Oil-resistant acrylic adhesive and preparation method thereof

An adhesive, acrylic technology, applied in the direction of adhesives, adhesive types, graft polymer adhesives, etc., can solve the problems of affecting the application effect, oil resistance, water resistance and other problems, achieve high practicability, excellent oil resistance, improve The effect of water resistance

Active Publication Date: 2022-06-28
CHANGZHOU BAOLI ADHESIVE
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Today's acrylic adhesives are poor in oil resistance and water resistance, which greatly affects their practical application effects. Therefore, in order to improve the comprehensive performance of acrylic adhesives, this application discloses an oil-resistant acrylic adhesive and its preparation method to solve this problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A preparation method of oil-resistant acrylic adhesive, comprising the following steps:

[0041] (1) taking emulsifier, deionized water and core layer monomer, pre-emulsification to obtain core layer pre-emulsion; the core layer monomer is composed of acrylate monomer and dibutyl itaconic acid copolymer; The mass ratio of acrylate monomer and itaconic acid dibutyl copolymer in the layer monomer is 9:2; the emulsifier in the core layer pre-emulsion is 2wt% of the amount of the core layer monomer; the deionized water is the core layer 25wt% of the monomer amount;

[0042] Taking the emulsifier, deionized water and the intermediate layer monomer, and pre-emulsification to obtain the intermediate layer pre-emulsion; the intermediate layer monomer is composed of acrylate monomer, dibutyl itaconic acid copolymer and fluorine-containing vinyl silane; The mass ratio of the acrylate monomer, the dibutyl itaconic acid copolymer and the fluorine-containing vinylsilane in the inte...

Embodiment 2

[0048] A preparation method of oil-resistant acrylic adhesive, comprising the following steps:

[0049] (1) taking emulsifier, deionized water and core layer monomer, pre-emulsification to obtain core layer pre-emulsion; the core layer monomer is composed of acrylate monomer and dibutyl itaconic acid copolymer; The mass ratio of acrylate monomer and itaconic acid dibutyl copolymer in the layer monomer is 9:2; the emulsifier in the core layer pre-emulsion is 2wt% of the amount of the core layer monomer; the deionized water is the core layer 25wt% of the monomer amount;

[0050] Taking the emulsifier, deionized water and the intermediate layer monomer, and pre-emulsification to obtain the intermediate layer pre-emulsion; the intermediate layer monomer is composed of acrylate monomer, dibutyl itaconic acid copolymer and fluorine-containing vinyl silane; The mass ratio of the acrylate monomer, the dibutyl itaconic acid copolymer and the fluorine-containing vinylsilane in the inte...

Embodiment 3

[0056] A preparation method of oil-resistant acrylic adhesive, comprising the following steps:

[0057] (1) taking emulsifier, deionized water and core layer monomer, pre-emulsification to obtain core layer pre-emulsion; the core layer monomer is composed of acrylate monomer and dibutyl itaconic acid copolymer; The mass ratio of acrylate monomer and itaconic acid dibutyl copolymer in the layer monomer is 9:2; the emulsifier in the core layer pre-emulsion is 2wt% of the amount of the core layer monomer; the deionized water is the core layer 25wt% of the monomer amount;

[0058] Taking the emulsifier, deionized water and the intermediate layer monomer, and pre-emulsification to obtain the intermediate layer pre-emulsion; the intermediate layer monomer is composed of acrylate monomer, dibutyl itaconic acid copolymer and fluorine-containing vinyl silane; The mass ratio of the acrylate monomer, the dibutyl itaconic acid copolymer and the fluorine-containing vinylsilane in the inte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

According to the scheme, monomers such as acrylate monomers, dibutyl itaconate copolymers and fluorine-containing vinyl silane are used as main raw materials, and the adhesive with a three-layer core-shell structure is synthesized through emulsion polymerization; according to the scheme, during preparation, firstly, the core layer monomer, the middle layer monomer and the shell layer monomer are pre-emulsified, and in the step, component selection and content of the core layer monomer, the middle layer monomer and the shell layer monomer are limited, so that the oil resistance and the water resistance of the adhesive are improved, and the high-temperature resistance of the adhesive is improved. The invention discloses an oil-resistant acrylic adhesive and a preparation method thereof, the acrylic adhesive with a core layer-middle layer-shell layer composite structure is prepared, and the adhesive has excellent high temperature resistance, excellent water resistance, excellent oil resistance, good chemical corrosion resistance and high practicability.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to an oil-resistant acrylic adhesive and a preparation method thereof. Background technique [0002] Acrylic adhesives are a class of adhesives with unique properties and a wide range of applications. According to the form and application characteristics of the adhesive, it can be divided into solvent type, emulsion type, reactive type, pressure sensitive type, instant drying type, anaerobic type, photosensitive type and hot melt type. From this classification, it is not difficult to see that the application range of dienoic acid adhesives is very wide. It can be said that all metal and non-metallic materials can be bonded with acrylic adhesives, and can also be widely used in daily life and factory processing applications. [0003] Today's acrylic adhesives have poor oil resistance and water resistance, which greatly affects their practical application effect. Therefore, in orde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F285/00C08F220/34C08F222/14C08F226/12C08F267/06C08F220/14C08F220/18C08F220/20C08F230/08C08F220/06C08F2/26C08F2/30C09J151/00
CPCC08F285/00C08F267/06C08F222/145C08F2/26C08F2/30C09J151/003C08F220/34C08F226/12C08F220/14C08F220/1804C08F220/20C08F230/085C08F220/06
Inventor 胡文虎
Owner CHANGZHOU BAOLI ADHESIVE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap