind of flame-retardant polyester film has flame-retardant performance up to UL94VTM-0 grade, the minimum film thickness can reach 25μm , has the advantages of high cost performance, but there is a problem of low strength, which is prone to damage and affects the service life of the film
[0004] Chinese Patent No. CN109795197A discloses a halogen-free flame-retardant polyester film and its preparation method, which is an ABA three-layer film structure; wherein, the A-layer film is made by mixing the following components by mass: 67-75 parts poly Ethylene terephthalate and 25-33 parts of mixture; B-layer film is made by mixing the following parts by mass: 55-60 parts of polyethylene terephthalate, 20 parts of opening agent Chips and 20-25 parts of flame retardant masterbatch; wherein, the mixture is a mixture of flame retardant masterbatch or flame retardant masterbatch and titanium dioxide white masterbatch or a mixture of flame retardant masterbatch and blue polyester masterbatch; wherein, the The flame retardant masterbatch is prepared by the following method: add 10-40% of phenoxycyclophosphazene, 1-2% of antioxidant and 2-3% of dispersant to polyester by weight, and blend The flame retardant masterbatch is obtained by extruding and granulating after uniformity. Although the phenoxycyclophosphazene flame retardant is added to the polyester film through a special process, this kind of polyester film not only does not affect the mechanical properties and thermal properties of the polyester film. Stable performance and light transmittance, and also obtained a polyester film with high flame retardancy, but there is a problem of poor antistatic performance, so when the polyester film is applied to electronic products, it is easy to affect the normal use of electronic products
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
see figure 1 , a flame-retardant polyester film, the flame-retardant polyester film comprises a first layer of film, a second layer of film and a third layer of film, the first layer of film by weight percentage includes the following components: polyethylene terephthalate 90 parts of glycol ester, 18 parts of glass fiber, 3 parts of toughening agent, 7 parts of antioxidant;
The second layer of film includes the following components by weight percentage: 60 parts of polyethylene terephthalate, 25 parts of flame retardant, 8 parts of stabilizer, and 6 parts of opening agent;
The third layer of film includes the following components by weight percentage: 85 parts of polyethylene terephthalate, 8 parts of antistatic agent, 12 parts of light stabilizer, and 4 parts of antibacterial agent.
[0023] In this embodiment, the toughening agent is any one of acrylonitrile-butadiene-styrene copolymer, chlorinated polyethylene and ethylene-vinyl acetate copolymer.
[0024] In this embod...
Embodiment 2
see figure 1 , a flame retardant polyester film, the flame retardant polyester film comprises a first layer of film, a second layer of film and a third layer of film, the first layer of film by weight percentage includes the following components: polyethylene terephthalate 70 parts of glycol ester, 10 parts of glass fiber, 2 parts of toughening agent, 6 parts of antioxidant;
The second layer of film includes the following components by weight percentage: 55 parts of polyethylene terephthalate, 22 parts of flame retardant, 7 parts of stabilizer, and 4 parts of opening agent;
The third layer of film includes the following components by weight percentage: 82 parts of polyethylene terephthalate, 5 parts of antistatic agent, 10 parts of light stabilizer, and 2 parts of antibacterial agent.
[0033] In this embodiment, the toughening agent is any one of acrylonitrile-butadiene-styrene copolymer, chlorinated polyethylene and ethylene-vinyl acetate copolymer.
[0034] In this embod...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
Login to view more
Abstract
The invention provides a flame-retardant polyester film and a preparation method thereof, and relates to the technical field of polyester films, the flame-retardant polyester film comprises a first-layer film, a second-layer film and a third-layer film, the first-layer film comprises the following components by weight: 70-90 parts of polyethylene glycol terephthalate, 10-18 parts of glass fiber, and 1-3 parts of a flexibilizer, and the third-layer film comprises the following components by weight: 1-3 parts of a flame retardant; 5-7 parts of an antioxidant; the second-layer film comprises the following components in parts by weight: 50-60 parts of polyethylene glycol terephthalate, 20-25 parts of a flame retardant, 5-8 parts of a stabilizer and 3-6 parts of an anti-blocking agent; and the third-layer film comprises the following components in percentage by weight: 80-85 parts of polyethylene glycol terephthalate. The flame-retardant polyester film is prepared by compounding the first-layer film, the second-layer film and the third-layer film, the glass fibers are added into the first-layer film to improve the strength, the second-layer film has the characteristic of high fire resistance, and the third-layer film can effectively inhibit static electricity, so that the flame-retardant polyester film is remarkable in advancement.
Description
technical field [0001] The invention relates to the technical field of polyester films, in particular to a flame-retardant polyester film and a preparation method thereof. Background technique [0002] Polyethylene terephthalate film has a wide range of applications in the field of electronic products, but because polyethylene terephthalate film is easy to burn, so the flame retardant properties of polyethylene terephthalate film Put forward certain requirements, flame retardant polyester film is born. [0003] Chinese Patent No. CN110041672A discloses a flame retardant polyester film and a preparation method thereof. The flame retardant polyester film is mainly prepared from the following weight components: 55-65% PET, 30-35% phosphorus-containing flame retardant, 3~5% stabilizer, 0.5~1.0% nano inorganic matter and 0~4% colorant, although this kind of flame retardant polyester film has flame retardant performance up to UL94VTM-0 level, the minimum film thickness can reach ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more